Print Report | Back to Test Summary

Testing Report for 2016-07-19-16-3

Note: Fields with no data or with a value of "Unknown" will not be displayed on the print out.

Project Information

DEA: 59912684
EFIS:
Project ID: 8196
QA Service Level: 1
DIST-CO-RTE-PM: 59---
Work Description:
Location Description:
Contractor Name: Unknown
Contractor Address: Unknown
Resident Engineer: Unknown
Structure Rep.: Unknown

Sample Information

DIME Sample ID: 2016-07-19-16
TL Number from the TL Form: Unknown
Sample Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Sample Organization Contact: (916) 227-7253
Type of Sample: Quality Assurance
Type of Material: SMTL TM2 - Type B Elastomeric Joint Seal
Sample Taken Date: 7/19/2016
Date that the sample was received by the laboratory/organization performing the testing: 7/21/2016
The quantity of what the sample constitutes: 550ft
A brief description of the sample: Joint Seal
From where was the sample collected: Manufacturer
Laboratory sample identification: Unknown
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: Watson Bowman

Material Information

Mfg. Lot Number(s): 1116294
Manufacturer(s): Watson Bowman
Temperature: 72
Humidity: 50
Comments: Unknown
Joint Seal Size: 3.75in

Test Information

DIME Test ID: 2016-07-19-16-3
Test Method: ASTM D412-06a-re13: Standard Test Methods for Vulcanized Rubber and Thermoplastic Elastomers-Tension
Date Tested: 8/2/2016
Verified Date: 8/17/2016
Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Organization Address: 5900 Folsom Blvd,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: paul.lukkarila@dot.ca.gov
Organization Phone: (916) 227-7253
General Comments for this Test:
Test Result Compliance:
Additional Comments When Verified :

Submitted Test Results

UTM: 2KIP
Humidity: 50 %
Temperature: 72 F
Sample 1 Median Thickness: 0.073 in
Sample 1 Thickness all Within 0.003 inch?: Yes
Sample 1 Ultimate Tensile: 2131.1 lbf?in/in?
Sample 1 Elongation (350% Min): Pass
Sample 2 Median Thickness: 0.078 in
Sample 2 Thickness all Within 0.003 inch?: Yes
Sample 2 Ultimate Tensile: 2359 lbf?in/in?
Sample 2 Elongation (350% Min): Pass
Sample 3 Median Thickness: 0.083 in
Sample 3 Thickness all Within 0.003 inch?: Yes
Sample 3 Ultimate Tensile: 2211.5 lbf?in/in?
Sample 3 Elongation (350% Min): Pass
Median of the Ultimate Tensile Values: 2211.5 psi