Print Report | Back to Test Summary

Testing Report for 2016-06-08-3-2

Note: Fields with no data or with a value of "Unknown" will not be displayed on the print out.

Project Information

DEA: 59912684
EFIS:
Project ID: 8196
QA Service Level: 1
DIST-CO-RTE-PM: 59---
Work Description:
Location Description:
Contractor Name: Unknown
Contractor Address: Unknown
Resident Engineer: Unknown
Structure Rep.: Unknown

Sample Information

DIME Sample ID: 2016-06-08-3
TL Number from the TL Form: C711151
Sample Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Sample Organization Contact: (916) 227-7253
Type of Sample: Quality Assurance
Type of Material: SMTL TM1 - Elastomeric Bearing Pad
Sample Taken Date: 6/8/2016
Date that the sample was received by the laboratory/organization performing the testing: 6/9/2016
The quantity of what the sample constitutes: 30ft
A brief description of the sample: Plain Bearing Pad
From where was the sample collected: Distributor
Laboratory sample identification: Unknown
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: Warco Cal Neva

Material Information

Mfg. Lot Number(s): 10 14 14 1
Material/Compound/Elastomer ID: NA
Samples Representing: 30ft
Description (size): .375in x 48in
Comments: Unknown
Description (Number of Shims): 0
Type of Bearing Pad: Plain
Description (Thickness of Shims): NA
Manufacturer(s): Warco
Batch Number: NA

Test Information

DIME Test ID: 2016-06-08-3-2
Test Method: ASTM D412-06a-re13: Standard Test Methods for Vulcanized Rubber and Thermoplastic Elastomers—Tension
Date Tested: 6/10/2016
Verified Date: 6/21/2016
Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Organization Address: 5900 Folsom Blvd,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: paul.lukkarila@dot.ca.gov
Organization Phone: (916) 227-7253
General Comments for this Test:
Test Result Compliance: complies
Additional Comments When Verified :

Submitted Test Results

UTM: 2KIP
Humidity: 50 %
Temperature: 72 F
Sample 1 Median Thickness: 0.084 in
Sample 1 Thickness all Within 0.003 inch?: Yes
Sample 1 Ultimate Tensile: 2619 lbf/in^2
Sample 1 Elongation (350% Min): Pass
Sample 2 Median Thickness: 0.082 in
Sample 2 Thickness all Within 0.003 inch?: Yes
Sample 2 Ultimate Tensile: 2829.3 lbf/in^2
Sample 2 Elongation (350% Min): Pass
Sample 3 Median Thickness: 0.083 in
Sample 3 Thickness all Within 0.003 inch?: Yes
Sample 3 Ultimate Tensile: 3028.8 lbf/in^2
Sample 3 Elongation (350% Min): Pass
Median of the Ultimate Tensile Values: 2829.3 lbf/in^2