Print Report | Back to Test Summary

Testing Report for 2016-03-31-6-3

Note: Fields with no data or with a value of "Unknown" will not be displayed on the print out.

Project Information

DEA: 59912684
Project ID: 8196
QA Service Level: 1
Work Description:
Location Description:
Contractor Name: Unknown
Contractor Address: Unknown
Resident Engineer: Unknown
Structure Rep.: Unknown

Sample Information

DIME Sample ID: 2016-03-31-6
TL Number from the TL Form: Unknown
Sample Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Sample Organization Contact: (916) 227-7253
Type of Sample: Quality Assurance
Type of Material: SMTL TM1 - Elastomeric Bearing Pad
Sample Taken Date: 3/31/2016
Date that the sample was received by the laboratory/organization performing the testing: 4/5/2016
The quantity of what the sample constitutes: roll
A brief description of the sample: Plain Bearing Pad
From where was the sample collected: Fabricator
Laboratory sample identification: Unknown
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: Scougal Rubber

Material Information

Mfg. Lot Number(s): 1605069
Material/Compound/Elastomer ID: 1605069
Samples Representing: Roll
Description (size): 0.125in
Comments: Unknown
Description (Number of Shims): NA
Type of Bearing Pad: Plain
Description (Thickness of Shims): NA
Manufacturer(s): Scougal Rubber
Batch Number: NA

Test Information

DIME Test ID: 2016-03-31-6-3
Test Method: ASTM D624-00-re12: Standard Test Method for Tear Strength of Conventional Vulcanized Rubber and Thermoplastic Elastomers
Date Tested: 4/7/2016
Verified Date: 4/14/2016
Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Organization Address: 5900 Folsom Blvd,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email:
Organization Phone: (916) 227-7253
General Comments for this Test:
Test Result Compliance: complies
Additional Comments When Verified :

Submitted Test Results

Number of specimens tested: 3
Humidity: 50 %
Temperature: 72 F
Sample 1 Median Thickness: 0.139 in
Sample 1 Tear Strength: 251.8 lbf / in
Sample 2 Median Thickness: 0.139 in
Sample 2 Tear Strength: 266.2 lbf / in
Sample 3 Median Thickness: 0.139 in
Sample 3 Tear Strength: 273.4 lbf / in
Median of the Tear Strength Values: 266.2 lb/in