Print Report | Back to Test Summary

Testing Report for 2021-09-29-5-3

Note: Fields with no data or with a value of "Unknown" will not be displayed on the print out.

Project Information

DEA: 101K9304
EFIS: 1020000014
Project ID: 215417
QA Service Level: 1
DIST-CO-RTE-PM: 10-SJ-VAR,580-VAR
Work Description: BRIDGE DECKS INVESTIGATION AND REHABILITATION IN AND NEAR TRACY
Location Description: SJ CTY IN & NEAR TRACY FROM GAFFERY RD TO EAST MIDWAY
Contractor Name: Unknown
Contractor Address: Unknown
Resident Engineer: Bal Bahadur Paul
Structure Rep.: Ron Matin

Sample Information

DIME Sample ID: 2021-09-29-5
TL Number from the TL Form: Sacramento Caltrans lab
Sample Submitted By Organization: Kwik Bond Polymers
Sample Organization Contact: 760-518-6064
Type of Sample: Quality Control
Type of Material: Polyester
Sample Taken Date: 9/29/2021
Date that the sample was received by the laboratory/organization performing the testing: 9/29/2021
The quantity of what the sample constitutes: 2 tankers
A brief description of the sample: 1 gallon can
From where was the sample collected: Source
Laboratory sample identification:
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: Kwik Bond Polymers and Polynt

Material Information

Mfg. Lot Number(s): 1361244
Batch number: 1361244
Mix number: 1361244

Test Information

DIME Test ID: 2021-09-29-5-3
Test Method: ASTM D638-Dec14: Standard Test Method for Tensile Properties of Plastics
Date Tested: 10/15/2021
Verified Date: 10/15/2021
Submitted By Organization: CT HQ - Sacramento Concrete Testing Laboratory
Organization Address: 5900 Folsom Blvd,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: larry.mccrum@dot.ca.gov
Organization Phone: (916) 227-7283
General Comments for this Test: Accepted Based On Supplier Results
Test Result Compliance: complies
Additional Comments When Verified :

Submitted Test Results

Number of specimens tested: 5
Conditioning procedure: 18/25/50+5/70
Speed of testing: 0.45 in/min
Sample 1 Width: 0.486 in
Sample 1 Ultimate strength: 3504.7 psi
Sample 1 Thickness: 0.245 in
Sample 1 Area: 0.1191 in^2
Sample 1 Ultimate Strength Actual: 417.41 lbs
Sample 1 percent elongation: 67.73 %
Sample 1 Time: no data
Sample 2 Width: 0.486 in
Sample 2 Thickness: 0.243 in
Sample 2 Area: 0.1181 in^2
Sample 2 Ultimate strength : 3170.3 psi
Sample 2 Ultimate Strength Actual: 374.412 lbs
Sample 2 percent elongation: 58.97 %
Sample 2 Time: no data
Sample 3 Width: 0.486 in
Sample 3 Thickness: 0.244 in
Sample 3 Area: 0.1186 in^2
Sample 3 Ultimate strength: 3620 psi
Sample 3 Ultimate Strength Actual: 429.332 lbs
Sample 3 percent elongation: 70.38 %
Sample 3 Time: no data
Sample 4 Width: 0.486 in
Sample 4 Thickness: 0.244 in
Sample 4 Area: 0.1186 in^2
Sample 4 Ultimate strength: 3469.3 psi
Sample 4 Ultimate Strength Actual: 411.459 lbs
Sample 4 percent elongation: 67.12 %
Sample 4 Time: no data
Sample 5 Width: 0.486 in
Sample 5 Thickness: 0.251 in
Sample 5 Area: 0.122 in^2
Sample 5 Ultimate strength: 3387.5 psi
Sample 5 Ultimate Strength Actual: 413.275 lbs
Sample 5 percent elongation: 65.33 %
Sample 5 Time: no data
Ultimate Strength Average: 3430 psi
Percent Elongation Average: 66 %