Print Report | Back to Test Summary

Testing Report for 2021-09-20-25-5

Note: Fields with no data or with a value of "Unknown" will not be displayed on the print out.

Project Information

DEA: 010J8704
EFIS: 0119000117
Project ID: 215621
QA Service Level: 1
DIST-CO-RTE-PM: 01-MEN-101,271-VAR
Work Description: PLACE HMA, POLYESTER CONCRETE OVERLAY AND COLD PLANE.
Location Description: MENDOCINO COUNTY AT VARIOUS LOCATIONS
Contractor Name: Unknown
Contractor Address: Unknown
Resident Engineer: Mike Anderson
Structure Rep.: Kari Forbes

Sample Information

DIME Sample ID: 2021-09-20-25
TL Number from the TL Form: Sacramento Caltrans lab
Sample Submitted By Organization: Kwik Bond Polymers
Sample Organization Contact: 760-518-6064
Type of Sample: Quality Control
Type of Material: Polyester
Sample Taken Date: 9/20/2021
Date that the sample was received by the laboratory/organization performing the testing: 9/20/2021
The quantity of what the sample constitutes: 2 tankers
A brief description of the sample: 1 gallon can
From where was the sample collected: Source
Laboratory sample identification:
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: Kwik Bond Polymers and Polynt

Material Information

Mfg. Lot Number(s): 1360547
Batch number: 1360547
Mix number: 1360547

Test Information

DIME Test ID: 2021-09-20-25-5
Test Method: CTM 551-August 2012: Method of Test for Determining Suitability of Materials for Overlayment and Repair of Portland Cement Concrete Pavements and Structures
Date Tested: 9/29/2021
Verified Date: 9/29/2021
Submitted By Organization: CT HQ - Sacramento Concrete Testing Laboratory
Organization Address: 5900 Folsom Blvd,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: larry.mccrum@dot.ca.gov
Organization Phone: (916) 227-7283
General Comments for this Test: Accepted Based On Vendor Results.
Test Result Compliance: complies
Additional Comments When Verified :

Submitted Test Results

Curing history for Sample 1: 24hr
Maximum applied load (P) for Sample 1: 1909.58 lb
Span length for Sample 1: 9 in
Break location for Sample 1: PCC
Specimen defects/notes for Sample 1: no data
Surface type for Sample 1: SSD
Modulus of rupture (R) for Sample 1: 954.79 psi
Curing history for Sample 2: 24hr
Maximum applied load (P) for Sample 2: 1839.11 lb
Span length for Sample 2: 9 in
Break location for Sample 2: PCC
Specimen defects/notes for Sample 2: no data
Surface type for Sample 2: SSD
Modulus of rupture (R) for Sample 2: 919.555 psi
Curing history for Sample 3: 24hr
Maximum applied load (P) for Sample 3: 1763.79 lb
Span length for Sample 3: 9 in
Break location for Sample 3: PCC
Specimen defects/notes for Sample 3: no data
Surface type for Sample 3: SSD
Modulus of rupture (R) for Sample 3: 881.895 psi