Project Information

DEA: 040A5394
EFIS: 0418000244
Project ID: 214114
QA Service Level: 1
DIST-CO-RTE-PM: 04-SOL-80,12-11.4/12.8, 2.1/2.8
Work Description: Widen EB SR-12 Connector, Construct 3 ramps & 2 box girder bridges, remove existing bridge, etc.
Location Description: I-80/I-680/Route 12 Interchange
Contractor Name: Unknown
Contractor Address: Unknown
Resident Engineer: Fernando Dos Santos
Structure Rep.: Alejandro Lara

Sample Information

DIME Sample ID: 2021-08-20-45
TL Number from the TL Form:
Sample Submitted By Organization: CT D04 - DME / District Lab
Sample Organization Contact: (510) 507-3456
Type of Sample: Verification
Type of Material: Hot Mix Asphalt
Sample Taken Date: 8/20/2021
Date that the sample was received by the laboratory/organization performing the testing: 8/20/2021
The quantity of what the sample constitutes: 16 boxes of 1/2" Type A HMA with RAP
A brief description of the sample: 16 Boxes of HMA
From where was the sample collected: Manufacturer
Laboratory sample identification:
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: Syar Vallejo

Material Information

HMA Type: Type A HMA
HMA Grading: 1/2 inch
Lot number:
Sublot number:

Test Information

DIME Test ID: 2021-08-20-45-4
Test Method: AASHTO T283-14: Standard Method of Test for Resistance of Compacted Asphalt Mixtures to Moisture-Induced Damage (Moisture Content)
Date Tested: 9/3/2021
Verified Date: 9/15/2021
Submitted By Organization: CT D04 - DME / District Lab
Organization Address: 21339 Cabot Blvd,
Organization City: Hayward
Organization State: CA
Organization Zipcode: 94545
Organization Email:
Organization Phone: (510) 507-3456
General Comments for this Test:
Test Result Compliance:
Additional Comments When Verified :

Submitted Test Results

Average Dry Tensile Strength: 203 psi
Average Wet Tensile Strength: 193 psi
Tensile Strength Ratio: 0.95