Note: Fields with no data or with a value of "Unknown" will not be displayed on the print out.
Project ID: 44444 DEA: ASCP EFIS: ASCP
QA Service Level:
DIST-CO-RTE-PM: 59---
Work Description: Special project for submitting Sample information for Asphalt Supplier Certification Program.
Location Description:
Contractor Name: Unknown
Contractor Address: Unknown
Resident Engineer: Unknown Structure Rep.: Unknown
DIME Sample ID: 2021-08-02-35
TL Number from the TL Form:
Sample Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Sample Organization Contact: (916) 227-7302
Type of Sample: Verification
Type of Material: Asphalt Binder
Sample Taken Date: 08/02/2021
Date that the sample was received by the laboratory/organization performing the testing: 08/02/2021
The quantity of what the sample constitutes: 2 of 2, split sample
A brief description of the sample: Asphalt Binder Sample
From where was the sample collected: Source
Laboratory sample identification: Z3227244
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: Ergon Las Vegas
Performance Grade: PG 76-22 M
Modified: Yes
Lot number:
Sublot number:
Tank number:
Time of sample: 0700
HMA Supplier:
Certified Asphalt Supplier: Ergon Asphalt & Emulsions Incorporated - Las Vegas NV
Multigrade: No
Multigrade Type:
Asphalt Binder Mix Number:
DIME Test ID: 2021-08-02-35-1
Test Method: AASHTO T240-17: Standard Method of Test for Effect of Heat and Air on a Moving Film of Asphalt Binder (Rolling Thin-Film Oven Test)
Verified Date: 09/14/2021
Date Tested: 09/02/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Boulevard, Room 225,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test:
Test Result Compliance: complies
Additional Comments When Verified:
Is mass change based on one or two containers?
|
Two
|
Any material loss from containers during heating process/testing?
|
No
|
Mass of empty container #1
|
171.443 grams
|
Mass of empty container #2
|
160.652 grams
|
Mass of container #1 before test (m1i)
|
206.833 grams
|
Mass of container #2 before test (m2i)
|
195.874 grams
|
Mass of container #1 after test (m1f)
|
206.720 grams
|
Mass of container #2 after test (m2f)
|
195.763 grams
|
Average mass change
|
-0.317 percent
|
DIME Test ID: 2021-08-02-35-2
Test Method: AASHTO T301-13: Standard Method of Test for Elastic Recovery Test of Asphalt Materials by Means of a Ductilometer
Verified Date: 09/14/2021
Date Tested: 09/02/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Boulevard, Room 225,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test:
Test Result Compliance: complies
Additional Comments When Verified:
Final Reading from the testing machine (X)
|
3 cm
|
% Elongation Recovery
|
85 %
|
DIME Test ID: 2021-08-02-35-3
Test Method: AASHTO T315-20: Standard Method of Test for Determining the Rheological Properties of Asphalt Binder Using a Dynamic Shear Rheometer (DSR) (Dynamic Shear)
Verified Date: 09/14/2021
Date Tested: 09/02/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Boulevard, Room 225,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test:
Test Result Compliance: complies
Additional Comments When Verified:
Phase
|
Original binder
|
Test Plate Diameter
|
25 mm
|
Test Gap
|
1 mm
|
Test Frequency
|
10.0 rad/s
|
Strain Amplitude
|
12.00 %
|
Stress Amplitude
|
0.177 kPa
|
Phase Angle (δ) (for the 10 cycles)
|
52.8 degree
|
Complex Modulus (G*) (for the 10 measurements)
|
1.476 kPa
|
Test Temperature (Specimen 1)
|
76.0 C
|
Dynamic Shear, G*/sin(δ)
|
1.85 kPa
|
DIME Test ID: 2021-08-02-35-4
Test Method: AASHTO T315-20: Standard Method of Test for Determining the Rheological Properties of Asphalt Binder Using a Dynamic Shear Rheometer (DSR) (Dynamic Shear)
Verified Date: 09/14/2021
Date Tested: 09/02/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Boulevard, Room 225,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: RTFO
Test Result Compliance: complies
Additional Comments When Verified:
Phase
|
RTFO residue
|
Test Plate Diameter
|
25 mm
|
Test Gap
|
1 mm
|
Test Frequency
|
10.0 rad/s
|
Strain Amplitude
|
10.00 %
|
Stress Amplitude
|
0.236 kPa
|
Phase Angle (δ) (for the 10 cycles)
|
52.7 degree
|
Complex Modulus (G*) (for the 10 measurements)
|
2.364 kPa
|
Test Temperature (Specimen 1)
|
76.0 C
|
Dynamic Shear, G*/sin(δ)
|
2.97 kPa
|
DIME Test ID: 2021-08-02-35-5
Test Method: AASHTO T315-20: Standard Method of Test for Determining the Rheological Properties of Asphalt Binder Using a Dynamic Shear Rheometer (DSR) (Dynamic Shear)
Verified Date: 09/14/2021
Date Tested: 09/09/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Boulevard, Room 225,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: PAV
Test Result Compliance: complies
Additional Comments When Verified:
Phase
|
PAV residue
|
Test Plate Diameter
|
8 mm
|
Test Gap
|
2 mm
|
Test Frequency
|
10.0 rad/s
|
Strain Amplitude
|
1.00 %
|
Stress Amplitude
|
11.474 kPa
|
Phase Angle (δ) (for the 10 cycles)
|
49.1 degree
|
Complex Modulus (G*) (for the 10 measurements)
|
1147.487 kPa
|
Test Temperature (Specimen 1)
|
31.0 C
|
(G*) x sin(δ)=
|
867 kPa
|
DIME Test ID: 2021-08-02-35-6
Test Method: AASHTO T313-19: Standard Method of Test for Determining the Flexural Creep Stiffness of Asphalt Binder Using the Bending Beam Rheometer (BBR)
Verified Date: 09/14/2021
Date Tested: 09/13/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Boulevard, Room 225,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test:
Test Result Compliance: complies
Additional Comments When Verified:
Minimum test bath temperature at 240 s
|
-12.0 C
|
Maximum test bath temperature at 240 s
|
-12.0 C
|
Time of test load application
|
no data HH:MM:SS
|
File name of test data
|
no data
|
Time beam in bath
|
no data
|
Time test started
|
no data HH:MM:SS
|
Flags issued by software during test
|
no data
|
Correlation coefficient (R²)
|
0
|
Regression coefficient a
|
no data
|
Regression coefficient b
|
no data
|
Regression coefficient c
|
no data
|
Load at time 0.0
|
0.0 mN
|
Deflection at time 0.0 s
|
0.000 µm
|
Load at time 0.5 s
|
0.0 mN
|
Deflection at time 0.5 s
|
0.000 µm
|
Load at 60.0 s
|
986.0 mN
|
Beam deflection 60.0 s
|
0.979 µm
|
Measured Stiffness Modulus 60.0 s
|
81.200 mPa
|
Estimated Stiffness Modulus 60.0 s
|
81.300 mPa
|
Difference between stiffness moduli 60.0 s
|
no data
|
Estimated m-value 60.0 s
|
0.380
|
DIME Test ID: 2021-08-02-35-7
Test Method: AASHTO T315-20: Standard Method of Test for Determining the Rheological Properties of Asphalt Binder Using a Dynamic Shear Rheometer (DSR) (Dynamic Shear)
Verified Date: 09/14/2021
Date Tested: 09/14/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Boulevard, Room 225,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: RTFO +6C for delta
Test Result Compliance: complies
Additional Comments When Verified:
Phase
|
RTFO residue
|
Test Plate Diameter
|
25 mm
|
Test Gap
|
1 mm
|
Test Frequency
|
10.0 rad/s
|
Strain Amplitude
|
10.00 %
|
Stress Amplitude
|
0.149 kPa
|
Phase Angle (δ) (for the 10 cycles)
|
51.1 degree
|
Complex Modulus (G*) (for the 10 measurements)
|
1.486 kPa
|
Test Temperature (Specimen 1)
|
82.0 C
|
Dynamic Shear, G*/sin(δ)
|
1.91 kPa
|