Sample Record for 2021-08-30-25

Note: Fields with no data or with a value of "Unknown" will not be displayed on the print out.

Project Information

Project ID: 215393 DEA: 021J5104 EFIS: 0220000086 QA Service Level: 1
DIST-CO-RTE-PM: 02-LAS,MOD-139-57.0/66.635,0.0/0.1
Work Description: PERFORM COLD IN-PLACE RECYCLING AND PLACE HOT MIX ASPHALT (TYPE A).
Location Description: LASSEN AND MODOC COUNTIES NEAR ADIN FROM 4.5 MILES SOUTH OF COUNTY ROAD A2 TO 0.1 MILE SOUTH OF ROUTE 299
Contractor Name: Hat Creek Construction
Contractor Address: 24339 Highway 89 N, Burney, CA 96013
Resident Engineer: Mike Zdenek Structure Rep.: Unknown

Sample Information

DIME Sample ID: 2021-08-30-25
TL Number from the TL Form: C848953
Sample Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Sample Organization Contact: (916) 227-7302
Type of Sample: Acceptance
Type of Material: Asphalt Binder
Sample Taken Date: 08/30/2021
Date that the sample was received by the laboratory/organization performing the testing: 09/03/2021
The quantity of what the sample constitutes: 1 OF 2 CANS, #1 TEST
A brief description of the sample: BINDER
From where was the sample collected: Source
Laboratory sample identification:
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: KLAMATH FALLS, OR

Material Information

Performance Grade: PG 58-34 M
Modified: Yes
Lot number:
Sublot number:
Tank number:
Time of sample:
HMA Supplier: CONTRACTOR HAT CREEK
Certified Asphalt Supplier: Albina Asphalt - Klamath Falls Plant - Klamath Falls OR
Multigrade: No
Multigrade Type:
Asphalt Binder Mix Number:

Test Results

Test 1 of 6

DIME Test ID: 2021-08-30-25-1
Test Method: AASHTO T240-17: Standard Method of Test for Effect of Heat and Air on a Moving Film of Asphalt Binder (Rolling Thin-Film Oven Test)
Verified Date: 09/15/2021
Date Tested: 09/09/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Boulevard, Room 225,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: as per 2018 standard specs
Test Result Compliance: complies
Additional Comments When Verified:
Is mass change based on one or two containers? Two
Any material loss from containers during heating process/testing? No
Mass of empty container #1 176.372 grams
Mass of empty container #2 179.453 grams
Mass of container #1 before test (m1i) 212.032 grams
Mass of container #2 before test (m2i) 214.851 grams
Mass of container #1 after test (m1f) 211.873 grams
Mass of container #2 after test (m2f) 214.685 grams
Average mass change -0.457 percent

Test 2 of 6

DIME Test ID: 2021-08-30-25-2
Test Method: AASHTO T315-20: Standard Method of Test for Determining the Rheological Properties of Asphalt Binder Using a Dynamic Shear Rheometer (DSR) (Dynamic Shear)
Verified Date: 09/15/2021
Date Tested: 09/08/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Boulevard, Room 225,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: Per 2018 Standard Specifications ORIG
Test Result Compliance: complies
Additional Comments When Verified:
Phase Original binder
Test Plate Diameter 25 mm
Test Gap 1 mm
Test Frequency 10.0 rad/s
Strain Amplitude 12.00 %
Stress Amplitude 0.187 kPa
Phase Angle (δ) (for the 10 cycles) 69.3 degree
Complex Modulus (G*) (for the 10 measurements) 1.555 kPa
Test Temperature (Specimen 1) 58.0 C
Dynamic Shear, G*/sin(δ) 1.66 kPa

Test 3 of 6

DIME Test ID: 2021-08-30-25-3
Test Method: AASHTO T315-20: Standard Method of Test for Determining the Rheological Properties of Asphalt Binder Using a Dynamic Shear Rheometer (DSR) (Dynamic Shear)
Verified Date: 09/15/2021
Date Tested: 09/08/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Boulevard, Room 225,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: Per 2018 Standard Specifications RTFO
Test Result Compliance: complies
Additional Comments When Verified:
Phase RTFO residue
Test Plate Diameter 25 mm
Test Gap 1 mm
Test Frequency 10.0 rad/s
Strain Amplitude 10.00 %
Stress Amplitude 0.370 kPa
Phase Angle (δ) (for the 10 cycles) 62.8 degree
Complex Modulus (G*) (for the 10 measurements) 3.702 kPa
Test Temperature (Specimen 1) 58.0 C
Dynamic Shear, G*/sin(δ) 4.16 kPa

Test 4 of 6

DIME Test ID: 2021-08-30-25-4
Test Method: AASHTO T315-20: Standard Method of Test for Determining the Rheological Properties of Asphalt Binder Using a Dynamic Shear Rheometer (DSR) (Dynamic Shear)
Verified Date: 09/15/2021
Date Tested: 09/08/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Boulevard, Room 225,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: Per 2018 Standard Specifications RTFO+6
Test Result Compliance: complies
Additional Comments When Verified:
Phase RTFO residue
Test Plate Diameter 25 mm
Test Gap 1 mm
Test Frequency 10.0 rad/s
Strain Amplitude 10.00 %
Stress Amplitude 0.210 kPa
Phase Angle (δ) (for the 10 cycles) 64.5 degree
Complex Modulus (G*) (for the 10 measurements) 2.097 kPa
Test Temperature (Specimen 1) 64.0 C
Dynamic Shear, G*/sin(δ) 2.32 kPa

Test 5 of 6

DIME Test ID: 2021-08-30-25-5
Test Method: AASHTO T315-20: Standard Method of Test for Determining the Rheological Properties of Asphalt Binder Using a Dynamic Shear Rheometer (DSR) (Dynamic Shear)
Verified Date: 09/15/2021
Date Tested: 09/13/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Boulevard, Room 225,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: Per 2018 Standard Specifications PAV
Test Result Compliance: complies
Additional Comments When Verified:
Phase PAV residue
Test Plate Diameter 8 mm
Test Gap 2 mm
Test Frequency 10.0 rad/s
Strain Amplitude 1.00 %
Stress Amplitude 47.169 kPa
Phase Angle (δ) (for the 10 cycles) 39.6 degree
Complex Modulus (G*) (for the 10 measurements) 4715.033 kPa
Test Temperature (Specimen 1) 16.0 C
(G*) x sin(δ)= 3005 kPa

Test 6 of 6

DIME Test ID: 2021-08-30-25-6
Test Method: AASHTO T313-19: Standard Method of Test for Determining the Flexural Creep Stiffness of Asphalt Binder Using the Bending Beam Rheometer (BBR)
Verified Date: 09/15/2021
Date Tested: 09/13/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Boulevard, Room 225,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: Per 2018 Standard Specifications
Test Result Compliance: complies
Additional Comments When Verified:
Minimum test bath temperature at 240 s -24.0 C
Maximum test bath temperature at 240 s -23.9 C
Time of test load application no data HH:MM:SS
File name of test data no data
Time beam in bath no data
Time test started no data HH:MM:SS
Flags issued by software during test no data
Correlation coefficient (R²) 0
Regression coefficient a no data
Regression coefficient b no data
Regression coefficient c no data
Load at time 0.0 0.0 mN
Deflection at time 0.0 s 0.000 µm
Load at time 0.5 s 0.0 mN
Deflection at time 0.5 s 0.000 µm
Load at 60.0 s 946.0 mN
Beam deflection 60.0 s 0.563 µm
Measured Stiffness Modulus 60.0 s 135.000 mPa
Estimated Stiffness Modulus 60.0 s 136.000 mPa
Difference between stiffness moduli 60.0 s no data
Estimated m-value 60.0 s 0.309