Print Report | Back to Sample Detail

Sample Record for 2021-07-14-17

Note: Fields with no data or with a value of "Unknown" will not be displayed on the print out.

Project Information

Project ID: 215607 DEA: 061C6504 EFIS: 0621000099 QA Service Level: 1
DIST-CO-RTE-PM: 06-FRE-41-R0.5/M5.9
Work Description: RESURFACE AC PAVEMENT AND INSTALL MEDIAN TYPE K CONCRETE BARRIER.
Location Description: FRESNO COUNTY ABOUT 6 MILES NORTH OF LEMOORE FROM 0.5 MILE NORTH OF EXCELSIOR AVENUE UNDERCROSSING TO 0.2 MILE SOUTH OF ELKHORN AVENUE
Contractor Name: Cal Valley Construction
Contractor Address: 5125 N. Gates Ave., Ste. 102, Fresno, CA, 93722-6414
Resident Engineer: Mark Mengoni Structure Rep.: Unknown

Sample Information

DIME Sample ID: 2021-07-14-17
TL Number from the TL Form: 039894
Sample Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Sample Organization Contact: (916) 227-7302
Type of Sample: Acceptance
Type of Material: Asphalt Binder
Sample Taken Date: 07/14/2021
Date that the sample was received by the laboratory/organization performing the testing: 07/20/2021
The quantity of what the sample constitutes: 1 OF 1 CAN
A brief description of the sample: BINDER 64-16
From where was the sample collected: Source
Laboratory sample identification:
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: San Joaquin Refining Co Inc

Material Information

Performance Grade: PG 64-16
Modified: No
Lot number: 2
Sublot number: 10
Tank number:
Time of sample:
HMA Supplier: Granite Coalinga
Certified Asphalt Supplier: San Joaquin Refinery - Bakersfield CA
Multigrade: No
Multigrade Type:
Asphalt Binder Mix Number:

Test Results

Test 1 of 6

DIME Test ID: 2021-07-14-17-1
Test Method: AASHTO T240-17: Standard Method of Test for Effect of Heat and Air on a Moving Film of Asphalt Binder (Rolling Thin-Film Oven Test)
Verified Date: 07/27/2021
Date Tested: 07/22/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Boulevard, Room 225,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: Per 2018 standard specifications
Test Result Compliance: complies
Additional Comments When Verified:
Is mass change based on one or two containers? Two
Any material loss from containers during heating process/testing? No
Mass of empty container #1 168.627 grams
Mass of empty container #2 171.074 grams
Mass of container #1 before test (m1i) 205.584 grams
Mass of container #2 before test (m2i) 206.969 grams
Mass of container #1 after test (m1f) 205.581 grams
Mass of container #2 after test (m2f) 206.954 grams
Average mass change -0.025 percent

Test 2 of 6

DIME Test ID: 2021-07-14-17-2
Test Method: AASHTO T315-20: Standard Method of Test for Determining the Rheological Properties of Asphalt Binder Using a Dynamic Shear Rheometer (DSR) (Dynamic Shear)
Verified Date: 07/27/2021
Date Tested: 07/22/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Boulevard, Room 225,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: Per 2018 Standard Specifications
Test Result Compliance: complies
Additional Comments When Verified:
Phase Original binder
Test Plate Diameter 25 mm
Test Gap 1 mm
Test Frequency 10.0 rad/s
Strain Amplitude 12.00 %
Stress Amplitude 0.176 kPa
Phase Angle (δ) (for the 10 cycles) 89.2 degree
Complex Modulus (G*) (for the 10 measurements) 1.465 kPa
Test Temperature (Specimen 1) 64.0 C
Dynamic Shear, G*/sin(δ) 1.47 kPa

Test 3 of 6

DIME Test ID: 2021-07-14-17-3
Test Method: AASHTO T315-20: Standard Method of Test for Determining the Rheological Properties of Asphalt Binder Using a Dynamic Shear Rheometer (DSR) (Dynamic Shear)
Verified Date: 07/27/2021
Date Tested: 07/22/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Boulevard, Room 225,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: Per 2018 Standard Specifications RTFO
Test Result Compliance: complies
Additional Comments When Verified:
Phase RTFO residue
Test Plate Diameter 25 mm
Test Gap 1 mm
Test Frequency 10.0 rad/s
Strain Amplitude 10.00 %
Stress Amplitude 0.267 kPa
Phase Angle (δ) (for the 10 cycles) 88.4 degree
Complex Modulus (G*) (for the 10 measurements) 2.674 kPa
Test Temperature (Specimen 1) 64.0 C
Dynamic Shear, G*/sin(δ) 2.68 kPa

Test 4 of 6

DIME Test ID: 2021-07-14-17-4
Test Method: AASHTO T315-20: Standard Method of Test for Determining the Rheological Properties of Asphalt Binder Using a Dynamic Shear Rheometer (DSR) (Dynamic Shear)
Verified Date: 07/27/2021
Date Tested: 07/23/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Boulevard, Room 225,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: Per 2018 Standard Specifications PAV
Test Result Compliance: not applicable
Additional Comments When Verified:
Phase PAV residue
Test Plate Diameter 8 mm
Test Gap 2 mm
Test Frequency 10.0 rad/s
Strain Amplitude 1.00 %
Stress Amplitude 68.555 kPa
Phase Angle (δ) (for the 10 cycles) 58.1 degree
Complex Modulus (G*) (for the 10 measurements) 6854.699 kPa
Test Temperature (Specimen 1) 28.0 C
(G*) x sin(δ)= 5819 kPa

Test 5 of 6

DIME Test ID: 2021-07-14-17-5
Test Method: AASHTO T313-19: Standard Method of Test for Determining the Flexural Creep Stiffness of Asphalt Binder Using the Bending Beam Rheometer (BBR)
Verified Date: 07/27/2021
Date Tested: 07/26/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Boulevard, Room 225,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: per 2018 standard specifications
Test Result Compliance: complies
Additional Comments When Verified:
Minimum test bath temperature at 240 s -6.0 C
Maximum test bath temperature at 240 s -6.0 C
Time of test load application no data HH:MM:SS
File name of test data no data
Time beam in bath no data
Time test started no data HH:MM:SS
Flags issued by software during test no data
Correlation coefficient (R²) 0
Regression coefficient a no data
Regression coefficient b no data
Regression coefficient c no data
Load at time 0.0 0.0 mN
Deflection at time 0.0 s 0.000 µm
Load at time 0.5 s 0.0 mN
Deflection at time 0.5 s 0.000 µm
Load at 60.0 s 0.0 mN
Beam deflection 60.0 s 0.000 µm
Measured Stiffness Modulus 60.0 s 230.000 mPa
Estimated Stiffness Modulus 60.0 s 229.000 mPa
Difference between stiffness moduli 60.0 s no data
Estimated m-value 60.0 s 0.381

Test 6 of 6

DIME Test ID: 2021-07-14-17-7
Test Method: AASHTO T315-16: Standard Method of Test for Determining the Rheological Properties of Asphalt Binder Using a Dynamic Shear Rheometer (DSR) (Dynamic Shear)
Verified Date: 07/27/2021
Date Tested: 07/23/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Boulevard, Room 225,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: Per 2018 Standard Specifications +3C
Test Result Compliance: complies
Additional Comments When Verified:
Phase PAV residue
Test Plate Diameter 8 mm
Test Gap 2 mm
Test Frequency 10.0 rad/s
Strain Amplitude 1.00 %
Stress Amplitude 41.814 kPa
Phase Angle (δ) (for the 10 cycles) 62.0 degree
Complex Modulus (G*) (for the 10 measurements) 4181.047 kPa
Test Temperature (Specimen 1) 31.0 C
(G*) x sin(δ)= 3692 kPa