Print Report | Back to Sample Detail

Sample Record for 2021-05-17-38

Note: Fields with no data or with a value of "Unknown" will not be displayed on the print out.

Project Information

Project ID: 44444 DEA: ASCP EFIS: ASCP QA Service Level:
DIST-CO-RTE-PM: 59---
Work Description: Special project for submitting Sample information for Asphalt Supplier Certification Program.
Location Description:
Contractor Name: Unknown
Contractor Address: Unknown
Resident Engineer: Unknown Structure Rep.: Unknown

Sample Information

DIME Sample ID: 2021-05-17-38
TL Number from the TL Form:
Sample Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Sample Organization Contact: (916) 227-7302
Type of Sample: Verification
Type of Material: Asphalt Binder
Sample Taken Date: 05/17/2021
Date that the sample was received by the laboratory/organization performing the testing: 06/17/2021
The quantity of what the sample constitutes: 1 out of 4
A brief description of the sample: Binder
From where was the sample collected: Manufacturer
Laboratory sample identification: 05172-4
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: PNAC LLC, Marathon Petroleum

Material Information

Performance Grade: PG 64-28 M
Modified: Yes
Lot number:
Sublot number:
Tank number: 4
Time of sample:
HMA Supplier:
Certified Asphalt Supplier: PNAC LLC - Fernley NV
Multigrade: No
Multigrade Type:
Asphalt Binder Mix Number:

Test Results

Test 1 of 5

DIME Test ID: 2021-05-17-38-1
Test Method: AASHTO T240-17: Standard Method of Test for Effect of Heat and Air on a Moving Film of Asphalt Binder (Rolling Thin-Film Oven Test)
Verified Date: 06/28/2021
Date Tested: 06/25/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Boulevard, Room 225,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test:
Test Result Compliance: complies
Additional Comments When Verified:
Is mass change based on one or two containers? Two
Any material loss from containers during heating process/testing? No
Mass of empty container #1 173.715 grams
Mass of empty container #2 179.440 grams
Mass of container #1 before test (m1i) 208.894 grams
Mass of container #2 before test (m2i) 214.490 grams
Mass of container #1 after test (m1f) 208.728 grams
Mass of container #2 after test (m2f) 214.329 grams
Average mass change -0.466 percent

Test 2 of 5

DIME Test ID: 2021-05-17-38-2
Test Method: AASHTO T301-13: Standard Method of Test for Elastic Recovery Test of Asphalt Materials by Means of a Ductilometer
Verified Date: 06/28/2021
Date Tested: 06/28/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Boulevard, Room 225,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test:
Test Result Compliance: complies
Additional Comments When Verified:
Final Reading from the testing machine (X) 2 cm
% Elongation Recovery 90 %

Test 3 of 5

DIME Test ID: 2021-05-17-38-3
Test Method: AASHTO T315-16: Standard Method of Test for Determining the Rheological Properties of Asphalt Binder Using a Dynamic Shear Rheometer (DSR) (Dynamic Shear)
Verified Date: 06/28/2021
Date Tested: 06/25/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Boulevard, Room 225,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: ORIG
Test Result Compliance: complies
Additional Comments When Verified:
Phase Original binder
Test Plate Diameter 25 mm
Test Gap 1 mm
Test Frequency 10.0 rad/s
Strain Amplitude 12.00 %
Stress Amplitude 0.131 kPa
Phase Angle (δ) (for the 10 cycles) 70.9 degree
Complex Modulus (G*) (for the 10 measurements) 1.089 kPa
Test Temperature (Specimen 1) 64.0 C
Dynamic Shear, G*/sin(δ) 1.15 kPa

Test 4 of 5

DIME Test ID: 2021-05-17-38-4
Test Method: AASHTO T315-16: Standard Method of Test for Determining the Rheological Properties of Asphalt Binder Using a Dynamic Shear Rheometer (DSR) (Dynamic Shear)
Verified Date: 06/28/2021
Date Tested: 06/25/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Boulevard, Room 225,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: RTFO
Test Result Compliance: complies
Additional Comments When Verified:
Phase RTFO residue
Test Plate Diameter 25 mm
Test Gap 1 mm
Test Frequency 10.0 rad/s
Strain Amplitude 10.00 %
Stress Amplitude 0.215 kPa
Phase Angle (δ) (for the 10 cycles) 69.2 degree
Complex Modulus (G*) (for the 10 measurements) 2.155 kPa
Test Temperature (Specimen 1) 64.0 C
Dynamic Shear, G*/sin(δ) 2.31 kPa

Test 5 of 5

DIME Test ID: 2021-05-17-38-7
Test Method: AASHTO T315-16: Standard Method of Test for Determining the Rheological Properties of Asphalt Binder Using a Dynamic Shear Rheometer (DSR) (Dynamic Shear)
Verified Date: 06/28/2021
Date Tested: 06/25/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Boulevard, Room 225,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: RTFO+6, Delta @ 2.2 kPa = 69.4
Test Result Compliance: complies
Additional Comments When Verified:
Phase RTFO residue
Test Plate Diameter 25 mm
Test Gap 1 mm
Test Frequency 10.0 rad/s
Strain Amplitude 10.00 %
Stress Amplitude 0.120 kPa
Phase Angle (δ) (for the 10 cycles) 70.4 degree
Complex Modulus (G*) (for the 10 measurements) 1.198 kPa
Test Temperature (Specimen 1) 70.0 C
Dynamic Shear, G*/sin(δ) 1.27 kPa