Print Report | Back to Test Summary

Testing Report for 2021-05-16-10-6

Note: Fields with no data or with a value of "Unknown" will not be displayed on the print out.

Project Information

DEA: 061A8404
EFIS: 0620000083
Project ID: 215716
QA Service Level: 1
DIST-CO-RTE-PM: 06--,241-
Work Description:
Location Description:
Contractor Name: Unknown
Contractor Address: Unknown
Resident Engineer: John Carter
Structure Rep.: Unknown

Sample Information

DIME Sample ID: 2021-05-16-10
TL Number from the TL Form: 040434
Sample Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Sample Organization Contact: (916) 227-7302
Type of Sample: Acceptance
Type of Material: Asphalt Binder
Sample Taken Date: 5/16/2021
Date that the sample was received by the laboratory/organization performing the testing: 5/26/2021
The quantity of what the sample constitutes: 1can
A brief description of the sample: binder
From where was the sample collected: Source
Laboratory sample identification:
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: San Joaquin Refinery

Material Information

Performance Grade: PG 70-10
Modified: No
Lot number: 1
Sublot number: 1
Tank number:
Time of sample:
HMA Supplier: Vulcan Ashlan
Asphalt Binder Supplier: San Joaquin Refinery - Bakersfield CA
Multigrade: No
Multigrade Type:

Test Information

DIME Test ID: 2021-05-16-10-6
Test Method: AASHTO T315-16: Standard Method of Test for Determining the Rheological Properties of Asphalt Binder Using a Dynamic Shear Rheometer (DSR) (Dynamic Shear)
Date Tested: 6/3/2021
Verified Date: 6/3/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Blvd,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email:
Organization Phone: (916) 227-7302
General Comments for this Test: Per 2018 Standard Specifications PAV+3
Test Result Compliance: complies
Additional Comments When Verified :

Submitted Test Results

Phase: PAV residue
Test Plate Diameter: 8 mm
Test Gap: 2 mm
Test Frequency: 10.0 rad/s
Strain Amplitude: 1.00 %
Stress Amplitude: 39.047 kPa
Phase Angle (δ) (for the 10 cycles): 62.6 degree
Complex Modulus (G*) (for the 10 measurements): 3904.487 kPa
Test Temperature (Specimen 1): 37.0 C
(G*) x sin(δ)=: 3466 kPa