Unit system used?
|
SI Units
|
Number of specimens
|
6
|
Test performed
|
With no density determined
|
Capped in accordance with?
|
ASTM C617/CTM521
|
Average diameter of cylinder 1
|
6.02 mm
|
Average diameter of cylinder 2
|
6.01 mm
|
Average diameter of cylinder 3
|
6.01 mm
|
Average diameter of cylinder 4
|
6.02 mm
|
Average diameter of cylinder 5
|
6.02 mm
|
Average diameter of cylinder 6
|
6.01 mm
|
Cross sectional area of cylinder 1
|
28.46 mm^2
|
Cross sectional area of cylinder 2
|
28.37 mm^2
|
Cross sectional area of cylinder 3
|
28.37 mm^2
|
Cross sectional area of cylinder 4
|
28.46 mm^2
|
Cross sectional area of cylinder 5
|
28.46 mm^2
|
Cross sectional area of cylinder 6
|
28.37 mm^2
|
Compressive strength (to nearest 0.1MPa)
|
1439.8 MPa
|
Maximum load on cylinder 1
|
41085 N
|
Maximum load on cylinder 2
|
42520 N
|
Maximum load on cylinder 3
|
41875 N
|
Maximum load on cylinder 4
|
41740 N
|
Maximum load on cylinder 5
|
42870 N
|
Maximum load on cylinder 6
|
35390 N
|
Type of fracture pattern of cylinder 1
|
2
|
Compressive strength of cylinder 1
|
1443.6 MPa
|
Compressive strength of cylinder 2
|
1498.8 MPa
|
Compressive strength of cylinder 3
|
1476 MPa
|
Compressive strength of cylinder 4
|
1466.6 MPa
|
Type of fracture pattern of cylinder 2
|
3
|
Compressive strength of cylinder 5
|
1506.3 MPa
|
Compressive strength of cylinder 6
|
1247.4 MPa
|
Type of fracture pattern of cylinder 3
|
3
|
Type of fracture pattern of cylinder 4
|
2
|
Type of fracture pattern of cylinder 5
|
3
|
Type of fracture pattern of cylinder 6
|
3
|
Comment on any defect in either specimen or caps (Max 250 Characters)
|
no data
|
Correction factor for cylinder 1
|
1
|
Correction factor for cylinder 2
|
1
|
Correction factor for cylinder 3
|
1
|
Correction factor for cylinder 4
|
1
|
Correction factor for cylinder 5
|
1
|
Correction factor for cylinder 6
|
1
|
Age of specimen
|
7 days
|
Age of specimen in hours
|
no data
|