Print Report | Back to Test Summary

Testing Report for 2021-02-08-25-5

Note: Fields with no data or with a value of "Unknown" will not be displayed on the print out.

Project Information

Project ID: 44444 DEA: ASCP EFIS: ASCP QA Service Level:
DIST-CO-RTE-PM: 59---
Work Description: Special project for submitting Sample information for Asphalt Supplier Certification Program.
Location Description:
Contractor Name: Unknown
Contractor Address: Unknown
Resident Engineer: Unknown Structure Rep.: Unknown

Sample Information

DIME Sample ID: 2021-02-08-25
TL Number from the TL Form:
Sample Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Sample Organization Contact: (916) 227-7302
Type of Sample: Verification
Type of Material: Asphalt Binder
Sample Taken Date: 02/08/2021
Date that the sample was received by the laboratory/organization performing the testing: 03/22/2021
The quantity of what the sample constitutes: 1 OF 2 CANS
A brief description of the sample: COC Sample
From where was the sample collected: Manufacturer
Laboratory sample identification:
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: San Joaquin Refining Co Inc

Material Information

Performance Grade: PG 58-16
Modified: No
Lot number: 21581604
Sublot number:
Tank number: 2002
Time of sample: ?
HMA Supplier:
Asphalt Binder Supplier: San Joaquin Refinery - Bakersfield CA
Multigrade:
Multigrade Type:

Test Information

DIME Test ID: 2021-02-08-25-1
Test Method: AASHTO T240-17: Standard Method of Test for Effect of Heat and Air on a Moving Film of Asphalt Binder (Rolling Thin-Film Oven Test)
Verified Date: 03/26/2021
Date Tested: 03/24/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Blvd,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: Per 2018 standard specifications
Test Result Compliance: complies
Additional Comments When Verified :

Submitted Test Results

Phase PAV residue
Test Plate Diameter 8 mm
Test Gap 2 mm
Test Frequency 10.0 rad/s
Strain Amplitude 1.00 %
Stress Amplitude 54.976 kPa
Phase Angle (δ) (for the 10 cycles) 56.4 degree
Complex Modulus (G*) (for the 10 measurements) 5496.679 kPa
Test Temperature 25.0 C
(G*) x sin(δ)= 4578 kPa