Print Report | Back to Test Summary

Testing Report for 2021-02-08-22-4

Note: Fields with no data or with a value of "Unknown" will not be displayed on the print out.

Project Information

Project ID: 44444 DEA: ASCP EFIS: ASCP QA Service Level:
Work Description: Special project for submitting Sample information for Asphalt Supplier Certification Program.
Location Description:
Contractor Name: Unknown
Contractor Address: Unknown
Resident Engineer: Unknown Structure Rep.: Unknown

Sample Information

DIME Sample ID: 2021-02-08-22
TL Number from the TL Form:
Sample Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Sample Organization Contact: (916) 227-7302
Type of Sample: Verification
Type of Material: Asphalt Binder
Sample Taken Date: 02/08/2021
Date that the sample was received by the laboratory/organization performing the testing: 03/08/2021
The quantity of what the sample constitutes: 1 of 3 cans
A brief description of the sample: Asphalt Binder Multi-Grade 64-10/16
From where was the sample collected: Manufacturer
Laboratory sample identification: AC-1025-WS
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: VSS Emultech

Material Information

Performance Grade: PG 64-16
Modified: No
Lot number:
Sublot number:
Tank number: 2002
Time of sample: 8am
HMA Supplier:
Asphalt Binder Supplier: VSS Emultech - West Sacramento CA
Multigrade Type:

Test Information

DIME Test ID: 2021-02-08-22-1
Test Method: AASHTO T240-17: Standard Method of Test for Effect of Heat and Air on a Moving Film of Asphalt Binder (Rolling Thin-Film Oven Test)
Verified Date: 03/19/2021
Date Tested: 03/17/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Blvd,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email:
Organization Phone: (916) 227-7302
General Comments for this Test: as per 2018 standard specs
Test Result Compliance: complies
Additional Comments When Verified :

Submitted Test Results

Phase RTFO residue
Test Plate Diameter 25 mm
Test Gap 1 mm
Test Frequency 10.0 rad/s
Strain Amplitude 10.00 %
Stress Amplitude 0.391 kPa
Phase Angle (δ) (for the 10 cycles) 82.6 degree
Complex Modulus (G*) (for the 10 measurements) 3.910 kPa
Test Temperature 64.0 C
Dynamic Shear, G*/sin(δ) 3.94 kPa