Print Report | Back to Test Summary

Testing Report for 2020-11-02-24-4

Note: Fields with no data or with a value of "Unknown" will not be displayed on the print out.

Project Information

Project ID: 44444 DEA: ASCP EFIS: ASCP QA Service Level:
Work Description: Special project for submitting Sample information for Asphalt Supplier Certification Program.
Location Description:
Contractor Name: Unknown
Contractor Address: Unknown
Resident Engineer: Unknown Structure Rep.: Unknown

Sample Information

DIME Sample ID: 2020-11-02-24
TL Number from the TL Form:
Sample Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Sample Organization Contact: (916) 227-7302
Type of Sample: Verification
Type of Material: Asphalt Binder
Sample Taken Date: 11/02/2020
Date that the sample was received by the laboratory/organization performing the testing: 12/08/2020
The quantity of what the sample constitutes: 1 CAN
A brief description of the sample: ASPHALT BINDER
From where was the sample collected: Manufacturer
Laboratory sample identification: 7622PM-110220
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: Valero - Pittsburg

Material Information

Performance Grade: PG 76-22 M
Modified: Yes
Lot number:
Sublot number:
Tank number:
Time of sample:
HMA Supplier:
Asphalt Binder Supplier:
Multigrade Type:

Test Information

DIME Test ID: 2020-11-02-24-1
Test Method: AASHTO T240-17: Standard Method of Test for Effect of Heat and Air on a Moving Film of Asphalt Binder (Rolling Thin-Film Oven Test)
Verified Date: 12/21/2020
Date Tested: 12/10/2020
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Blvd,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email:
Organization Phone: (916) 227-7302
General Comments for this Test: as per 2018 standard specs
Test Result Compliance: complies
Additional Comments When Verified :

Submitted Test Results

Phase RTFO residue
Test Plate Diameter 25 mm
Test Gap 1 mm
Test Frequency 10.0 rad/s
Strain Amplitude 10.00 %
Stress Amplitude 0.291 kPa
Phase Angle (δ) (for the 10 cycles) 63.5 degree
Complex Modulus (G*) (for the 10 measurements) 2.912 kPa
Test Temperature 76.0 C
Dynamic Shear, G*/sin(δ) 3.25 kPa