Project Information

Project ID: 55555 DEA: AMRL EFIS: AMRL QA Service Level:
DIST-CO-RTE-PM: 59---
Work Description: Special project for submitting Sample information for AASHTO Materials Reference Laboratory (AMRL).
Location Description:
Contractor Name: Unknown
Contractor Address: Unknown
Resident Engineer: Unknown Structure Rep.: Unknown

Sample Information

DIME Sample ID: 2020-11-25-3
TL Number from the TL Form: 308
Sample Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Sample Organization Contact: (916) 227-7302
Type of Sample: Proficiency
Type of Material: Asphalt Binder
Sample Taken Date: 11/25/2020
Date that the sample was received by the laboratory/organization performing the testing: 11/30/2020
The quantity of what the sample constitutes: 1 can, Due DEC, 25
A brief description of the sample: Asphalt Binder PG 70-22 ER
From where was the sample collected: Source
Laboratory sample identification:
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: AASHTO resource

Material Information

Performance Grade: PG 76-22 M
Modified: Yes
Lot number:
Sublot number:
Tank number:
Time of sample:
HMA Supplier:
Asphalt Binder Supplier:
Multigrade:
Multigrade Type:

Test Information

DIME Test ID: 2020-11-25-3-1
Test Method: AASHTO T240-17: Standard Method of Test for Effect of Heat and Air on a Moving Film of Asphalt Binder (Rolling Thin-Film Oven Test)
Verified Date: 12/09/2020
Date Tested: 12/01/2020
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Blvd,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: Per 2018 Standard Specifications
Test Result Compliance: complies
Additional Comments When Verified :

Submitted Test Results

Phase Original binder
Test Plate Diameter 25 mm
Test Gap 1 mm
Test Frequency 10.0 rad/s
Strain Amplitude 12.00 %
Stress Amplitude 0.151 kPa
Phase Angle (δ) (for the 10 cycles) 76.6 degree
Complex Modulus (G*) (for the 10 measurements) 1.258 kPa
Test Temperature 70.0 C
Dynamic Shear, G*/sin(δ) 1.29 kPa