Print Report | Back to Test Summary

Testing Report for 2021-01-11-13-5

Note: Fields with no data or with a value of "Unknown" will not be displayed on the print out.

Project Information

Project ID: 44444 DEA: ASCP EFIS: ASCP QA Service Level:
DIST-CO-RTE-PM: 59---
Work Description: Special project for submitting Sample information for Asphalt Supplier Certification Program.
Location Description:
Contractor Name: Unknown
Contractor Address: Unknown
Resident Engineer: Unknown Structure Rep.: Unknown

Sample Information

DIME Sample ID: 2021-01-11-13
TL Number from the TL Form:
Sample Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Sample Organization Contact: (916) 227-7302
Type of Sample: Verification
Type of Material: Asphalt Binder
Sample Taken Date: 01/11/2021
Date that the sample was received by the laboratory/organization performing the testing: 02/17/2021
The quantity of what the sample constitutes: 1 of 4 cans
A brief description of the sample: received 4 cans of PG64-10
From where was the sample collected: Manufacturer
Laboratory sample identification: 1720641001212
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: Seventeen Twenty Oil Company, Corona CA

Material Information

Performance Grade: PG 64-10
Modified: No
Lot number:
Sublot number:
Tank number:
Time of sample:
HMA Supplier:
Asphalt Binder Supplier:
Multigrade:
Multigrade Type:

Test Information

DIME Test ID: 2021-01-11-13-1
Test Method: AASHTO T240-17: Standard Method of Test for Effect of Heat and Air on a Moving Film of Asphalt Binder (Rolling Thin-Film Oven Test)
Verified Date: 03/01/2021
Date Tested: 02/18/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Blvd,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: Per 2018 standard specifications
Additional Comments When Verified:

Submitted Test Results

Phase PAV residue
Test Plate Diameter 8 mm
Test Gap 2 mm
Test Frequency 10.0 rad/s
Strain Amplitude 1.00 %
Stress Amplitude 21.859 kPa
Phase Angle (δ) (for the 10 cycles) 52.6 degree
Complex Modulus (G*) (for the 10 measurements) 2185.876 kPa
Test Temperature 31.0 C
(G*) x sin(δ)= 1736 kPa