Sample Record for 2021-02-01-11

Note: Fields with no data or with a value of "Unknown" will not be displayed on the print out.

Project Information

Project ID: 55555 DEA: AMRL EFIS: AMRL QA Service Level:
DIST-CO-RTE-PM: 59---
Work Description: Special project for submitting Sample information for AASHTO Materials Reference Laboratory (AMRL).
Location Description:
Contractor Name: Unknown
Contractor Address: Unknown
Resident Engineer: Unknown Structure Rep.: Unknown

Sample Information

DIME Sample ID: 2021-02-01-11
TL Number from the TL Form:
Sample Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Sample Organization Contact: (916) 227-7302
Type of Sample: Proficiency
Type of Material: Asphalt Binder
Sample Taken Date: 02/01/2021
Date that the sample was received by the laboratory/organization performing the testing: 02/04/2021
The quantity of what the sample constitutes: 1 can, Due Febraury 25
A brief description of the sample: Asphalt Binder OREGON COOP
From where was the sample collected: Manufacturer
Laboratory sample identification: 310
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: PNAC

Material Information

Performance Grade: PG 64-28 M
Modified: Yes
Lot number:
Sublot number:
Tank number:
Time of sample:
HMA Supplier:
Certified Asphalt Supplier:
Multigrade:
Multigrade Type:
Asphalt Binder Mix Number:

Test Results

Test 1 of 7

DIME Test ID: 2021-02-01-11-1
Test Method: AASHTO T240-17: Standard Method of Test for Effect of Heat and Air on a Moving Film of Asphalt Binder (Rolling Thin-Film Oven Test)
Verified Date: 03/01/2021
Date Tested: 02/22/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Boulevard, Room 225,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: Per 2018 standard specification
Test Result Compliance: complies
Additional Comments When Verified:
Is mass change based on one or two containers? Two
Any material loss from containers during heating process/testing? no data
Mass of empty container #1 172.666 grams
Mass of empty container #2 179.011 grams
Mass of container #1 before test (m1i) 207.765 grams
Mass of container #2 before test (m2i) 213.816 grams
Mass of container #1 after test (m1f) 207.608 grams
Mass of container #2 after test (m2f) 213.667 grams
Average mass change -0.438 percent

Test 2 of 7

DIME Test ID: 2021-02-01-11-2
Test Method: AASHTO T301-13: Standard Method of Test for Elastic Recovery Test of Asphalt Materials by Means of a Ductilometer
Verified Date: 03/01/2021
Date Tested: 02/23/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Boulevard, Room 225,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: Per 2018 Standard Test Specifications
Test Result Compliance: not applicable
Additional Comments When Verified:
Final Reading from the testing machine (X) 3 cm
% Elongation Recovery 85 %

Test 3 of 7

DIME Test ID: 2021-02-01-11-3
Test Method: AASHTO T315-16: Standard Method of Test for Determining the Rheological Properties of Asphalt Binder Using a Dynamic Shear Rheometer (DSR) (Dynamic Shear)
Verified Date: 03/01/2021
Date Tested: 02/22/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Boulevard, Room 225,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test:
Test Result Compliance: not applicable
Additional Comments When Verified:
Phase Original binder
Test Plate Diameter 25 mm
Test Gap 1 mm
Test Frequency 10.0 rad/s
Strain Amplitude 12.00 %
Stress Amplitude 0.151 kPa
Phase Angle (δ) (for the 10 cycles) 71.8 degree
Complex Modulus (G*) (for the 10 measurements) 1.261 kPa
Test Temperature (Specimen 1) 64.0 C
Dynamic Shear, G*/sin(δ) 1.33 kPa

Test 4 of 7

DIME Test ID: 2021-02-01-11-4
Test Method: AASHTO T315-16: Standard Method of Test for Determining the Rheological Properties of Asphalt Binder Using a Dynamic Shear Rheometer (DSR) (Dynamic Shear)
Verified Date: 03/01/2021
Date Tested: 03/22/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Boulevard, Room 225,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test:
Test Result Compliance: not applicable
Additional Comments When Verified:
Phase RTFO residue
Test Plate Diameter 25 mm
Test Gap 1 mm
Test Frequency 10.0 rad/s
Strain Amplitude 10.00 %
Stress Amplitude 0.296 kPa
Phase Angle (δ) (for the 10 cycles) 65.6 degree
Complex Modulus (G*) (for the 10 measurements) 2.961 kPa
Test Temperature (Specimen 1) 64.0 C
Dynamic Shear, G*/sin(δ) 3.25 kPa

Test 5 of 7

DIME Test ID: 2021-02-01-11-5
Test Method: AASHTO T315-16: Standard Method of Test for Determining the Rheological Properties of Asphalt Binder Using a Dynamic Shear Rheometer (DSR) (Dynamic Shear)
Verified Date: 03/01/2021
Date Tested: 02/23/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Boulevard, Room 225,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test:
Test Result Compliance: not applicable
Additional Comments When Verified:
Phase PAV residue
Test Plate Diameter 8 mm
Test Gap 2 mm
Test Frequency 10.0 rad/s
Strain Amplitude 1.00 %
Stress Amplitude 28.036 kPa
Phase Angle (δ) (for the 10 cycles) 46.4 degree
Complex Modulus (G*) (for the 10 measurements) 2803.587 kPa
Test Temperature (Specimen 1) 22.0 C
(G*) x sin(δ)= 2030 kPa

Test 6 of 7

DIME Test ID: 2021-02-01-11-6
Test Method: AASHTO T313-19: Standard Method of Test for Determining the Flexural Creep Stiffness of Asphalt Binder Using the Bending Beam Rheometer (BBR)
Verified Date: 03/01/2021
Date Tested: 02/23/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Boulevard, Room 225,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: Per 2018 Standard Test Specifications
Test Result Compliance: not applicable
Additional Comments When Verified:
Minimum test bath temperature at 240 s -18.0 C
Maximum test bath temperature at 240 s -18.0 C
Time of test load application no data HH:MM:SS
File name of test data no data
Time beam in bath no data
Time test started no data HH:MM:SS
Flags issued by software during test no data
Correlation coefficient (R²) 0
Regression coefficient a no data
Regression coefficient b no data
Regression coefficient c no data
Load at time 0.0 0.0 mN
Deflection at time 0.0 s 0.000 µm
Load at time 0.5 s 0.0 mN
Deflection at time 0.5 s 0.000 µm
Load at 60.0 s 0.0 mN
Beam deflection 60.0 s 0.000 µm
Measured Stiffness Modulus 60.0 s 119.000 mPa
Estimated Stiffness Modulus 60.0 s 119.000 mPa
Difference between stiffness moduli 60.0 s no data
Estimated m-value 60.0 s 0.355

Test 7 of 7

DIME Test ID: 2021-02-01-11-7
Test Method: AASHTO T350-19: Multiple Stress Creep Recovery (MSCR) Test of Asphalt Binder Using a Dynamic Shear Rheometer (DSR) (Multiple Stress Creep Recovery)
Verified Date: 03/01/2021
Date Tested: 02/22/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Boulevard, Room 225,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test:
Test Result Compliance: not applicable
Additional Comments When Verified:
PG test temperature 64.0 C
Average percent recovery at 0.1 kPa 57.0500 %
Average percent recovery at 3.2 kPa 26.2800 %
Nonrecoverable creep compliance 0.9119
Nonrecoverable creep compliance 1.6827
Percent difference between nonrecoverable creep compliance at 0.1 kPa and 3.2 kPa 84.5300 %