Print Report | Back to Test Summary

Testing Report for 2020-12-02-12-3

Note: Fields with no data or with a value of "Unknown" will not be displayed on the print out.

Project Information

Project ID: 44444 DEA: ASCP EFIS: ASCP QA Service Level:
DIST-CO-RTE-PM: 59---
Work Description: Special project for submitting Sample information for Asphalt Supplier Certification Program.
Location Description:
Contractor Name: Unknown
Contractor Address: Unknown
Resident Engineer: Unknown Structure Rep.: Unknown

Sample Information

DIME Sample ID: 2020-12-02-12
TL Number from the TL Form:
Sample Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Sample Organization Contact: (916) 227-7302
Type of Sample: Verification
Type of Material: Asphalt Binder
Sample Taken Date: 12/02/2020
Date that the sample was received by the laboratory/organization performing the testing: 01/25/2021
The quantity of what the sample constitutes: 1 of 3 cans
A brief description of the sample: COC Sample
From where was the sample collected: Manufacturer
Laboratory sample identification: 20701032
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: San Joaquin Refining Co Inc

Material Information

Performance Grade: PG 70-10
Modified: No
Lot number:
Sublot number:
Tank number: 9001
Time of sample:
HMA Supplier:
Asphalt Binder Supplier:
Multigrade:
Multigrade Type:

Test Information

DIME Test ID: 2020-12-02-12-1
Test Method: AASHTO T240-17: Standard Method of Test for Effect of Heat and Air on a Moving Film of Asphalt Binder (Rolling Thin-Film Oven Test)
Verified Date: 01/29/2021
Date Tested: 01/26/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Blvd,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: Per 2018 Standard Specifications
Additional Comments When Verified :

Submitted Test Results

Phase Original binder
Test Plate Diameter 25 mm
Test Gap 1 mm
Test Frequency 10.0 rad/s
Strain Amplitude 12.00 %
Stress Amplitude 0.140 kPa
Phase Angle (δ) (for the 10 cycles) 89.5 degree
Complex Modulus (G*) (for the 10 measurements) 1.168 kPa
Test Temperature 70.0 C
Dynamic Shear, G*/sin(δ) 1.17 kPa