Print Report | Back to Test Summary

Testing Report for 2019-09-17-1-3

Note: Fields with no data or with a value of "Unknown" will not be displayed on the print out.

Project Information

DEA: No Project QA Service Level:
DIST-CO-RTE-PM: ---
Work Description: Special project identifier for material not associated with a project
Location Description:
Contractor Name: Unknown
Contractor Address: Unknown
Resident Engineer: Unknown Structure Rep.: Unknown

Sample Information

DIME Sample ID: 2019-09-17-1
TL Number from the TL Form:
Sample Submitted By Organization: Caltrans Vallejo Field Laboratory
Sample Organization Contact: (510) 774-6009
Type of Sample: Quality Assurance
Type of Material: SMTL TM1 - Elastomeric Bearing Pad
Sample Taken Date: 09/17/2019
Date that the sample was received by the laboratory/organization performing the testing: 09/20/2019
The quantity of what the sample constitutes: 1 Batch
A brief description of the sample: 1/2 " neo bearing pad
From where was the sample collected: Fabricator
Laboratory sample identification:
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: Cal-Neva

Material Information

Mfg. Lot Number(s): 41-1200-12
Material/Compound/Elastomer ID: Neoprene Pad 55
Samples Representing: 45
Description (size): 1
Comments:
Description (Number of Shims): 0
Type of Bearing Pad: Plain
Description (Thickness of Shims): NA
Manufacturer(s): GRT Rubber
Batch Number: BP056206

Test Information

DIME Test ID: 2019-09-17-1-1
Test Method: ASTM D2240-05re10: Standard Test Method for Rubber Property - Durometer Hardness
Verified Date: 09/27/2019
Date Tested: 09/25/2019
Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Organization Address: 5900 Folsom Blvd,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: paul.lukkarila@dot.ca.gov
Organization Phone: (916) 227-7253
General Comments for this Test:
Additional Comments When Verified:

Submitted Test Results

Number of specimens tested 3
UTM 2kip
Humidity 50.00 %
Temperature 72 F
Sample 1 Median Thickness 0.069
Sample 1 Tear Strength 228.4
Sample 2 Median Thickness 0.073
Sample 2 Tear Strength 237.1
Sample 3 Median Thickness 0.068
Sample 3 Tear Strength 233.2
Median of the Tear Strength Values 233.2 lb/in