Print Report | Back to Test Summary

Testing Report for 2019-09-17-1-2

Note: Fields with no data or with a value of "Unknown" will not be displayed on the print out.

Project Information

DEA: No Project QA Service Level:
Work Description: Special project identifier for material not associated with a project
Location Description:
Contractor Name: Unknown
Contractor Address: Unknown
Resident Engineer: Unknown Structure Rep.: Unknown

Sample Information

DIME Sample ID: 2019-09-17-1
TL Number from the TL Form:
Sample Submitted By Organization: Caltrans Vallejo Field Laboratory
Sample Organization Contact: (510) 774-6009
Type of Sample: Quality Assurance
Type of Material: SMTL TM1 - Elastomeric Bearing Pad
Sample Taken Date: 09/17/2019
Date that the sample was received by the laboratory/organization performing the testing: 09/20/2019
The quantity of what the sample constitutes: 1 Batch
A brief description of the sample: 1/2 " neo bearing pad
From where was the sample collected: Fabricator
Laboratory sample identification:
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: Cal-Neva

Material Information

Mfg. Lot Number(s): 41-1200-12
Material/Compound/Elastomer ID: Neoprene Pad 55
Samples Representing: 45
Description (size): 1
Description (Number of Shims): 0
Type of Bearing Pad: Plain
Description (Thickness of Shims): NA
Manufacturer(s): GRT Rubber
Batch Number: BP056206

Test Information

DIME Test ID: 2019-09-17-1-1
Test Method: ASTM D2240-05re10: Standard Test Method for Rubber Property - Durometer Hardness
Verified Date: 09/27/2019
Date Tested: 09/25/2019
Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Organization Address: 5900 Folsom Blvd,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email:
Organization Phone: (916) 227-7253
General Comments for this Test:
Additional Comments When Verified:

Submitted Test Results

UTM 2kip
Humidity 50.00 %
Temperature 72 F
Sample 1 Median Thickness 0.071
Sample 1 Thickness all Within 0.003 inch? Yes
Sample 1 Ultimate Tensile 1489.05 lbf/in^2
Sample 1 Elongation (350% Min) Pass
Sample 2 Median Thickness 0.067
Sample 2 Thickness all Within 0.003 inch? Yes
Sample 2 Ultimate Tensile 2711.2 lbf/in^2
Sample 2 Elongation (350% Min) Pass
Sample 3 Median Thickness 0.07
Sample 3 Thickness all Within 0.003 inch? Yes
Sample 3 Ultimate Tensile 2678 lbf/in^2
Sample 3 Elongation (350% Min) Pass
Sample 4 Median Thickness 0.071
Sample 4 Thickness all Within 0.003 inch? Yes
Sample 4 Ultimate Tensile 2750.14 lbf/in^2
Sample 4 Elongation (350% Min) Pass
Sample 5 Median Thickness 0.07
Sample 5 Thickness all Within 0.003 inch? Yes
Sample 5 Ultimate Tensile 1863.94 lbf/in^2
Sample 5 Elongation (350% Min) Pass
Median of the Ultimate Tensile Values 2678 lbf/in^2