Sample Record for 2019-05-01-30


Project Information

Project ID: 66667 DEA: JMFPP EFIS: 0019000043 QA Service Level:
DIST-CO-RTE-PM: 59---
Work Description: Special project for submitting Sample information for JMF Prequalification Program.
Location Description:
Contractor Name: Contractor Address:
Resident Engineer: Unknown Structure Rep.: Unknown

Sample Information

DIME Sample ID: 2019-05-01-30
TL Number from the TL Form:
Sample Submitted By Organization: CT HQ - Hot Mix Asphalt Laboratory
Sample Organization Contact: (916) 227-7302
Type of Sample: Quality Control
Type of Material: Aggregate
Sample Taken Date: 05/01/2019
Date that the sample was received by the laboratory/organization performing the testing:
The quantity of what the sample constitutes: 1
A brief description of the sample: 1/2 " HMA-SP w/15% RAP
From where was the sample collected: Source
Laboratory sample identification:
Structure unique identifier:
Structure name:

Material Information

Source Identification (SMARA or name of Pit): 91-10-0006::AVENAL AGGREGATES
The fabricator's/manufacturer's product name for the sample:
The fabricator/manufacturer designation for the sample:
The plant number:
A detailed description of where the material sample was collected: Stockpile @ Plant
Where the material sample would have been placed if not sampled:
Primary Aggregate Nominal Size: 1/2 inch
The concrete mix design number:
Lot number:
Sublot number:

Test Results

Test Information 4 of 9

DIME Test ID: 2019-05-01-30-4
Test Method: AASHTO T96-02r10: Standard Method of Test for Resistance to Degradation of Small-Size Coarse Aggregate by Abrasion and Impact in the Los Angeles Machine (Los Angeles Rattler)
Verified Date: 08/06/2019
Date Tested: 05/01/2019
Submitted By Organization: CT HQ - Hot Mix Asphalt Laboratory
Organization Address: 5900 Folsom Blvd
Test General Comments: T-96
Additional Comments When Verified:
Grading designation B
Percent loss after 100 revolutions 5 %
Percent loss after 500 revolutions 21 %