Print Report | Back to Sample Detail

Sample Record for 2016-10-10-3

Note: Fields with no data or with a value of "Unknown" will not be displayed on the print out.

Project Information

Project ID: 8196 DEA: 59912684 QA Service Level: 1
DIST-CO-RTE-PM: 59---
Work Description:
Location Description:
Contractor Name: Unknown
Contractor Address: Unknown
Resident Engineer: Unknown Structure Rep.: Unknown

Sample Information

DIME Sample ID: 2016-10-10-3
TL Number from the TL Form: NA
Sample Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Sample Organization Contact: (530) 329-6527
Type of Sample: Quality Assurance
Type of Material: SMTL TM1 - Elastomeric Bearing Pad
Sample Taken Date: 10/10/2016
Date that the sample was received by the laboratory/organization performing the testing: 10/11/2016
The quantity of what the sample constitutes: Unknown
A brief description of the sample: Bearing Pad
From where was the sample collected: Source
Laboratory sample identification: Unknown
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: Warco

Material Information

Mfg. Lot Number(s): 9-22-16-1
Material/Compound/Elastomer ID: NA
Samples Representing: 1 roll
Description (size): .250 x 36
Comments: Unknown
Description (Number of Shims): 0
Type of Bearing Pad: Plain
Description (Thickness of Shims): NA
Manufacturer(s): Warco
Batch Number: NA

Test Results

Test 1 of 4

DIME Test ID: 2016-10-10-3-1
Test Method: ASTM D2240-05re10: Standard Test Method for Rubber Property - Durometer Hardness
Verified Date: 10/18/2016
Date Tested: 10/13/2016
Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: joshua.moore@dot.ca.gov
Organization Phone: (530) 329-6527
General Comments for this Test:
Test Result Compliance:
Additional Comments When Verified:
Temperature 72 f
Humidity 50 %
Reading #1 55
Reading #2 55
Reading #3 56
Reading #4 56
Reading #5 55
Mean 55.4

Test 2 of 4

DIME Test ID: 2016-10-10-3-2
Test Method: ASTM D412-06a-re13: Standard Test Methods for Vulcanized Rubber and Thermoplastic Elastomers-Tension
Verified Date: 10/18/2016
Date Tested: 10/13/2016
Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: joshua.moore@dot.ca.gov
Organization Phone: (530) 329-6527
General Comments for this Test:
Test Result Compliance:
Additional Comments When Verified:
Number of specimens tested 3
Unit of the Ultimate Tensile Values lbf per sqr in
UTM 2KIP
Humidity 50 %
Temperature 72 F
Sample 1 Median Thickness 0.07 in
Sample 1 Thickness all Within 0.003 inch? Yes
Sample 1 Ultimate Tensile 2685.7 lbf/in^2
Sample 1 Elongation (350% Min) Pass
Sample 2 Median Thickness 0.073 in
Sample 2 Thickness all Within 0.003 inch? Yes
Sample 2 Ultimate Tensile 2732.2 lbf/in^2
Sample 2 Elongation (350% Min) Pass
Sample 3 Median Thickness 0.071 in
Sample 3 Thickness all Within 0.003 inch? Yes
Sample 3 Ultimate Tensile 2696.6 lbf/in^2
Sample 3 Elongation (350% Min) Pass
Median of the Ultimate Tensile Values 2696.6 lbf/in^2

Test 3 of 4

DIME Test ID: 2016-10-10-3-3
Test Method: ASTM D624-00-re12: Standard Test Method for Tear Strength of Conventional Vulcanized Rubber and Thermoplastic Elastomers
Verified Date: 10/18/2016
Date Tested: 10/13/2016
Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: joshua.moore@dot.ca.gov
Organization Phone: (530) 329-6527
General Comments for this Test:
Test Result Compliance:
Additional Comments When Verified:
Number of specimens tested 3
UTM no data
Humidity 50 %
Temperature 72 F
Sample 1 Median Thickness 0.075 in
Sample 1 Tear Strength 320 lbf / in
Sample 2 Median Thickness 0.067 in
Sample 2 Tear Strength 313.4 lbf / in
Sample 3 Median Thickness 0.066 in
Sample 3 Tear Strength 318.2 lbf / in
Median of the Tear Strength Values 318.2 lb/in

Test 4 of 4

DIME Test ID: 2016-10-10-3-4
Test Method: SMTL BILST-06: (Neoprene Verification) Bilstein Test
Verified Date: 10/18/2016
Date Tested: 10/17/2016
Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: joshua.moore@dot.ca.gov
Organization Phone: (530) 329-6527
General Comments for this Test:
Test Result Compliance: complies
Additional Comments When Verified:
Result Pass