Print Report | Back to Sample Detail

Sample Record for 2016-07-26-5

Note: Fields with no data or with a value of "Unknown" will not be displayed on the print out.

Project Information

Project ID: 8196 DEA: 59912684 QA Service Level: 1
DIST-CO-RTE-PM: 59---
Work Description:
Location Description:
Contractor Name: Unknown
Contractor Address: Unknown
Resident Engineer: Unknown Structure Rep.: Unknown

Sample Information

DIME Sample ID: 2016-07-26-5
TL Number from the TL Form: Unknown
Sample Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Sample Organization Contact: (916) 227-7253
Type of Sample: Quality Assurance
Type of Material: SMTL TM2 - Type B Elastomeric Joint Seal
Sample Taken Date: 07/26/2016
Date that the sample was received by the laboratory/organization performing the testing: 07/29/2016
The quantity of what the sample constitutes: 500ft
A brief description of the sample: Joint Seal
From where was the sample collected: Manufacturer
Laboratory sample identification: Unknown
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: Watson Bowman

Material Information

Mfg. Lot Number(s): 0716303
Manufacturer(s): Watson Bowman
Temperature: 72
Humidity: 50
Comments: Unknown
Joint Seal Size: 2.75

Test Results

Test 1 of 7

DIME Test ID: 2016-07-26-5-1
Test Method: CTM 673-July 2012: Method of Determining Movement Rating of Type B1 and B2 Preformed Elastomeric Joint Seals
Verified Date: 08/18/2016
Date Tested: 08/03/2016
Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Organization Address: 5900 Folsom Blvd,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: paul.lukkarila@dot.ca.gov
Organization Phone: (916) 227-7253
General Comments for this Test:
Test Result Compliance:
Additional Comments When Verified:
UTM 11KIP
Temperature 72 ?F
Humidity 50 %
Load at W1 50.1221 lbs
Width at 4 x Load at W1 1.21899 in
Nominal Width 2.75 in
Measured Maximum Uncompressed Width 2.924 in
Measured Minimum Uncompressed Width 2.8925 in
Minimum Uncompressed Width as Specified by the Manufacturer (MUWASBM) 2.867 in
Height of Contact Face 2.8185 in
Spec Minimum Uncompressed Width 2.867 in
Area (5 Times of the Height of Contact Face) 14.093 sqin
Half of the Spec Minimum Uncompressed Width 1.4335 in
85 Percent of the Spec Minimum Uncompressed Width 2.43695 in
3 Times of the Area 42.279 sqin
4 Times of the Load at W1 200.489 in
W1 (US Units) 2.437 in
W1 (Metric Units) 61.899 millimeters
W2 (US Units) 1.219 in
W2 (Metric Units) 30.962 millimeters
Satisfactory of MR of (US Units) 1.218 in
Satisfactory of MR of (Metric Units) 30.936 millimeters
Optional W1 Measurement 1 2.4586 in
Optional W1 Measurement 2 42.5609 sqin

Test 2 of 7

DIME Test ID: 2016-07-26-5-2
Test Method: ASTM D2240-05re10: Standard Test Method for Rubber Property - Durometer Hardness
Verified Date: 08/18/2016
Date Tested: 08/04/2016
Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Organization Address: 5900 Folsom Blvd,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: paul.lukkarila@dot.ca.gov
Organization Phone: (916) 227-7253
General Comments for this Test:
Test Result Compliance:
Additional Comments When Verified:
Temperature 74 f
Humidity 46 %
Reading #1 54
Reading #2 55
Reading #3 55
Reading #4 54
Reading #5 55
Mean 54.6

Test 3 of 7

DIME Test ID: 2016-07-26-5-3
Test Method: ASTM D412-06a-re13: Standard Test Methods for Vulcanized Rubber and Thermoplastic Elastomers—Tension
Verified Date: 08/18/2016
Date Tested: 08/04/2016
Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Organization Address: 5900 Folsom Blvd,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: paul.lukkarila@dot.ca.gov
Organization Phone: (916) 227-7253
General Comments for this Test:
Test Result Compliance:
Additional Comments When Verified:
UTM 2KIP
Humidity 46 %
Temperature 74 F
Sample 1 Median Thickness 0.079 in
Sample 1 Thickness all Within 0.003 inch? Yes
Sample 1 Ultimate Tensile 2272.7 lbf?in/in?
Sample 1 Elongation (350% Min) Pass
Sample 2 Median Thickness 0.079 in
Sample 2 Thickness all Within 0.003 inch? Yes
Sample 2 Ultimate Tensile 2424.2 lbf?in/in?
Sample 2 Elongation (350% Min) Pass
Sample 3 Median Thickness 0.078 in
Sample 3 Thickness all Within 0.003 inch? Yes
Sample 3 Ultimate Tensile 2461.5 lbf?in/in?
Sample 3 Elongation (350% Min) Pass
Median of the Ultimate Tensile Values 2424.2 psi

Test 4 of 7

DIME Test ID: 2016-07-26-5-4
Test Method: ASTM D2628-91-re11-low: Standard Specification for Preformed Polychloroprene Elastomeric Joint Seals for Concrete Pavements (Low Temp Recovery)
Verified Date: 08/18/2016
Date Tested: 08/04/2016
Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Organization Address: 5900 Folsom Blvd,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: paul.lukkarila@dot.ca.gov
Organization Phone: (916) 227-7253
General Comments for this Test:
Test Result Compliance:
Additional Comments When Verified:
Temperature 72 f
Humidity 50 %
Low Temp Recovery (22 hrs at -20F) Size Before (Height of Contact Face ) 2.75 in
Low Temp Recovery (22 hrs at -20F) Size After (Recovered Contact Face ) 2.622 in
Percent Recovery (Low Temp) 95 %

Test 5 of 7

DIME Test ID: 2016-07-26-5-5
Test Method: ASTM D2628-91-re11-high: Standard Specification for Preformed Polychloroprene Elastomeric Joint Seals for Concrete Pavements (High Temp Recovery)
Verified Date: 08/18/2016
Date Tested: 08/08/2016
Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Organization Address: 5900 Folsom Blvd,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: paul.lukkarila@dot.ca.gov
Organization Phone: (916) 227-7253
General Comments for this Test:
Test Result Compliance:
Additional Comments When Verified:
Temperature 72 f
Humidity 50 %
High Temp Recovery (70 hrs at 212F) Size Before (Height of Contact Face ) 2.75 in
High Temp Recovery (70 hrs at 212F) Size After (Expanded Contact Face ) 2.658 in
Percent Recovery (High Temp) 97 %

Test 6 of 7

DIME Test ID: 2016-07-26-5-6
Test Method: ASTM D471-15a: Standard Test Method for Rubber Property - Effect of Liquids
Verified Date: 08/18/2016
Date Tested: 08/12/2016
Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Organization Address: 5900 Folsom Blvd,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: paul.lukkarila@dot.ca.gov
Organization Phone: (916) 227-7253
General Comments for this Test:
Test Result Compliance: complies
Additional Comments When Verified:
Oil Swell Percentage 34.1 %

Test 7 of 7

DIME Test ID: 2016-07-26-5-7
Test Method: SMTL BILST-06: (Neoprene Verification) Bilstein Test
Verified Date: 08/18/2016
Date Tested: 08/12/2016
Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Organization Address: 5900 Folsom Blvd,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: paul.lukkarila@dot.ca.gov
Organization Phone: (916) 227-7253
General Comments for this Test:
Test Result Compliance: complies
Additional Comments When Verified:
Result Pass