Sample Information

DIME Sample ID: 2016-07-19-15
TL Number from the TL Form: Unknown
Sample Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Sample Organization Contact: (916) 227-7253
Type of Sample: Quality Assurance
Type of Material: SMTL TM2 - Type B Elastomeric Joint Seal
Sample Taken Date: 07/19/2016
Date that the sample was received by the laboratory/organization performing the testing: 07/21/2016
The quantity of what the sample constitutes: 550ft
A brief description of the sample: Joint Seal
From where was the sample collected: Manufacturer
Laboratory sample identification: Unknown
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: Watson Bowman

Material Information

Mfg. Lot Number(s): 1016294
Manufacturer(s): Watson Bowman
Temperature: 72
Humidity: 50
Comments: Unknown
Joint Seal Size: 3.75in

Test Results

Test 1 of 7

DIME Test ID: 2016-07-19-15-1
Test Method: CTM 673-July 2012: Method of Determining Movement Rating of Type B1 and B2 Preformed Elastomeric Joint Seals
Verified Date: 08/17/2016
Date Tested: 07/29/2016
Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Organization Address: 5900 Folsom Blvd,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: paul.lukkarila@dot.ca.gov
Organization Phone: (916) 227-7253
General Comments for this Test:
Test Result Compliance:
Additional Comments When Verified:
UTM 11KIP
Temperature 72 ?F
Humidity 50 %
Load at W1 60.6236 lbs
Width at 4 x Load at W1 1.57323 in
Nominal Width 3.75 in
Measured Maximum Uncompressed Width 3.9625 in
Measured Minimum Uncompressed Width 3.902 in
Minimum Uncompressed Width as Specified by the Manufacturer (MUWASBM) 3.879 in
Height of Contact Face 3.689 in
Spec Minimum Uncompressed Width 3.879 in
Area (5 Times of the Height of Contact Face) 18.445 sqin
Half of the Spec Minimum Uncompressed Width 1.9395 in
85 Percent of the Spec Minimum Uncompressed Width 3.29715 in
3 Times of the Area 55.335 sqin
4 Times of the Load at W1 242.495 in
W1 (US Units) 3.297 in
W1 (Metric Units) 83.748 millimeters
W2 (US Units) 1.573 in
W2 (Metric Units) 39.96 millimeters
Satisfactory of MR of (US Units) 1.724 in
Satisfactory of MR of (Metric Units) 43.788 millimeters
Optional W1 Measurement 1 3.3167 in
Optional W1 Measurement 2 55.7039 sqin

Test 2 of 7

DIME Test ID: 2016-07-19-15-2
Test Method: ASTM D2240-05re10: Standard Test Method for Rubber Property - Durometer Hardness
Verified Date: 08/17/2016
Date Tested: 08/02/2016
Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Organization Address: 5900 Folsom Blvd,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: paul.lukkarila@dot.ca.gov
Organization Phone: (916) 227-7253
General Comments for this Test:
Test Result Compliance:
Additional Comments When Verified:
Temperature 72 f
Humidity 50 %
Reading #1 54
Reading #2 54
Reading #3 55
Reading #4 54
Reading #5 55
Mean 54.4

Test 3 of 7

DIME Test ID: 2016-07-19-15-3
Test Method: ASTM D412-06a-re13: Standard Test Methods for Vulcanized Rubber and Thermoplastic Elastomers—Tension
Verified Date: 08/17/2016
Date Tested: 08/02/2016
Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Organization Address: 5900 Folsom Blvd,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: paul.lukkarila@dot.ca.gov
Organization Phone: (916) 227-7253
General Comments for this Test:
Test Result Compliance:
Additional Comments When Verified:
UTM 2KIP
Humidity 50 %
Temperature 72 F
Sample 1 Median Thickness 0.075 in
Sample 1 Thickness all Within 0.003 inch? Yes
Sample 1 Ultimate Tensile 2446.8 lbf?in/in?
Sample 1 Elongation (350% Min) Pass
Sample 2 Median Thickness 0.081 in
Sample 2 Thickness all Within 0.003 inch? Yes
Sample 2 Ultimate Tensile 2266 lbf?in/in?
Sample 2 Elongation (350% Min) Pass
Sample 3 Median Thickness 0.087 in
Sample 3 Thickness all Within 0.003 inch? Yes
Sample 3 Ultimate Tensile 2156 lbf?in/in?
Sample 3 Elongation (350% Min) Pass
Median of the Ultimate Tensile Values 2266 psi

Test 4 of 7

DIME Test ID: 2016-07-19-15-4
Test Method: ASTM D2628-91-re11-low: Standard Specification for Preformed Polychloroprene Elastomeric Joint Seals for Concrete Pavements (Low Temp Recovery)
Verified Date: 08/17/2016
Date Tested: 08/02/2016
Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Organization Address: 5900 Folsom Blvd,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: paul.lukkarila@dot.ca.gov
Organization Phone: (916) 227-7253
General Comments for this Test:
Test Result Compliance:
Additional Comments When Verified:
Temperature 72 f
Humidity 50 %
Low Temp Recovery (22 hrs at -20F) Size Before (Height of Contact Face ) 3.75 in
Low Temp Recovery (22 hrs at -20F) Size After (Recovered Contact Face ) 3.602 in
Percent Recovery (Low Temp) 96 %

Test 5 of 7

DIME Test ID: 2016-07-19-15-5
Test Method: ASTM D2628-91-re11-high: Standard Specification for Preformed Polychloroprene Elastomeric Joint Seals for Concrete Pavements (High Temp Recovery)
Verified Date: 08/17/2016
Date Tested: 08/02/2016
Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Organization Address: 5900 Folsom Blvd,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: paul.lukkarila@dot.ca.gov
Organization Phone: (916) 227-7253
General Comments for this Test:
Test Result Compliance:
Additional Comments When Verified:
Temperature 72 f
Humidity 50 %
High Temp Recovery (70 hrs at 212F) Size Before (Height of Contact Face ) 3.75 in
High Temp Recovery (70 hrs at 212F) Size After (Expanded Contact Face ) 3.626 in
Percent Recovery (High Temp) 97 %

Test 6 of 7

DIME Test ID: 2016-07-19-15-6
Test Method: ASTM D471-15a: Standard Test Method for Rubber Property - Effect of Liquids
Verified Date: 08/17/2016
Date Tested: 08/12/2016
Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Organization Address: 5900 Folsom Blvd,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: paul.lukkarila@dot.ca.gov
Organization Phone: (916) 227-7253
General Comments for this Test:
Test Result Compliance: complies
Additional Comments When Verified:
Oil Swell Percentage 34 %

Test 7 of 7

DIME Test ID: 2016-07-19-15-7
Test Method: SMTL BILST-06: (Neoprene Verification) Bilstein Test
Verified Date: 08/17/2016
Date Tested: 08/12/2016
Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Organization Address: 5900 Folsom Blvd,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: paul.lukkarila@dot.ca.gov
Organization Phone: (916) 227-7253
General Comments for this Test:
Test Result Compliance: complies
Additional Comments When Verified:
Result Pass