Note: Fields with no data or with a value of "Unknown" will not be displayed on the print out.
Project ID: 993208 DEA: 034F38U4 EFIS: 0321000092
QA Service Level: 1
DIST-CO-RTE-PM: 03-YUB-70-16.2/25.8
Work Description: WIDEN SHOULDERS AND IMPROVE CLEAR RECOVERY ZONE.
Location Description: YUBA COUNTY NEAR MARYSVILLE FROM 0.2 MILE NORTH OF LAURELLEN ROAD TO SOUTH HONCUT CREEK BRIDGE
Contractor Name: DeSilva Gates
Contractor Address: 11555 Dublin Boulevard, Dublin, CA 94568
Resident Engineer: Manoharan Selvendran Structure Rep.: Unknown
DIME Sample ID: 2023-10-18-47
TL Number from the TL Form: 849496
Sample Submitted By Organization: CT D03 - Olivehurst Northern Regional Laboratory
Sample Organization Contact: (530) 741-4238
Type of Sample: Quality Assurance
Type of Material: Hot Mix Asphalt
Sample Taken Date: 10/18/2023
Date that the sample was received by the laboratory/organization performing the testing: 10/24/2023
The quantity of what the sample constitutes: 750
A brief description of the sample: 1/2" HMA-O
From where was the sample collected: Source
Laboratory sample identification: 23-265
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: Desilva Gates-Marysville
DIME Test ID: 2023-10-18-47-1
Test Method: AASHTO T308-10: Standard Method of Test for Determining the Asphalt Binder Content of Hot Mix Asphalt (HMA) by the Ignition Method (Method A) (Asphalt Binder Content)
Verified Date: 11/14/2023
Date Tested: 10/24/2023
Submitted By Organization: CT D03 - Olivehurst Northern Regional Laboratory
Organization Address: 5330 Arboga Road,
Organization City: Olivehurst
Organization State: CA
Organization Zipcode: 95961
Organization Email: jeff.herbert@dot.ca.gov
Organization Phone: (530) 741-4238
General Comments for this Test:
Test Result Compliance: complies
Additional Comments When Verified:
What temperature unit is used?
|
Celsius
|
Test procedure used?
|
Method A
|
Mass of the specimen basket assembly
|
4036.3 g
|
Mass of the specimen and specimen basket assembly prior to ignition
|
6056.1 g
|
Mass of HMA Sample prior to ignition
|
2019.8 g
|
Corrected Asphalt Binder Content
|
5.21 %
|
Mass Loss
|
113.2 g
|
Mass of aggregate remaining after ignition
|
1906.6 g
|
Correction Factor (Percent by mass of HMA Specimen)
|
0.39 %
|
Moisture Content
|
0.00 %
|
Temperature Compensation Factor
|
0.00 %
|
Test Temperature
|
538 C
|