Sample Information

DIME Sample ID: 2016-01-07-1
TL Number from the TL Form: Unknown
Sample Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Sample Organization Contact: (916) 227-7253
Type of Sample: Quality Assurance
Type of Material: SMTL TM1 - Elastomeric Bearing Pad
Sample Taken Date: 01/07/2016
Date that the sample was received by the laboratory/organization performing the testing: 01/11/2016
The quantity of what the sample constitutes: 55ft
A brief description of the sample: 2 Plain Bearing Pads
From where was the sample collected: Source
Laboratory sample identification: Unknown
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: Warco

Material Information

Mfg. Lot Number(s): 12-9-15-1
Material/Compound/Elastomer ID: NC8168
Samples Representing: 55ft
Description (size): .25in x 36in
Comments: Unknown
Description (Number of Shims): 0
Type of Bearing Pad: Plain
Description (Thickness of Shims): NA
Manufacturer(s): Warco
Batch Number: NA

Test Results

Test 1 of 3

DIME Test ID: 2016-01-07-1-1
Test Method: ASTM D2240-05re10: Standard Test Method for Rubber Property - Durometer Hardness
Verified Date: 01/28/2016
Date Tested: 01/13/2016
Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Organization Address: 5900 Folsom Blvd,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: paul.lukkarila@dot.ca.gov
Organization Phone: (916) 227-7253
General Comments for this Test:
Test Result Compliance: complies
Additional Comments When Verified:
Temperature 72 f
Humidity 50 %
Reading #1 56
Reading #2 55
Reading #3 55
Reading #4 57
Reading #5 57
Mean 56

Test 2 of 3

DIME Test ID: 2016-01-07-1-2
Test Method: ASTM D412-06a-re13: Standard Test Methods for Vulcanized Rubber and Thermoplastic Elastomers—Tension
Verified Date: 01/28/2016
Date Tested: 01/14/2016
Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Organization Address: 5900 Folsom Blvd,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: paul.lukkarila@dot.ca.gov
Organization Phone: (916) 227-7253
General Comments for this Test:
Test Result Compliance: complies
Additional Comments When Verified:
UTM 2KIP
Humidity 50 %
Temperature 72 F
Sample 1 Median Thickness 0.068 in
Sample 1 Thickness all Within 0.003 inch? Yes
Sample 1 Ultimate Tensile 2705.9 lbf/in^2
Sample 1 Elongation (350% Min) Pass
Sample 2 Median Thickness 0.069 in
Sample 2 Thickness all Within 0.003 inch? Yes
Sample 2 Ultimate Tensile 2832.4 lbf/in^2
Sample 2 Elongation (350% Min) Pass
Sample 3 Median Thickness 0.067 in
Sample 3 Thickness all Within 0.003 inch? Yes
Sample 3 Ultimate Tensile 2797.6 lbf/in^2
Sample 3 Elongation (350% Min) Pass
Median of the Ultimate Tensile Values 2797.6 lbf/in^2

Test 3 of 3

DIME Test ID: 2016-01-07-1-3
Test Method: ASTM D624-00-re12: Standard Test Method for Tear Strength of Conventional Vulcanized Rubber and Thermoplastic Elastomers
Verified Date: 01/28/2016
Date Tested: 01/14/2016
Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Organization Address: 5900 Folsom Blvd,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: paul.lukkarila@dot.ca.gov
Organization Phone: (916) 227-7253
General Comments for this Test:
Test Result Compliance:
Additional Comments When Verified:
Number of specimens tested 3
UTM 2KIP
Humidity 50 %
Temperature 72 F
Sample 1 Median Thickness 0.078 in
Sample 1 Tear Strength 230.8 lbf / in
Sample 2 Median Thickness 0.071 in
Sample 2 Tear Strength 309.9 lbf / in
Sample 3 Median Thickness 0.075 in
Sample 3 Tear Strength 266.7 lbf / in
Median of the Tear Strength Values 266.7 lb/in