Sample Record for 2023-06-13-17
Note: Fields with no data or with a value of "Unknown" will not be displayed on the print out.
Project Information
Project ID: 994506 DEA: 061F7204 EFIS: 0623000158
QA Service Level: 1
DIST-CO-RTE-PM: 06-TUL-198-14.65, 14.65/14.65
Work Description:
Location Description:
Contractor Name: MCM Construction, Inc.
Contractor Address: 6413 32nd Street, North Highlands, Ca 95660
Resident Engineer: Haidar Haddadin Structure Rep.: Ramandeep Guraya
Sample Information
DIME Sample ID: 2023-06-13-17
TL Number from the TL Form:
Sample Submitted By Organization: CT HQ - QASI Bay Area Field Office
Sample Organization Contact: (916) 284-6784
Type of Sample: Quality Assurance
Type of Material: SMTL TM6 - Steel Check Sample Plate
Sample Taken Date: 06/13/2023
Date that the sample was received by the laboratory/organization performing the testing: 06/15/2023
The quantity of what the sample constitutes: 1 plate
A brief description of the sample: Check Sample Plates
From where was the sample collected: Fabricator
Laboratory sample identification:
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: XKT Engineering
Material Information
Heat Number(s): 811S011800
Material Specification: A709
Grade: 50
Thickness: .375
Shape: Plate
Metal Foundry Manufacturer (Mill): Cleveland Cliffs
Plate Dimension: 120 x 360
Test Results
Test 1 of 3
DIME Test ID: 2023-06-13-17-1
Test Method: ASTM A370-20: Standard Test Methods and Definitions for Mechanical Testing of Steel Products (Tensile - Round Sample)
Verified Date: 07/07/2023
Date Tested: 06/19/2023
Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: joshua.moore@dot.ca.gov
Organization Phone: (530) 329-6527
General Comments for this Test:
Test Result Compliance:
Additional Comments When Verified:
Number of Samples
|
2
|
Sample | Heat Number | Diameter (in) | Area (sqin) | Stress at Offset (psi) | Tensile Strength (psi) | Elongation in 4 x d (%) | Tested By | | 811S01800 | 0.253 | 0.05027 | 72347 | 77785 | 33.8 | aauvinen | | 811S01800 | 0.255 | 0.05107 | 70946 | 78061 | 33.5 | aauvinen |
| |
UTM
|
67kip
|
Temperature
|
72 F
|
Test 2 of 3
DIME Test ID: 2023-06-13-17-2
Test Method: ASTM E415-21: Standard Test Method for Analysis of Carbon and Low-Alloy Steel by Spark Atomic Emission Spectrometry
Submitted By Organization: CT HQ - Sacramento Chemistry Laboratory
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: sanchita.dey@dot.ca.gov
Organization Phone: (916) 227-7912
This test has been superseded on 07/07/2023. The corrected test ID is: 2023-06-13-17-3
Reason: corrected
Test 3 of 3
DIME Test ID: 2023-06-13-17-3
Test Method: ASTM E415-21: Standard Test Method for Analysis of Carbon and Low-Alloy Steel by Spark Atomic Emission Spectrometry
Verified Date: 07/07/2023
Date Tested: 06/28/2023
Submitted By Organization: CT HQ - Sacramento Chemistry Laboratory
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: sanchita.dey@dot.ca.gov
Organization Phone: (916) 227-7912
General Comments for this Test: Correcting the previous test results that were published. The values were mixed up with another sample.
The test was superseded from test ID: 2023-06-13-17-2
Test Result Compliance: complies
Additional Comments When Verified:
Content, carbon
|
0.0831 %
|
Content, Si
|
0.227 %
|
Content, Mn
|
1.32 %
|
Content, P
|
0.0114 %
|
Content, S
|
0.0073 %
|
Content, Cr
|
0.0264 %
|
Content, Mo
|
0.006 %
|
Content, Al
|
0.031 %
|
Content, Co
|
0.0047 %
|
Content, Copper
|
0.0244 %
|
Content, Nb
|
0.0363 %
|
Content, Ti
|
0.0169 %
|
Content, V
|
0.0557 %
|
Content, Lead
|
0.0164 %
|
Content, Boron
|
0.00095 %
|
Content, Fe
|
98.1 %
|
Content, Ni
|
0.0091 %
|