Sample Record for 2023-04-17-24

Note: Fields with no data or with a value of "Unknown" will not be displayed on the print out.

Project Information

Project ID: 212737 DEA: 060S8304 EFIS: 0615000046 QA Service Level: 1
DIST-CO-RTE-PM: 06-FRE-5-44.4-45.4
Work Description: TUMEY GULCH ABUTMENT REHAB BR# 42-0246L/R.
Contractor Name: Bruce Shumacher
Contractor Address: 2716 S Granite Ct, Fresno, CA 93706
Resident Engineer: Cary Cruz Structure Rep.: Ben Holton

Sample Information

DIME Sample ID: 2023-04-17-24
TL Number from the TL Form:
Sample Submitted By Organization: CT D06 - Millbrook Field Laboratory
Sample Organization Contact: (559) 417-5341
Type of Sample: Quality Assurance
Type of Material: Hot Mix Asphalt
Sample Taken Date: 04/17/2023
Date that the sample was received by the laboratory/organization performing the testing: 04/18/2023
The quantity of what the sample constitutes: 750 Tons
A brief description of the sample: 3/4 HMA-A R25
From where was the sample collected: Manufacturer
Laboratory sample identification:
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: Granite Coalinga HMA Plant

Material Information

HMA Type: Type A HMA
HMA Grading: 3/4 inch
Lot number: 2
Sublot number: 1
HMA Mix Number:

Test Results

Test 1 of 1

DIME Test ID: 2023-04-17-24-1
Test Method: AASHTO T308-10: Standard Method of Test for Determining the Asphalt Binder Content of Hot Mix Asphalt (HMA) by the Ignition Method (Method A) (Asphalt Binder Content)
Verified Date: 04/21/2023
Date Tested: 04/18/2023
Submitted By Organization: CT D06 - Millbrook Field Laboratory
Organization Address: 3240 North Millbrook Avenue,
Organization City: Fresno
Organization State: CA
Organization Zipcode: 93726
Organization Email:
Organization Phone: (559) 417-5341
General Comments for this Test:
Test Result Compliance: complies
Additional Comments When Verified:
What temperature unit is used? Celsius
Test procedure used? Method A
Mass of the specimen basket assembly 2872.7 g
Mass of the specimen and specimen basket assembly prior to ignition 4916.3 g
Mass of HMA Sample prior to ignition 2043.6 g
Corrected Asphalt Binder Content 4.85 %
Mass Loss 121.6 g
Mass of aggregate remaining after ignition 1922.0 g
Correction Factor (Percent by mass of HMA Specimen) 0.99 %
Moisture Content 0.00 %
Temperature Compensation Factor 0.11 %
Test Temperature 482 C