Print Report | Back to Sample Detail

Sample Record for 2023-03-08-49

Note: Fields with no data or with a value of "Unknown" will not be displayed on the print out.

Project Information

Project ID: 212737 DEA: 060S8304 EFIS: 0615000046 QA Service Level: 1
DIST-CO-RTE-PM: 06-FRE-5-44.4-45.4
Work Description: TUMEY GULCH ABUTMENT REHAB BR# 42-0246L/R.
Location Description: IN FRESNO COUNTY AT TUMEY GULCH.
Contractor Name: Bruce Shumacher
Contractor Address: 2716 S Granite Ct, Fresno, CA 93706
Resident Engineer: Cary Cruz Structure Rep.: Ben Holton

Sample Information

DIME Sample ID: 2023-03-08-49
TL Number from the TL Form:
Sample Submitted By Organization: CT D06 - Millbrook Field Laboratory
Sample Organization Contact: (559) 417-5341
Type of Sample: Department Acceptance
Type of Material: Concrete
Sample Taken Date: 03/08/2023
Date that the sample was received by the laboratory/organization performing the testing: 03/09/2023
The quantity of what the sample constitutes: 300 cy
A brief description of the sample: structural concrete
From where was the sample collected: Fabricator
Laboratory sample identification:
Structure unique identifier:
Structure name: Bridge Deck
The fabricator/manufacturer/facility name: Unknown

Material Information

The concrete mix design number: g67534st
The truck number from where the sample was collected:
The batch plant ticket number from where the sample was collected: 419701
Concrete batch plant:
The fabricator/manufacturer designation for the sample:
A detailed description of where the material sample was collected: Discharge from concrete truck into wheelbarrow.
Where the material sample would have been placed if not sampled:
From Lot No.:
Bag Lot No.:

Test Results

Test 1 of 3

DIME Test ID: 2023-03-08-49-1
Test Method: ASTM C39-18: Standard Test Method for Compressive Strength of Cylindrical Concrete Specimens
Verified Date: 03/17/2023
Date Tested: 03/15/2023
Submitted By Organization: CT D06 - Millbrook Field Laboratory
Organization Address: 3240 North Millbrook Avenue,
Organization City: Fresno
Organization State: CA
Organization Zipcode: 93726
Organization Email: tomas.silva@dot.ca.gov
Organization Phone: (559) 417-5341
General Comments for this Test:
Test Result Compliance: complies
Additional Comments When Verified:
Unit system used? US Units
Number of specimens 3
Test performed With no density determined
Average diameter of cylinder 1 4.01 in
Average diameter of cylinder 2 4.01 in
Capped in accordance with? ASTM C1231 - Unbonded Elastomeric Pad Cap
Average diameter of cylinder 3 4.01 in
Cross sectional area of cylinder 1 12.63 in^2
Cross sectional area of cylinder 2 12.63 in^2
Cross sectional area of cylinder 3 12.63 in^2
Compressive strength (to nearest 10 psi) 4010 psi
Maximum load on cylinder 1 52800 lb
Maximum load on cylinder 2 49510 lb
Maximum load on cylinder 3 49550 lb
Compressive strength of cylinder 1 4180.5 psi
Type of fracture pattern of cylinder 1 3
Compressive strength of cylinder 2 3920.0 psi
Compressive strength of cylinder 3 3923.2 psi
Type of fracture pattern of cylinder 2 3
Type of fracture pattern of cylinder 3 3
Comment on any defect in either specimen or caps (Max 250 Characters) no data
Correction factor for cylinder 1 1
Correction factor for cylinder 2 1
Correction factor for cylinder 3 1
Age of specimen 6 days
Age of specimen in hours 0 hours

Test 2 of 3

DIME Test ID: 2023-03-08-49-2
Test Method: ASTM C39-18: Standard Test Method for Compressive Strength of Cylindrical Concrete Specimens
Verified Date: 03/24/2023
Date Tested: 03/22/2023
Submitted By Organization: CT D06 - Millbrook Field Laboratory
Organization Address: 3240 North Millbrook Avenue,
Organization City: Fresno
Organization State: CA
Organization Zipcode: 93726
Organization Email: tomas.silva@dot.ca.gov
Organization Phone: (559) 417-5341
General Comments for this Test:
Test Result Compliance: complies
Additional Comments When Verified:
Unit system used? US Units
Number of specimens 3
Test performed With no density determined
Average diameter of cylinder 1 4.00 in
Average diameter of cylinder 2 4.01 in
Capped in accordance with? ASTM C1231 - Unbonded Elastomeric Pad Cap
Average diameter of cylinder 3 4.00 in
Cross sectional area of cylinder 1 12.57 in^2
Cross sectional area of cylinder 2 12.63 in^2
Cross sectional area of cylinder 3 12.57 in^2
Compressive strength (to nearest 10 psi) 5350 psi
Maximum load on cylinder 1 67070 lb
Maximum load on cylinder 2 68000 lb
Maximum load on cylinder 3 67160 lb
Compressive strength of cylinder 1 5335.7 psi
Type of fracture pattern of cylinder 1 3
Compressive strength of cylinder 2 5384.0 psi
Compressive strength of cylinder 3 5342.9 psi
Type of fracture pattern of cylinder 2 3
Type of fracture pattern of cylinder 3 3
Comment on any defect in either specimen or caps (Max 250 Characters) no data
Correction factor for cylinder 1 1
Correction factor for cylinder 2 1
Correction factor for cylinder 3 1
Age of specimen 14 days
Age of specimen in hours 0 hours

Test 3 of 3

DIME Test ID: 2023-03-08-49-3
Test Method: ASTM C39-18: Standard Test Method for Compressive Strength of Cylindrical Concrete Specimens
Verified Date: 04/10/2023
Date Tested: 04/05/2023
Submitted By Organization: CT D06 - Millbrook Field Laboratory
Organization Address: 3240 North Millbrook Avenue,
Organization City: Fresno
Organization State: CA
Organization Zipcode: 93726
Organization Email: tomas.silva@dot.ca.gov
Organization Phone: (559) 417-5341
General Comments for this Test:
Test Result Compliance: complies
Additional Comments When Verified:
Unit system used? US Units
Number of specimens 3
Test performed With no density determined
Average diameter of cylinder 1 4.00 in
Average diameter of cylinder 2 4.00 in
Capped in accordance with? ASTM C1231 - Unbonded Elastomeric Pad Cap
Average diameter of cylinder 3 4.00 in
Cross sectional area of cylinder 1 12.57 in^2
Cross sectional area of cylinder 2 12.57 in^2
Cross sectional area of cylinder 3 12.57 in^2
Compressive strength (to nearest 10 psi) 6640 psi
Maximum load on cylinder 1 82520 lb
Maximum load on cylinder 2 84880 lb
Maximum load on cylinder 3 82860 lb
Compressive strength of cylinder 1 6564.8 psi
Type of fracture pattern of cylinder 1 3
Compressive strength of cylinder 2 6752.6 psi
Compressive strength of cylinder 3 6591.9 psi
Type of fracture pattern of cylinder 2 3
Type of fracture pattern of cylinder 3 3
Comment on any defect in either specimen or caps (Max 250 Characters) no data
Correction factor for cylinder 1 1
Correction factor for cylinder 2 1
Correction factor for cylinder 3 1
Age of specimen 28 days
Age of specimen in hours 0 hours