Note: Fields with no data or with a value of "Unknown" will not be displayed on the print out.

Project Information

Project ID: 8801 DEA: AML-CEM EFIS: AML-CEM QA Service Level:
DIST-CO-RTE-PM: 59---
Work Description: Special project for Cementitious Materials for use in Concrete Authorized Material List (AML)
Location Description:
Contractor Name: Unknown
Contractor Address: Unknown
Resident Engineer: Unknown Structure Rep.: Unknown

Sample Information

DIME Sample ID: 2022-06-06-2
TL Number from the TL Form:
Sample Submitted By Organization: CT HQ - Sacramento Cement Testing Laboratory
Sample Organization Contact: (916) 227-7071
Type of Sample: Annual Source Testing
Type of Material: Cementitious
Sample Taken Date: 06/06/2022
Date that the sample was received by the laboratory/organization performing the testing: 06/06/2022
The quantity of what the sample constitutes: 1 Bucket
A brief description of the sample: Silica Fume Control
From where was the sample collected: Source
Laboratory sample identification: CM229220
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: Control

Material Information

Brand: Nevada Cement
Mill: Fernley
Type of Cementitious Material: Type II Cement

Test Results

Test 1 of 1

DIME Test ID: 2022-06-06-2-2
Test Method: ASTM C109-16a: Standard Test Method for Compressive Strength of Hydraulic Cement Mortars (Using 2-in. or [50-mm] Cube Specimens)
Verified Date: 06/21/2022
Date Tested: 06/13/2022
Submitted By Organization: CT HQ - Sacramento Cement Testing Laboratory
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: ben.lenz@dot.ca.gov
Organization Phone: (916) 227-7071
General Comments for this Test:
Test Result Compliance:
Additional Comments When Verified:
Will control cubes be used per ASTM C311? no
Age of specimen 7 days
The amount of flow 115 %
The amount of water used 48.5 %
Compressive strength of 1st specimen 4777 psi
Compressive strength of 2nd specimen 4644 psi
Compressive strength of 3rd specimen 4871 psi
Average Compressive strength (to nearest 10 psi) 4760 psi