Note: Fields with no data or with a value of "Unknown" will not be displayed on the print out.
Project ID: 44444 DEA: ASCP EFIS: ASCP
QA Service Level:
DIST-CO-RTE-PM: 59---
Work Description: Special project for submitting Sample information for Asphalt Supplier Certification Program.
Location Description:
Contractor Name: Unknown
Contractor Address: Unknown
Resident Engineer: Unknown Structure Rep.: Unknown
DIME Sample ID: 2021-10-04-50
TL Number from the TL Form:
Sample Submitted By Organization: Valero-NuStar PAT - Pittsburg
Sample Organization Contact: (707) 745-7089
Type of Sample: Quality Control
Type of Material: Asphalt Binder
Sample Taken Date: 10/04/2021
Date that the sample was received by the laboratory/organization performing the testing: 10/04/2021
The quantity of what the sample constitutes: 1 of 2
A brief description of the sample: Tank 0150
From where was the sample collected: Manufacturer
Laboratory sample identification: 6416-100421
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: Pittsburg, CA
Performance Grade: PG 64-16
Modified: No
Lot number:
Sublot number:
Tank number:
Time of sample:
HMA Supplier:
Certified Asphalt Supplier: Valero-NuStar PAT - Pittsburg CA
Multigrade: Yes
Multigrade Type: PG 64-16 / PG 64-10
Asphalt Binder Mix Number:
DIME Test ID: 2021-10-04-50-1
Test Method: AASHTO T48-18: Standard Method of Test for Flash Point of Asphalt Binder by Cleveland Open Cup
Verified Date: 10/22/2021
Date Tested: 10/07/2021
Submitted By Organization: Valero-NuStar PAT - Pittsburg
Organization Address: 1100 Willow Pass Road,
Organization City: Pittsburg
Organization State: CA
Organization Zipcode: 94565
Organization Email: patrick.sendegeya@valero.com
Organization Phone: (707) 745-7214
General Comments for this Test: Submitted from ASCP bulk upload. Had to edit test date and add Observed Flash Point & Barometric Pressure
Test Result Compliance:
Additional Comments When Verified:
Units of measurement for Observed Flash Point (C or F) and Ambient barometric pressure (kP or mmHg)
|
Celsius and mmHg
|
Observed Flash Point
|
310 C
|
Ambient Barometric Pressure
|
752.8 mmHg
|
Cleveland Open-Cup Flash Point in Celsius
|
310 C
|
DIME Test ID: 2021-10-04-50-2
Test Method: AASHTO T316-17: Standard Method of Test for Viscosity Determination of Asphalt Binder Using Rotational Viscometer
Verified Date: 12/06/2021
Date Tested: 10/07/2021
Submitted By Organization: Valero-NuStar PAT - Pittsburg
Organization Address: 1100 Willow Pass Road,
Organization City: Pittsburg
Organization State: CA
Organization Zipcode: 94565
Organization Email: patrick.sendegeya@valero.com
Organization Phone: (707) 745-7214
General Comments for this Test: Submitted from ASCP bulk upload. Had to correct test date and add in all *tests except Average Visc
Test Result Compliance:
Additional Comments When Verified:
Is viscosity reading in cP/Pa-s?
|
Pa-s
|
Time of test
|
09:08 HH:MM
|
Test Temperature
|
135 C
|
Speed
|
20 rpm
|
Spindle size
|
S21 in
|
Torque
|
16 %
|
Viscosity reading #1 (A)
|
0.399 Pa-s
|
Viscosity reading #2 (B)
|
0.403 Pa-s
|
Viscosity reading #3 (C)
|
0.399 Pa-s
|
Average viscosity
|
0.4 Pa-s
|
DIME Test ID: 2021-10-04-50-3
Test Method: AASHTO T315-16: Standard Method of Test for Determining the Rheological Properties of Asphalt Binder Using a Dynamic Shear Rheometer (DSR) (Dynamic Shear)
Verified Date: 10/22/2021
Date Tested: 10/07/2021
Submitted By Organization: Valero-NuStar PAT - Pittsburg
Organization Address: 1100 Willow Pass Road,
Organization City: Pittsburg
Organization State: CA
Organization Zipcode: 94565
Organization Email: patrick.sendegeya@valero.com
Organization Phone: (707) 745-7214
General Comments for this Test: Submitted from ASCP bulk upload. Had to correct Test date and add in Phase Angle
Test Result Compliance:
Additional Comments When Verified:
Phase
|
Original binder
|
Test Plate Diameter
|
25 mm
|
Phase Angle (δ) (for the 10 cycles)
|
85.5 degree
|
Dynamic Shear, G*/sin(δ)
|
1.62 kPa
|
DIME Test ID: 2021-10-04-50-4
Test Method: AASHTO T44-18: Standard Method of Test for Solubility of Bituminous Materials
Verified Date: 10/22/2021
Date Tested: 10/07/2021
Submitted By Organization: Valero-NuStar PAT - Pittsburg
Organization Address: 1100 Willow Pass Road,
Organization City: Pittsburg
Organization State: CA
Organization Zipcode: 94565
Organization Email: patrick.sendegeya@valero.com
Organization Phone: (707) 745-7214
General Comments for this Test: Submitted from ASCP bulk upload.
Test Result Compliance:
Additional Comments When Verified:
Was test performed on residue from distillation or evaporation?
|
NA
|
Soluble, percent
|
99.9 %
|
Insoluble, percent
|
0.1 %
|
DIME Test ID: 2021-10-04-50-5
Test Method: AASHTO T315-16: Standard Method of Test for Determining the Rheological Properties of Asphalt Binder Using a Dynamic Shear Rheometer (DSR) (Dynamic Shear)
Verified Date: 10/22/2021
Date Tested: 10/07/2021
Submitted By Organization: Valero-NuStar PAT - Pittsburg
Organization Address: 1100 Willow Pass Road,
Organization City: Pittsburg
Organization State: CA
Organization Zipcode: 94565
Organization Email: patrick.sendegeya@valero.com
Organization Phone: (707) 745-7214
General Comments for this Test: Submitted from ASCP bulk upload.
Test Result Compliance:
Additional Comments When Verified:
Phase
|
RTFO residue
|
Test Plate Diameter
|
25 mm
|
Phase Angle (δ) (for the 10 cycles)
|
80.8 degree
|
Dynamic Shear, G*/sin(δ)
|
4.40 kPa
|
DIME Test ID: 2021-10-04-50-6
Test Method: AASHTO T51-13: Standard Method of Test for Ductility of Asphalt Materials (Asphalt Binder)
Verified Date: 10/22/2021
Date Tested: 10/07/2021
Submitted By Organization: Valero-NuStar PAT - Pittsburg
Organization Address: 1100 Willow Pass Road,
Organization City: Pittsburg
Organization State: CA
Organization Zipcode: 94565
Organization Email: patrick.sendegeya@valero.com
Organization Phone: (707) 745-7214
General Comments for this Test: Submitted from ASCP bulk upload. It is the average of 3 specimens, but when loaded from bulk upload, no opportunity to select # of beams
Test Result Compliance:
Additional Comments When Verified:
Is a normal test obtainable?
|
Yes
|
Number of replicates tested
|
One
|
Ductility of test #1 (D1)
|
150 cm
|
Ductility of sample
|
150 cm
|
DIME Test ID: 2021-10-04-50-7
Test Method: AASHTO T240-17: Standard Method of Test for Effect of Heat and Air on a Moving Film of Asphalt Binder (Rolling Thin-Film Oven Test)
Verified Date: 10/22/2021
Date Tested: 10/07/2021
Submitted By Organization: Valero-NuStar PAT - Pittsburg
Organization Address: 1100 Willow Pass Road,
Organization City: Pittsburg
Organization State: CA
Organization Zipcode: 94565
Organization Email: patrick.sendegeya@valero.com
Organization Phone: (707) 745-7214
General Comments for this Test: Submitted from ASCP bulk upload.
Test Result Compliance:
Additional Comments When Verified:
Is mass change based on one or two containers?
|
One
|
Average mass change
|
-0.420 percent
|
DIME Test ID: 2021-10-04-50-8
Test Method: AASHTO T315-16: Standard Method of Test for Determining the Rheological Properties of Asphalt Binder Using a Dynamic Shear Rheometer (DSR) (Dynamic Shear)
Verified Date: 10/22/2021
Date Tested: 10/08/2021
Submitted By Organization: Valero-NuStar PAT - Pittsburg
Organization Address: 1100 Willow Pass Road,
Organization City: Pittsburg
Organization State: CA
Organization Zipcode: 94565
Organization Email: patrick.sendegeya@valero.com
Organization Phone: (707) 745-7214
General Comments for this Test: Submitted from ASCP bulk upload.
Test Result Compliance:
Additional Comments When Verified:
Phase
|
PAV residue
|
Test Plate Diameter
|
8 mm
|
Phase Angle (δ) (for the 10 cycles)
|
50.1 degree
|
(G*) x sin(δ)=
|
1901 kPa
|
DIME Test ID: 2021-10-04-50-9
Test Method: AASHTO T313-19: Standard Method of Test for Determining the Flexural Creep Stiffness of Asphalt Binder Using the Bending Beam Rheometer (BBR)
Verified Date: 10/22/2021
Date Tested: 10/08/2021
Submitted By Organization: Valero-NuStar PAT - Pittsburg
Organization Address: 1100 Willow Pass Road,
Organization City: Pittsburg
Organization State: CA
Organization Zipcode: 94565
Organization Email: patrick.sendegeya@valero.com
Organization Phone: (707) 745-7214
General Comments for this Test: Submitted from ASCP bulk upload.
Test Result Compliance:
Additional Comments When Verified:
Time test started
|
no data HH:MM:SS
|
Flags issued by software during test
|
no data
|
Correlation coefficient (R²)
|
0
|
Regression coefficient a
|
no data
|
Regression coefficient b
|
no data
|
Regression coefficient c
|
no data
|
Load at time 0.0
|
0.0 mN
|
Deflection at time 0.0 s
|
0.000 µm
|
Load at time 0.5 s
|
0.0 mN
|
Deflection at time 0.5 s
|
0.000 µm
|
Load at 60.0 s
|
0.0 mN
|
Beam deflection 60.0 s
|
0.000 µm
|
Measured Stiffness Modulus 60.0 s
|
68.449 mPa
|
Estimated Stiffness Modulus 60.0 s
|
69.000 mPa
|
Difference between stiffness moduli 60.0 s
|
no data
|
Estimated m-value 60.0 s
|
0.410
|
DIME Test ID: 2021-10-04-50-10
Test Method: AASHTO T313-19: Standard Method of Test for Determining the Flexural Creep Stiffness of Asphalt Binder Using the Bending Beam Rheometer (BBR)
Verified Date: 10/22/2021
Date Tested: 10/08/2021
Submitted By Organization: Valero-NuStar PAT - Pittsburg
Organization Address: 1100 Willow Pass Road,
Organization City: Pittsburg
Organization State: CA
Organization Zipcode: 94565
Organization Email: patrick.sendegeya@valero.com
Organization Phone: (707) 745-7214
General Comments for this Test: Submitted from ASCP bulk upload.
Test Result Compliance:
Additional Comments When Verified:
Time test started
|
no data HH:MM:SS
|
Flags issued by software during test
|
no data
|
Correlation coefficient (R²)
|
0
|
Regression coefficient a
|
no data
|
Regression coefficient b
|
no data
|
Regression coefficient c
|
no data
|
Load at time 0.0
|
0.0 mN
|
Deflection at time 0.0 s
|
0.000 µm
|
Load at time 0.5 s
|
0.0 mN
|
Deflection at time 0.5 s
|
0.000 µm
|
Load at 60.0 s
|
0.0 mN
|
Beam deflection 60.0 s
|
0.000 µm
|
Measured Stiffness Modulus 60.0 s
|
68.450 mPa
|
Estimated Stiffness Modulus 60.0 s
|
69.000 mPa
|
Difference between stiffness moduli 60.0 s
|
no data
|
Estimated m-value 60.0 s
|
0.411
|