Print Report | Back to Sample Detail

Sample Record for 2021-08-26-33

Note: Fields with no data or with a value of "Unknown" will not be displayed on the print out.

Project Information

Project ID: 215554 DEA: 061A9004 EFIS: 0621000018 QA Service Level: 1
DIST-CO-RTE-PM: 06-KER-5-4.4/R15.8
Work Description: COLD PLANE & PLACE HMA & INDIVIDUAL SLAB REPLACEMENT.
Location Description: KERN COUNTY AT GRAPEVINE FROM 0.4 MILE NORTH OF LEBEC ROAD OVERCROSSING TO ROUTES 5/99 SEPARATION
Contractor Name: RV Concrete
Contractor Address: 605 E. Commercial St., Anaheim, CA 92801
Resident Engineer: Isidro Perez Structure Rep.: Unknown

Sample Information

DIME Sample ID: 2021-08-26-33
TL Number from the TL Form: 772220
Sample Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Sample Organization Contact: (916) 227-7302
Type of Sample: Department Acceptance
Type of Material: Asphalt Binder
Sample Taken Date: 08/26/2021
Date that the sample was received by the laboratory/organization performing the testing: 08/31/2021
The quantity of what the sample constitutes: 1 can
A brief description of the sample: Asphalt Binder PG 70-10
From where was the sample collected: Job Site
Laboratory sample identification:
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: San Joaquin Refinery, Bakersfield, CA

Material Information

Performance Grade: PG 70-10
Modified: No
Lot number: 1
Sublot number: 4
Tank number: 32001
Time of sample:
HMA Supplier: Vulcan Materials
Certified Asphalt Supplier: San Joaquin Refinery - Bakersfield CA
Multigrade: No
Multigrade Type:
Asphalt Binder Mix Number:
Test results on following page(s): 6

Test Results

Test 1 of 6

DIME Test ID: 2021-08-26-33-1
Test Method: AASHTO T240-17: Standard Method of Test for Effect of Heat and Air on a Moving Film of Asphalt Binder (Rolling Thin-Film Oven Test)
Verified Date: 09/21/2021
Date Tested: 09/08/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Boulevard, Room 225,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: per 2018 standard specifications mass change
Test Result Compliance: complies
Additional Comments When Verified:
Is mass change based on one or two containers? Two
Any material loss from containers during heating process/testing? No
Mass of empty container #1 169.221 grams
Mass of empty container #2 179.168 grams
Mass of container #1 before test (m1i) 205.960 grams
Mass of container #2 before test (m2i) 215.165 grams
Mass of container #1 after test (m1f) 205.959 grams
Mass of container #2 after test (m2f) 215.164 grams
Average mass change -0.003 percent

Test 2 of 6

DIME Test ID: 2021-08-26-33-2
Test Method: AASHTO T315-20: Standard Method of Test for Determining the Rheological Properties of Asphalt Binder Using a Dynamic Shear Rheometer (DSR) (Dynamic Shear)
Verified Date: 09/21/2021
Date Tested: 09/07/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Boulevard, Room 225,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: Per 2018 Standard Specifications Original
Test Result Compliance: complies
Additional Comments When Verified:
Phase Original binder
Test Plate Diameter 25 mm
Test Gap 1 mm
Test Frequency 10.0 rad/s
Strain Amplitude 12.00 %
Stress Amplitude 0.220 kPa
Phase Angle (δ) (for the 10 cycles) 89.0 degree
Complex Modulus (G*) (for the 10 measurements) 1.832 kPa
Test Temperature (Specimen 1) 70.0 C
Dynamic Shear, G*/sin(δ) 1.83 kPa

Test 3 of 6

DIME Test ID: 2021-08-26-33-3
Test Method: AASHTO T315-20: Standard Method of Test for Determining the Rheological Properties of Asphalt Binder Using a Dynamic Shear Rheometer (DSR) (Dynamic Shear)
Verified Date: 09/21/2021
Date Tested: 09/07/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Boulevard, Room 225,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: Per 2018 Standard Specifications RTFO
Test Result Compliance: complies
Additional Comments When Verified:
Phase RTFO residue
Test Plate Diameter 25 mm
Test Gap 1 mm
Test Frequency 10.0 rad/s
Strain Amplitude 10.00 %
Stress Amplitude 0.226 kPa
Phase Angle (δ) (for the 10 cycles) 88.9 degree
Complex Modulus (G*) (for the 10 measurements) 2.257 kPa
Test Temperature (Specimen 1) 70.0 C
Dynamic Shear, G*/sin(δ) 2.26 kPa

Test 4 of 6

DIME Test ID: 2021-08-26-33-4
Test Method: AASHTO T315-20: Standard Method of Test for Determining the Rheological Properties of Asphalt Binder Using a Dynamic Shear Rheometer (DSR) (Dynamic Shear)
Verified Date: 09/21/2021
Date Tested: 09/14/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Boulevard, Room 225,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: Per 2018 Standard Specifications PAV
Test Result Compliance: not applicable
Additional Comments When Verified:
Phase PAV residue
Test Plate Diameter 8 mm
Test Gap 2 mm
Test Frequency 10.0 rad/s
Strain Amplitude 1.00 %
Stress Amplitude 70.518 kPa
Phase Angle (δ) (for the 10 cycles) 58.1 degree
Complex Modulus (G*) (for the 10 measurements) 7049.198 kPa
Test Temperature (Specimen 1) 34.0 C
(G*) x sin(δ)= 5985 kPa

Test 5 of 6

DIME Test ID: 2021-08-26-33-5
Test Method: AASHTO T313-19: Standard Method of Test for Determining the Flexural Creep Stiffness of Asphalt Binder Using the Bending Beam Rheometer (BBR)
Verified Date: 09/21/2021
Date Tested: 09/15/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Boulevard, Room 225,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: Per 2018 standard specifications
Test Result Compliance: complies
Additional Comments When Verified:
Minimum test bath temperature at 240 s 0.0 C
Maximum test bath temperature at 240 s 0.0 C
Time of test load application no data HH:MM:SS
File name of test data no data
Time beam in bath no data
Time test started no data HH:MM:SS
Flags issued by software during test no data
Correlation coefficient (R²) 0
Regression coefficient a no data
Regression coefficient b no data
Regression coefficient c no data
Load at time 0.0 0.0 mN
Deflection at time 0.0 s 0.000 µm
Load at time 0.5 s 0.0 mN
Deflection at time 0.5 s 0.000 µm
Load at 60.0 s 996.0 mN
Beam deflection 60.0 s 0.302 µm
Measured Stiffness Modulus 60.0 s 266.000 mPa
Estimated Stiffness Modulus 60.0 s 266.000 mPa
Difference between stiffness moduli 60.0 s no data
Estimated m-value 60.0 s 0.370

Test 6 of 6

DIME Test ID: 2021-08-26-33-8
Test Method: AASHTO T315-20: Standard Method of Test for Determining the Rheological Properties of Asphalt Binder Using a Dynamic Shear Rheometer (DSR) (Dynamic Shear)
Verified Date: 09/21/2021
Date Tested: 09/14/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Boulevard, Room 225,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: Per 2018 Standard Specifications PAV+3
Test Result Compliance: complies
Additional Comments When Verified:
Phase PAV residue
Test Plate Diameter 8 mm
Test Gap 2 mm
Test Frequency 10.0 rad/s
Strain Amplitude 1.00 %
Stress Amplitude 41.683 kPa
Phase Angle (δ) (for the 10 cycles) 61.9 degree
Complex Modulus (G*) (for the 10 measurements) 4167.127 kPa
Test Temperature (Specimen 1) 37.0 C
(G*) x sin(δ)= 3676 kPa