Sample Record for 2021-08-12-29

Note: Fields with no data or with a value of "Unknown" will not be displayed on the print out.

Project Information

Project ID: 215321 DEA: 060U1004 EFIS: 0615000211 QA Service Level: 1
DIST-CO-RTE-PM: 06-KER-43,119-0.1/9.3,18.2/19.7
Work Description: COLD IN PLACE RECYCLING AND RESURFACING EXISTING ROADWAY WITH RHMA.
Location Description: KERN COUNTY NEAR BAKERSFIELD ON ROUTE 43 FROM ROUTE 119 TO 0.1 MILE NORTH OF ROUTE 58-MCKITTRICK HIGHWAY AND ON ROUTE 119 FROM ROUTE 43 TO ROUTE 119/5 SEPARATION
Contractor Name: GRANITE CONSTRUCTION COMPANY
Contractor Address: Unknown
Resident Engineer: Amarjit Dhaliwal Structure Rep.: Unknown

Sample Information

DIME Sample ID: 2021-08-12-29
TL Number from the TL Form: 771143
Sample Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Sample Organization Contact: (916) 227-7302
Type of Sample: Acceptance
Type of Material: Asphalt Binder
Sample Taken Date: 08/12/2021
Date that the sample was received by the laboratory/organization performing the testing: 08/20/2021
The quantity of what the sample constitutes: 1 of 1 can
A brief description of the sample: PG64-16
From where was the sample collected: Source
Laboratory sample identification:
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: San Joaquin Refining Co Inc

Material Information

Performance Grade: PG 64-16
Modified:
Lot number:
Sublot number:
Tank number:
Time of sample:
HMA Supplier:
Asphalt Binder Supplier: San Joaquin Refinery - Bakersfield CA
Multigrade: No
Multigrade Type:

Test Results

Test 1 of 6

DIME Test ID: 2021-08-12-29-1
Test Method: AASHTO T240-17: Standard Method of Test for Effect of Heat and Air on a Moving Film of Asphalt Binder (Rolling Thin-Film Oven Test)
Verified Date: 08/30/2021
Date Tested: 08/24/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Blvd,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: per 2018 standard specifications
Test Result Compliance: complies
Additional Comments When Verified:
Is mass change based on one or two containers? Two
Any material loss from containers during heating process/testing? No
Mass of empty container #1 169.644 grams
Mass of empty container #2 168.123 grams
Mass of container #1 before test (m1i) 204.847 grams
Mass of container #2 before test (m2i) 203.326 grams
Mass of container #1 after test (m1f) 204.850 grams
Mass of container #2 after test (m2f) 203.327 grams
Average mass change 0.006 percent

Test 2 of 6

DIME Test ID: 2021-08-12-29-2
Test Method: AASHTO T315-20: Standard Method of Test for Determining the Rheological Properties of Asphalt Binder Using a Dynamic Shear Rheometer (DSR) (Dynamic Shear)
Verified Date: 08/30/2021
Date Tested: 08/24/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Blvd,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: per 2018 standard specifications OG
Test Result Compliance: complies
Additional Comments When Verified:
Phase Original binder
Test Plate Diameter 25 mm
Test Gap 1 mm
Test Frequency 10.0 rad/s
Strain Amplitude 12.00 %
Stress Amplitude 0.165 kPa
Phase Angle (δ) (for the 10 cycles) 89.3 degree
Complex Modulus (G*) (for the 10 measurements) 1.376 kPa
Test Temperature 64.0 C
Dynamic Shear, G*/sin(δ) 1.38 kPa

Test 3 of 6

DIME Test ID: 2021-08-12-29-3
Test Method: AASHTO T315-20: Standard Method of Test for Determining the Rheological Properties of Asphalt Binder Using a Dynamic Shear Rheometer (DSR) (Dynamic Shear)
Verified Date: 08/30/2021
Date Tested: 08/26/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Blvd,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: per 2018 standard specifications
Test Result Compliance: complies
Additional Comments When Verified:
Phase RTFO residue
Test Plate Diameter 25 mm
Test Gap 1 mm
Test Frequency 10.0 rad/s
Strain Amplitude 10.00 %
Stress Amplitude 0.261 kPa
Phase Angle (δ) (for the 10 cycles) 88.4 degree
Complex Modulus (G*) (for the 10 measurements) 2.606 kPa
Test Temperature 64.0 C
Dynamic Shear, G*/sin(δ) 2.61 kPa

Test 4 of 6

DIME Test ID: 2021-08-12-29-4
Test Method: AASHTO T315-20: Standard Method of Test for Determining the Rheological Properties of Asphalt Binder Using a Dynamic Shear Rheometer (DSR) (Dynamic Shear)
Verified Date: 08/30/2021
Date Tested: 08/25/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Blvd,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: per 2018 standard specifications PAV
Test Result Compliance: not applicable
Additional Comments When Verified:
Phase PAV residue
Test Plate Diameter 8 mm
Test Gap 2 mm
Test Frequency 10.0 rad/s
Strain Amplitude 1.00 %
Stress Amplitude 69.059 kPa
Phase Angle (δ) (for the 10 cycles) 58.4 degree
Complex Modulus (G*) (for the 10 measurements) 6905.298 kPa
Test Temperature 28.0 C
(G*) x sin(δ)= 5881 kPa

Test 5 of 6

DIME Test ID: 2021-08-12-29-5
Test Method: AASHTO T313-19: Standard Method of Test for Determining the Flexural Creep Stiffness of Asphalt Binder Using the Bending Beam Rheometer (BBR)
Verified Date: 08/30/2021
Date Tested: 08/25/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Blvd,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: per 2018 standard specifications
Test Result Compliance: complies
Additional Comments When Verified: Pass
Minimum test bath temperature at 240 s -6.0 C
Maximum test bath temperature at 240 s -5.9 C
Time of test load application no data HH:MM:SS
File name of test data no data
Time beam in bath no data
Time test started no data HH:MM:SS
Flags issued by software during test no data
Correlation coefficient (R²) 0
Regression coefficient a no data
Regression coefficient b no data
Regression coefficient c no data
Load at time 0.0 0.0 mN
Deflection at time 0.0 s 0.000 µm
Load at time 0.5 s 0.0 mN
Deflection at time 0.5 s 0.000 µm
Load at 60.0 s 998.0 mN
Beam deflection 60.0 s 0.407 µm
Measured Stiffness Modulus 60.0 s 198.000 mPa
Estimated Stiffness Modulus 60.0 s 198.000 mPa
Difference between stiffness moduli 60.0 s no data
Estimated m-value 60.0 s 0.404

Test 6 of 6

DIME Test ID: 2021-08-12-29-6
Test Method: AASHTO T315-20: Standard Method of Test for Determining the Rheological Properties of Asphalt Binder Using a Dynamic Shear Rheometer (DSR) (Dynamic Shear)
Verified Date: 08/30/2021
Date Tested: 08/25/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Blvd,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: per 2018 standard specifications +3C
Test Result Compliance: complies
Additional Comments When Verified:
Phase PAV residue
Test Plate Diameter 8 mm
Test Gap 2 mm
Test Frequency 10.0 rad/s
Strain Amplitude 1.00 %
Stress Amplitude 40.841 kPa
Phase Angle (δ) (for the 10 cycles) 62.4 degree
Complex Modulus (G*) (for the 10 measurements) 4083.880 kPa
Test Temperature 31.0 C
(G*) x sin(δ)= 3619 kPa