Project Information

Project ID: 8801 DEA: AML-CEM EFIS: AML-CEM QA Service Level:
DIST-CO-RTE-PM: 59---
Work Description: Special project for Cementitious Materials for use in Concrete Authorized Material List (AML)
Location Description:
Contractor Name: Unknown
Contractor Address: Unknown
Resident Engineer: Unknown Structure Rep.: Unknown

Sample Information

DIME Sample ID: 2021-07-01-31
TL Number from the TL Form: CM218012
Sample Submitted By Organization: CT HQ - Sacramento Cement Testing Laboratory
Sample Organization Contact: (916) 227-7071
Type of Sample: Proficiency
Type of Material: Cementitious
Sample Taken Date: 07/01/2021
Date that the sample was received by the laboratory/organization performing the testing: 07/01/2021
The quantity of what the sample constitutes: 1 box
A brief description of the sample: CCRL 1260 No.12
From where was the sample collected: Source
Laboratory sample identification:
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: CCRL

Material Information

Brand: CCRL
Mill: CCRL
Type of Cementitious Material: Type II Cement

Test Results

Test 1 of 1

DIME Test ID: 2021-07-01-31-1
Test Method: ASTM C1260-14: Standard Test Method for Potential Alkali Reactivity of Aggregates (Mortar-Bar Method)
Verified Date: 07/11/2022
Date Tested: 08/19/2021
Submitted By Organization: CT HQ - Sacramento Cement Testing Laboratory
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: ben.lenz@dot.ca.gov
Organization Phone: (916) 227-7071
General Comments for this Test: Initial, Zero, 7 day, 14 day and 28 day readings input.
Test Result Compliance:
Additional Comments When Verified:
Type and source of aggregate CCRL
Type and source of Portland cement CCRL
Alkali content of cement as percent potassium oxide na
Alkali content of cement as percent sodium oxide na
Alkali content of cement as percent calculated sodium oxide na
Comments about aggregate preparation no data
Comments about specimen features no data
Amount of mixing water 207 ml
Percent change in length specimen 1 (zero reading) 0.0770
Percent change in length specimen 2 (zero reading) 0.0770
Percent change in length specimen 3 (zero reading) 0.0760
Percent change in length specimen 1 (first reading) 0.0930 %
Percent change in length specimen 2 (first reading) 0.1060 %
Percent change in length specimen 3 (first reading) 0.1010 %
Percent change in length specimen 1 (second reading) 0.2520 %
Percent change in length specimen 2 (second reading) 0.2650 %
Percent change in length specimen 3 (second reading) 0.2460 %
Percent change in length specimen 1 (third reading) 0.4430 %
Percent change in length specimen 2 (third reading) 0.4710 %
Percent change in length specimen 3 (third reading) 0.4400 %
Average percent change in length (zero reading) 0.0767
Average percent change in length (first reading) 0.1000 %
Average percent change in length (second reading) 0.2543 %
Average percent change in length (third reading) 0.4513 %