Print Report | Back to Sample Detail

Sample Record for 2021-06-28-23

Note: Fields with no data or with a value of "Unknown" will not be displayed on the print out.

Project Information

Project ID: 55556 DEA: OCR EFIS: OCR QA Service Level:
DIST-CO-RTE-PM: 59---
Work Description: Special project for submitting Sample information for Oregon Corp. Research.
Location Description:
Contractor Name: Unknown
Contractor Address: Unknown
Resident Engineer: Unknown Structure Rep.: Unknown

Sample Information

DIME Sample ID: 2021-06-28-23
TL Number from the TL Form:
Sample Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Sample Organization Contact: (916) 227-7302
Type of Sample: Proficiency
Type of Material: Asphalt Binder
Sample Taken Date: 06/28/2021
Date that the sample was received by the laboratory/organization performing the testing: 07/01/2021
The quantity of what the sample constitutes: 1 of 1 can
A brief description of the sample: PG70-28ER
From where was the sample collected: Source
Laboratory sample identification:
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: Albina - Vancouver

Material Information

Performance Grade: PG 70-22
Modified:
Lot number:
Sublot number:
Tank number:
Time of sample:
HMA Supplier:
Certified Asphalt Supplier: Oregon Corp - Salem OR
Multigrade: No
Multigrade Type:
Asphalt Binder Mix Number:
Test results on following page(s): 9

Test Results

Test 1 of 9

DIME Test ID: 2021-06-28-23-1
Test Method: AASHTO T240-17: Standard Method of Test for Effect of Heat and Air on a Moving Film of Asphalt Binder (Rolling Thin-Film Oven Test)
Verified Date: 07/19/2021
Date Tested: 07/07/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Boulevard, Room 225,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test:
Test Result Compliance:
Additional Comments When Verified:
Is mass change based on one or two containers? Two
Any material loss from containers during heating process/testing? No
Mass of empty container #1 174.570 grams
Mass of empty container #2 155.521 grams
Mass of container #1 before test (m1i) 210.158 grams
Mass of container #2 before test (m2i) 191.563 grams
Mass of container #1 after test (m1f) 210.035 grams
Mass of container #2 after test (m2f) 191.443 grams
Average mass change -0.339 percent

Test 2 of 9

DIME Test ID: 2021-06-28-23-2
Test Method: AASHTO T315-20: Standard Method of Test for Determining the Rheological Properties of Asphalt Binder Using a Dynamic Shear Rheometer (DSR) (Dynamic Shear)
Verified Date: 07/19/2021
Date Tested: 07/07/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Boulevard, Room 225,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: DSR @ 70c
Test Result Compliance:
Additional Comments When Verified:
Phase Original binder
Test Plate Diameter 25 mm
Test Gap 1 mm
Test Frequency 10.0 rad/s
Strain Amplitude 12.00 %
Stress Amplitude 0.147 kPa
Phase Angle (δ) (for the 10 cycles) 73.8 degree
Complex Modulus (G*) (for the 10 measurements) 1.225 kPa
Test Temperature (Specimen 1) 70.0 C
Dynamic Shear, G*/sin(δ) 1.28 kPa

Test 3 of 9

DIME Test ID: 2021-06-28-23-3
Test Method: AASHTO T315-20: Standard Method of Test for Determining the Rheological Properties of Asphalt Binder Using a Dynamic Shear Rheometer (DSR) (Dynamic Shear)
Verified Date: 07/19/2021
Date Tested: 07/07/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Boulevard, Room 225,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: RTFO-DSR @ 70c
Test Result Compliance:
Additional Comments When Verified:
Phase RTFO residue
Test Plate Diameter 25 mm
Test Gap 1 mm
Test Frequency 10.0 rad/s
Strain Amplitude 10.00 %
Stress Amplitude 0.266 kPa
Phase Angle (δ) (for the 10 cycles) 64.8 degree
Complex Modulus (G*) (for the 10 measurements) 2.661 kPa
Test Temperature (Specimen 1) 70.0 C
Dynamic Shear, G*/sin(δ) 2.94 kPa

Test 4 of 9

DIME Test ID: 2021-06-28-23-4
Test Method: AASHTO T301-13: Standard Method of Test for Elastic Recovery Test of Asphalt Materials by Means of a Ductilometer
Verified Date: 07/19/2021
Date Tested: 07/07/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Boulevard, Room 225,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test:
Test Result Compliance:
Additional Comments When Verified:
Final Reading from the testing machine (X) 4 cm
% Elongation Recovery 80 %

Test 5 of 9

DIME Test ID: 2021-06-28-23-5
Test Method: AASHTO T350-19: Multiple Stress Creep Recovery (MSCR) Test of Asphalt Binder Using a Dynamic Shear Rheometer (DSR) (Multiple Stress Creep Recovery)
Verified Date: 07/19/2021
Date Tested: 07/07/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Boulevard, Room 225,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: MSCR
Test Result Compliance:
Additional Comments When Verified:
PG test temperature 64.0 C
Average percent recovery at 0.1 kPa 62.1500 %
Average percent recovery at 3.2 kPa 34.2400 %
Nonrecoverable creep compliance 0.4833
Nonrecoverable creep compliance 0.9372
Percent difference between nonrecoverable creep compliance at 0.1 kPa and 3.2 kPa 93.9300 %

Test 6 of 9

DIME Test ID: 2021-06-28-23-6
Test Method: AASHTO T315-20: Standard Method of Test for Determining the Rheological Properties of Asphalt Binder Using a Dynamic Shear Rheometer (DSR) (Dynamic Shear)
Verified Date: 07/22/2021
Date Tested: 07/22/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Boulevard, Room 225,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: PAV-DSR @ 25c
Test Result Compliance:
Additional Comments When Verified:
Phase PAV residue
Test Plate Diameter 8 mm
Test Gap 2 mm
Test Frequency 10.0 rad/s
Strain Amplitude 1.00 %
Stress Amplitude 26.294 kPa
Phase Angle (δ) (for the 10 cycles) 42.8 degree
Complex Modulus (G*) (for the 10 measurements) 2628.619 kPa
Test Temperature (Specimen 1) 25.0 C
(G*) x sin(δ)= 1786 kPa

Test 7 of 9

DIME Test ID: 2021-06-28-23-8
Test Method: AASHTO T315-20: Standard Method of Test for Determining the Rheological Properties of Asphalt Binder Using a Dynamic Shear Rheometer (DSR) (Dynamic Shear)
Verified Date: 07/19/2021
Date Tested: 07/07/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Boulevard, Room 225,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: Original
Test Result Compliance:
Additional Comments When Verified:
Phase Original binder
Test Plate Diameter 25 mm
Test Gap 1 mm
Test Frequency 10.0 rad/s
Strain Amplitude 12.00 %
Stress Amplitude 0.149 kPa
Phase Angle (δ) (for the 10 cycles) 73.7 degree
Complex Modulus (G*) (for the 10 measurements) 1.239 kPa
Test Temperature (Specimen 1) 70.0 C
Dynamic Shear, G*/sin(δ) 1.29 kPa

Test 8 of 9

DIME Test ID: 2021-06-28-23-9
Test Method: AASHTO T315-20: Standard Method of Test for Determining the Rheological Properties of Asphalt Binder Using a Dynamic Shear Rheometer (DSR) (Dynamic Shear)
Verified Date: 07/19/2021
Date Tested: 07/07/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Boulevard, Room 225,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: Original
Test Result Compliance:
Additional Comments When Verified:
Phase Original binder
Test Plate Diameter 25 mm
Test Gap 1 mm
Test Frequency 10.0 rad/s
Strain Amplitude 12.00 %
Stress Amplitude 0.146 kPa
Phase Angle (δ) (for the 10 cycles) 73.9 degree
Complex Modulus (G*) (for the 10 measurements) 1.220 kPa
Test Temperature (Specimen 1) 70.0 C
Dynamic Shear, G*/sin(δ) 1.27 kPa

Test 9 of 9

DIME Test ID: 2021-06-28-23-10
Test Method: AASHTO T313-19: Standard Method of Test for Determining the Flexural Creep Stiffness of Asphalt Binder Using the Bending Beam Rheometer (BBR)
Verified Date: 07/22/2021
Date Tested: 07/22/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Boulevard, Room 225,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: BBR
Test Result Compliance:
Additional Comments When Verified:
Minimum test bath temperature at 240 s -18.0 C
Maximum test bath temperature at 240 s -18.0 C
Time of test load application no data HH:MM:SS
File name of test data no data
Time beam in bath no data
Time test started no data HH:MM:SS
Flags issued by software during test no data
Correlation coefficient (R²) 0
Regression coefficient a no data
Regression coefficient b no data
Regression coefficient c no data
Load at time 0.0 0.0 mN
Deflection at time 0.0 s 0.000 µm
Load at time 0.5 s 0.0 mN
Deflection at time 0.5 s 0.000 µm
Load at 60.0 s 947.0 mN
Beam deflection 60.0 s 0.623 µm
Measured Stiffness Modulus 60.0 s 123.000 mPa
Estimated Stiffness Modulus 60.0 s 123.000 mPa
Difference between stiffness moduli 60.0 s no data
Estimated m-value 60.0 s 0.331