Print Report | Back to Sample Detail

Sample Record for 2021-03-08-18

Note: Fields with no data or with a value of "Unknown" will not be displayed on the print out.

Project Information

Project ID: 44444 DEA: ASCP EFIS: ASCP QA Service Level:
DIST-CO-RTE-PM: 59---
Work Description: Special project for submitting Sample information for Asphalt Supplier Certification Program.
Location Description:
Contractor Name: Unknown
Contractor Address: Unknown
Resident Engineer: Unknown Structure Rep.: Unknown

Sample Information

DIME Sample ID: 2021-03-08-18
TL Number from the TL Form:
Sample Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Sample Organization Contact: (916) 227-7302
Type of Sample: Verification
Type of Material: Asphalt Binder
Sample Taken Date: 03/08/2021
Date that the sample was received by the laboratory/organization performing the testing: 04/19/2021
The quantity of what the sample constitutes: 1 out of 5
A brief description of the sample: Asphalt Binder
From where was the sample collected: Manufacturer
Laboratory sample identification:
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: Marathon Bakersfeild

Material Information

Performance Grade: PG 64-28 M
Modified: Yes
Lot number:
Sublot number:
Tank number:
Time of sample:
HMA Supplier:
Asphalt Binder Supplier: Marathon Petroleum Co. LP - Bakersfield CA
Multigrade: No
Multigrade Type:

Test Results

Test 1 of 7

DIME Test ID: 2021-03-08-18-1
Test Method: AASHTO T240-17: Standard Method of Test for Effect of Heat and Air on a Moving Film of Asphalt Binder (Rolling Thin-Film Oven Test)
Verified Date: 04/28/2021
Date Tested: 04/20/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Blvd,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: as per 2018 standard specs
Test Result Compliance: complies
Additional Comments When Verified:
Is mass change based on one or two containers? Two
Any material loss from containers during heating process/testing? No
Mass of empty container #1 166.873 grams
Mass of empty container #2 168.001 grams
Mass of container #1 before test (m1i) 202.328 grams
Mass of container #2 before test (m2i) 203.379 grams
Mass of container #1 after test (m1f) 202.240 grams
Mass of container #2 after test (m2f) 203.290 grams
Average mass change -0.250 percent

Test 2 of 7

DIME Test ID: 2021-03-08-18-2
Test Method: AASHTO T301-13: Standard Method of Test for Elastic Recovery Test of Asphalt Materials by Means of a Ductilometer
Verified Date: 04/28/2021
Date Tested: 04/20/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Blvd,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: as per 2018 standard specs
Test Result Compliance: complies
Additional Comments When Verified:
Final Reading from the testing machine (X) 4 cm
% Elongation Recovery 80 %

Test 3 of 7

DIME Test ID: 2021-03-08-18-3
Test Method: AASHTO T315-16: Standard Method of Test for Determining the Rheological Properties of Asphalt Binder Using a Dynamic Shear Rheometer (DSR) (Dynamic Shear)
Verified Date: 04/28/2021
Date Tested: 04/21/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Blvd,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: Per 2018 Std Specs ORIG
Test Result Compliance: complies
Additional Comments When Verified:
Phase Original binder
Test Plate Diameter 25 mm
Test Gap 1 mm
Test Frequency 10.0 rad/s
Strain Amplitude 12.00 %
Stress Amplitude 0.243 kPa
Phase Angle (δ) (for the 10 cycles) 69.1 degree
Complex Modulus (G*) (for the 10 measurements) 2.028 kPa
Test Temperature 64.0 C
Dynamic Shear, G*/sin(δ) 2.17 kPa

Test 4 of 7

DIME Test ID: 2021-03-08-18-4
Test Method: AASHTO T315-16: Standard Method of Test for Determining the Rheological Properties of Asphalt Binder Using a Dynamic Shear Rheometer (DSR) (Dynamic Shear)
Verified Date: 04/28/2021
Date Tested: 04/21/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Blvd,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: Per 2018 Std Specs RTFO
Test Result Compliance: complies
Additional Comments When Verified:
Phase RTFO residue
Test Plate Diameter 25 mm
Test Gap 1 mm
Test Frequency 10.0 rad/s
Strain Amplitude 10.00 %
Stress Amplitude 0.398 kPa
Phase Angle (δ) (for the 10 cycles) 64.9 degree
Complex Modulus (G*) (for the 10 measurements) 3.983 kPa
Test Temperature 64.0 C
Dynamic Shear, G*/sin(δ) 4.40 kPa

Test 5 of 7

DIME Test ID: 2021-03-08-18-5
Test Method: AASHTO T315-16: Standard Method of Test for Determining the Rheological Properties of Asphalt Binder Using a Dynamic Shear Rheometer (DSR) (Dynamic Shear)
Verified Date: 04/28/2021
Date Tested: 04/21/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Blvd,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: Per 2018 Std Specs PAV
Test Result Compliance: complies
Additional Comments When Verified:
Phase PAV residue
Test Plate Diameter 8 mm
Test Gap 2 mm
Test Frequency 10.0 rad/s
Strain Amplitude 1.00 %
Stress Amplitude 12.541 kPa
Phase Angle (δ) (for the 10 cycles) 58.8 degree
Complex Modulus (G*) (for the 10 measurements) 1254.102 kPa
Test Temperature 22.0 C
(G*) x sin(δ)= 1073 kPa

Test 6 of 7

DIME Test ID: 2021-03-08-18-6
Test Method: AASHTO T313-19: Standard Method of Test for Determining the Flexural Creep Stiffness of Asphalt Binder Using the Bending Beam Rheometer (BBR)
Verified Date: 04/28/2021
Date Tested: 04/26/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Blvd,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: PER 2018 STANDARD SPECS
Test Result Compliance: complies
Additional Comments When Verified:
Minimum test bath temperature at 240 s -18.0 C
Maximum test bath temperature at 240 s -18.0 C
Time of test load application no data HH:MM:SS
File name of test data no data
Time beam in bath no data
Time test started no data HH:MM:SS
Flags issued by software during test no data
Correlation coefficient (R²) 0
Regression coefficient a no data
Regression coefficient b no data
Regression coefficient c no data
Load at time 0.0 0.0 mN
Deflection at time 0.0 s 0.000 µm
Load at time 0.5 s 0.0 mN
Deflection at time 0.5 s 0.000 µm
Load at 60.0 s 957.0 mN
Beam deflection 60.0 s 0.750 µm
Measured Stiffness Modulus 60.0 s 103.000 mPa
Estimated Stiffness Modulus 60.0 s 103.000 mPa
Difference between stiffness moduli 60.0 s 0.00 %
Estimated m-value 60.0 s 0.423

Test 7 of 7

DIME Test ID: 2021-03-08-18-7
Test Method: AASHTO T315-16: Standard Method of Test for Determining the Rheological Properties of Asphalt Binder Using a Dynamic Shear Rheometer (DSR) (Dynamic Shear)
Verified Date: 04/28/2021
Date Tested: 04/21/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Blvd,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: Per 2018 Std Specs RTFO+6, Delta @ 2.2kPa = 68.8
Test Result Compliance: complies
Additional Comments When Verified:
Phase RTFO residue
Test Plate Diameter 25 mm
Test Gap 1 mm
Test Frequency 10.0 rad/s
Strain Amplitude 10.00 %
Stress Amplitude 0.229 kPa
Phase Angle (δ) (for the 10 cycles) 65.2 degree
Complex Modulus (G*) (for the 10 measurements) 2.288 kPa
Test Temperature 70.0 C
Dynamic Shear, G*/sin(δ) 2.52 kPa

Tests Assigned to this Sample

DIME Test IDTest MethodAssigned DateTest DateAssigned ByAssigned LabTest CommentsAssigned To
No tests have been assigned to this sample.