Unit system used?
|
SI Units
|
Number of specimens
|
6
|
Test performed
|
With no density determined
|
Capped in accordance with?
|
ASTM C617/CTM521
|
Average diameter of cylinder 1
|
6 mm
|
Average diameter of cylinder 2
|
6 mm
|
Average diameter of cylinder 3
|
6.01 mm
|
Average diameter of cylinder 4
|
6.01 mm
|
Average diameter of cylinder 5
|
6.01 mm
|
Average diameter of cylinder 6
|
6.01 mm
|
Cross sectional area of cylinder 1
|
28.27 mm^2
|
Cross sectional area of cylinder 2
|
28.27 mm^2
|
Cross sectional area of cylinder 3
|
28.37 mm^2
|
Cross sectional area of cylinder 4
|
28.37 mm^2
|
Cross sectional area of cylinder 5
|
28.37 mm^2
|
Cross sectional area of cylinder 6
|
28.37 mm^2
|
Compressive strength (to nearest 0.1MPa)
|
1002.7 MPa
|
Maximum load on cylinder 1
|
28000 N
|
Maximum load on cylinder 2
|
28020 N
|
Maximum load on cylinder 3
|
28120 N
|
Maximum load on cylinder 4
|
28940 N
|
Maximum load on cylinder 5
|
28630 N
|
Maximum load on cylinder 6
|
28770 N
|
Type of fracture pattern of cylinder 1
|
2
|
Compressive strength of cylinder 1
|
990.4 MPa
|
Compressive strength of cylinder 2
|
991.2 MPa
|
Compressive strength of cylinder 3
|
991.2 MPa
|
Compressive strength of cylinder 4
|
1020.1 MPa
|
Type of fracture pattern of cylinder 2
|
2
|
Compressive strength of cylinder 5
|
1009.2 MPa
|
Compressive strength of cylinder 6
|
1014.1 MPa
|
Type of fracture pattern of cylinder 3
|
1
|
Type of fracture pattern of cylinder 4
|
2
|
Type of fracture pattern of cylinder 5
|
2
|
Type of fracture pattern of cylinder 6
|
1
|
Comment on any defect in either specimen or caps (Max 250 Characters)
|
no data
|
Correction factor for cylinder 1
|
1
|
Correction factor for cylinder 2
|
1
|
Correction factor for cylinder 3
|
1
|
Correction factor for cylinder 4
|
1
|
Correction factor for cylinder 5
|
1
|
Correction factor for cylinder 6
|
1
|
Age of specimen
|
7 days
|
Age of specimen in hours
|
no data
|