Sample Record for 2021-01-05-18

Note: Fields with no data or with a value of "Unknown" will not be displayed on the print out.

Project Information

Project ID: 214293 DEA: 060S4604 EFIS: 0615000038 QA Service Level: 1
DIST-CO-RTE-PM: 06-FRE-99-R0.9/R5.0
Work Description: REPLACE CONCRETE AND ASPHALT PAVEMENT.
Location Description: FRESNO COUNTY IN AND NEAR KINGSBURG AND SELMA FROM ROUTE 99/201 SEPARATION TO 0.3 MILE SOUTH OF SECOND STREET UNDERCROSSING
Contractor Name: GRANITE CONSTRUCTION CO
Contractor Address: 38155 Monroe Street, Indio, CA 92203
Resident Engineer: Mohammad Samimi Structure Rep.: Moua, Peter

Sample Information

DIME Sample ID: 2021-01-05-18
TL Number from the TL Form: C040293
Sample Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Sample Organization Contact: (916) 227-7302
Type of Sample: Acceptance
Type of Material: Asphalt Binder
Sample Taken Date: 01/05/2021
Date that the sample was received by the laboratory/organization performing the testing: 01/22/2021
The quantity of what the sample constitutes: 1 of 5
A brief description of the sample: Project Sample
From where was the sample collected: Source
Laboratory sample identification:
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: CMI FRESNO

Material Information

Performance Grade: PG 64-10
Modified: No
Lot number:
Sublot number:
Tank number:
Time of sample:
HMA Supplier:
Asphalt Binder Supplier:
Multigrade:

Test Results

Test 1 of 7

DIME Test ID: 2021-01-05-18-1
Test Method: AASHTO T240-17: Standard Method of Test for Effect of Heat and Air on a Moving Film of Asphalt Binder (Rolling Thin-Film Oven Test)
Verified Date: 01/29/2021
Date Tested: 01/25/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Blvd,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: per 2018 standard specifications
Additional Comments When Verified:
Is mass change based on one or two containers? Two
Any material loss from containers during heating process/testing? No
Mass of empty container #1 167.740 grams
Mass of empty container #2 166.198 grams
Mass of container #1 before test (m1i) 202.826 grams
Mass of container #2 before test (m2i) 201.629 grams
Mass of container #1 after test (m1f) 202.726 grams
Mass of container #2 after test (m2f) 201.520 grams
Average mass change -0.296 percent

Test 2 of 7

DIME Test ID: 2021-01-05-18-2
Test Method: AASHTO T51-13: Standard Method of Test for Ductility of Asphalt Materials (Asphalt Binder)
Verified Date: 01/29/2021
Date Tested: 01/25/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Blvd,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: per 2018 standard specifications
Additional Comments When Verified:
Is a normal test obtainable? Yes
Number of replicates tested Three
Ductility of test #1 (D1) 137 cm
Ductility of test #2 (D2) 140 cm
Ductility of test #3 (D3) 142 cm
Ductility of sample 140 cm

Test 3 of 7

DIME Test ID: 2021-01-05-18-3
Test Method: AASHTO T313-19: Standard Method of Test for Determining the Flexural Creep Stiffness of Asphalt Binder Using the Bending Beam Rheometer (BBR)
Verified Date: 01/29/2021
Date Tested: 01/28/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Blvd,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: as per 2018 standard specs
Additional Comments When Verified:
Minimum test bath temperature at 240 s 0.0 C
Maximum test bath temperature at 240 s 0.0 C
Time of test load application no data HH:MM:SS
File name of test data no data
Time beam in bath no data
Time test started no data HH:MM:SS
Flags issued by software during test no data
Correlation coefficient (R²) 0
Regression coefficient a no data
Regression coefficient b no data
Regression coefficient c no data
Load at time 0.0 0.0 mN
Deflection at time 0.0 s 0.000 µm
Load at time 0.5 s 0.0 mN
Deflection at time 0.5 s 0.000 µm
Load at 60.0 s 0.0 mN
Beam deflection 60.0 s 0.000 µm
Measured Stiffness Modulus 60.0 s 181.000 mPa
Estimated Stiffness Modulus 60.0 s 181.000 mPa
Difference between stiffness moduli 60.0 s no data
Estimated m-value 60.0 s 0.441

Test 4 of 7

DIME Test ID: 2021-01-05-18-6
Test Method: AASHTO T315-16: Standard Method of Test for Determining the Rheological Properties of Asphalt Binder Using a Dynamic Shear Rheometer (DSR) (Dynamic Shear)
Verified Date: 01/28/2021
Date Tested: 01/28/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Blvd,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: Per 2018 Std Specs PAV
Additional Comments When Verified:
Phase PAV residue
Test Plate Diameter 8 mm
Test Gap 2 mm
Test Frequency 10.0 rad/s
Strain Amplitude 1.00 %
Stress Amplitude 31.051 kPa
Phase Angle (δ) (for the 10 cycles) 68.3 degree
Complex Modulus (G*) (for the 10 measurements) 3104.908 kPa
Test Temperature 34.0 C
(G*) x sin(δ)= 2885 kPa

Test 5 of 7

DIME Test ID: 2021-01-05-18-7
Test Method: AASHTO T315-16: Standard Method of Test for Determining the Rheological Properties of Asphalt Binder Using a Dynamic Shear Rheometer (DSR) (Dynamic Shear)
Verified Date: 01/25/2021
Date Tested: 01/25/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Blvd,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: Per 2018 Standard Specifications ORIGINAL
Additional Comments When Verified:
Phase Original binder
Test Plate Diameter 25 mm
Test Gap 1 mm
Test Frequency 10.0 rad/s
Strain Amplitude 12.00 %
Stress Amplitude 0.168 kPa
Phase Angle (δ) (for the 10 cycles) 89.6 degree
Complex Modulus (G*) (for the 10 measurements) 1.397 kPa
Test Temperature 64.0 C
Dynamic Shear, G*/sin(δ) 1.40 kPa

Test 6 of 7

DIME Test ID: 2021-01-05-18-8
Test Method: AASHTO T315-16: Standard Method of Test for Determining the Rheological Properties of Asphalt Binder Using a Dynamic Shear Rheometer (DSR) (Dynamic Shear)
Verified Date: 01/25/2021
Date Tested: 01/25/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Blvd,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: Per 2018 Standard Specifications RTFO
Additional Comments When Verified:
Phase RTFO residue
Test Plate Diameter 25 mm
Test Gap 1 mm
Test Frequency 10.0 rad/s
Strain Amplitude 10.00 %
Stress Amplitude 0.283 kPa
Phase Angle (δ) (for the 10 cycles) 88.9 degree
Complex Modulus (G*) (for the 10 measurements) 2.832 kPa
Test Temperature 64.0 C
Dynamic Shear, G*/sin(δ) 2.83 kPa

Test 7 of 7

DIME Test ID: 2021-01-05-18-9
Test Method: AASHTO T315-16: Standard Method of Test for Determining the Rheological Properties of Asphalt Binder Using a Dynamic Shear Rheometer (DSR) (Dynamic Shear)
Verified Date: 01/29/2021
Date Tested: 01/28/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Blvd,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: Per 2018 Std Specs PAV
Additional Comments When Verified:
Phase PAV residue
Test Plate Diameter 8 mm
Test Gap 2 mm
Test Frequency 10.0 rad/s
Strain Amplitude 1.00 %
Stress Amplitude 55.844 kPa
Phase Angle (δ) (for the 10 cycles) 64.4 degree
Complex Modulus (G*) (for the 10 measurements) 5584.115 kPa
Test Temperature 31.0 C
(G*) x sin(δ)= 5036 kPa