Print Report | Back to Sample Detail

Sample Record for 2020-12-03-10

Note: Fields with no data or with a value of "Unknown" will not be displayed on the print out.

Project Information

Project ID: 209520 DEA: 06470904 EFIS: 0600000973 COOP: 061529 QA Service Level: 1
DIST-CO-RTE-PM: 06-MAD-99-R7.5/15.1
Work Description: WIDEN FREEWAY FROM 4 LANES TO 6 LANES.
Location Description: MADERA COUNTY IN AND NEAR MADERA FROM AVENUE 12 OVERCROSSING TO 0.9 MILE NORTH OF AVENUE 17 OVERCROSSING
Contractor Name: SECURITY PAVING COMPANY, INC.
Contractor Address: 13170 TELFAIR AVENUE, SYLMAR CA 91342
Resident Engineer: Eric Karlson Structure Rep.: Moua, Peter

Sample Information

DIME Sample ID: 2020-12-03-10
TL Number from the TL Form: C039414
Sample Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Sample Organization Contact: (916) 227-7302
Type of Sample: Quality Assurance
Type of Material: Asphalt Binder
Sample Taken Date: 12/03/2020
Date that the sample was received by the laboratory/organization performing the testing: 12/09/2020
The quantity of what the sample constitutes: 1 can
A brief description of the sample: Asphalt Binder
From where was the sample collected: Other
Laboratory sample identification:
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: San Joaquin Refinery, Bakersfield, CA

Material Information

Performance Grade: PG 70-10
Modified: No
Lot number:
Sublot number:
Tank number:
Time of sample:
HMA Supplier:
Asphalt Binder Supplier:
Multigrade:
Multigrade Type:

Test Results

Test 1 of 7

DIME Test ID: 2020-12-03-10-1
Test Method: AASHTO T240-17: Standard Method of Test for Effect of Heat and Air on a Moving Film of Asphalt Binder (Rolling Thin-Film Oven Test)
Verified Date: 12/17/2020
Date Tested: 12/16/2020
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Blvd,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: as per 2018 Standard specs
Additional Comments When Verified:
Is mass change based on one or two containers? One
Any material loss from containers during heating process/testing? No
Mass of empty container #1 174.378 grams
Mass of container #1 before test (m1i) 210.945 grams
Mass of container #1 after test (m1f) 210.942 grams
Average mass change -0.008 percent

Test 2 of 7

DIME Test ID: 2020-12-03-10-2
Test Method: AASHTO T51-13: Standard Method of Test for Ductility of Asphalt Materials (Asphalt Binder)
Verified Date: 12/17/2020
Date Tested: 12/16/2020
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Blvd,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: as per 2018 Standard specs
Additional Comments When Verified:
Is a normal test obtainable? Yes
Number of replicates tested One
Ductility of test #1 (D1) 107 cm
Ductility of sample 107 cm

Test 3 of 7

DIME Test ID: 2020-12-03-10-3
Test Method: AASHTO T315-16: Standard Method of Test for Determining the Rheological Properties of Asphalt Binder Using a Dynamic Shear Rheometer (DSR) (Dynamic Shear)
Verified Date: 12/17/2020
Date Tested: 12/16/2020
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Blvd,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: Per Cal Trans 2018 Standards and Specifications
Additional Comments When Verified:
Phase RTFO residue
Test Plate Diameter 25 mm
Test Gap 1 mm
Test Frequency 10.0 rad/s
Strain Amplitude 10.00 %
Stress Amplitude 0.212 kPa
Phase Angle (δ) (for the 10 cycles) 88.9 degree
Complex Modulus (G*) (for the 10 measurements) 2.121 kPa
Test Temperature 70.0 C
Dynamic Shear, G*/sin(δ) 2.12 kPa

Test 4 of 7

DIME Test ID: 2020-12-03-10-4
Test Method: AASHTO T315-16: Standard Method of Test for Determining the Rheological Properties of Asphalt Binder Using a Dynamic Shear Rheometer (DSR) (Dynamic Shear)
Verified Date: 12/18/2020
Date Tested: 12/17/2020
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Blvd,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: Per 2018 Standard Specifications
Additional Comments When Verified:
Phase PAV residue
Test Plate Diameter 8 mm
Test Gap 2 mm
Test Frequency 10.0 rad/s
Strain Amplitude 1.00 %
Stress Amplitude 46.854 kPa
Phase Angle (δ) (for the 10 cycles) 63.9 degree
Complex Modulus (G*) (for the 10 measurements) 4685.193 kPa
Test Temperature 34.0 C
(G*) x sin(δ)= 4207 kPa

Test 5 of 7

DIME Test ID: 2020-12-03-10-5
Test Method: AASHTO T315-16: Standard Method of Test for Determining the Rheological Properties of Asphalt Binder Using a Dynamic Shear Rheometer (DSR) (Dynamic Shear)
Verified Date: 12/16/2020
Date Tested: 12/16/2020
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Blvd,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: Per Cal Trans 2018 Standards and Specifications
Additional Comments When Verified:
Phase Original binder
Test Plate Diameter 25 mm
Test Gap 1 mm
Test Frequency 10.0 rad/s
Strain Amplitude 12.00 %
Stress Amplitude 0.139 kPa
Phase Angle (δ) (for the 10 cycles) 89.5 degree
Complex Modulus (G*) (for the 10 measurements) 1.160 kPa
Test Temperature 70.0 C
Dynamic Shear, G*/sin(δ) 1.16 kPa

Test 6 of 7

DIME Test ID: 2020-12-03-10-6
Test Method: AASHTO T313-19: Standard Method of Test for Determining the Flexural Creep Stiffness of Asphalt Binder Using the Bending Beam Rheometer (BBR)
Verified Date: 12/23/2020
Date Tested: 12/21/2020
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Blvd,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: Per 2018 Standard Specifications
Additional Comments When Verified:
Minimum test bath temperature at 240 s no data
Maximum test bath temperature at 240 s no data
Time of test load application no data HH:MM:SS
File name of test data no data
Time beam in bath no data
Time test started no data HH:MM:SS
Flags issued by software during test no data
Correlation coefficient (R²) 0
Regression coefficient a no data
Regression coefficient b no data
Regression coefficient c no data
Load at time 0.0 0.0 mN
Deflection at time 0.0 s 0.000 µm
Load at time 0.5 s 0.0 mN
Deflection at time 0.5 s 0.000 µm
Load at 60.0 s 0.0 mN
Beam deflection 60.0 s 0.000 µm
Measured Stiffness Modulus 60.0 s 205.000 mPa
Estimated Stiffness Modulus 60.0 s no data
Difference between stiffness moduli 60.0 s no data
Estimated m-value 60.0 s 0.392

Test 7 of 7

DIME Test ID: 2020-12-03-10-7
Test Method: AASHTO T315-16: Standard Method of Test for Determining the Rheological Properties of Asphalt Binder Using a Dynamic Shear Rheometer (DSR) (Dynamic Shear)
Verified Date: 12/18/2020
Date Tested: 12/16/2020
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Blvd,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: Per Cal Trans 2018 Standards and Specifications
Additional Comments When Verified:
Phase RTFO residue
Test Plate Diameter 25 mm
Test Gap no data
Test Frequency 10.0 rad/s
Strain Amplitude 10.00 %
Stress Amplitude 0.212 kPa
Phase Angle (δ) (for the 10 cycles) 88.9 degree
Complex Modulus (G*) (for the 10 measurements) 2.121 kPa
Test Temperature 70.0 C
Dynamic Shear, G*/sin(δ) 2.12 kPa