Print Report | Back to Sample Detail

Sample Record for 2020-10-08-14

Note: Fields with no data or with a value of "Unknown" will not be displayed on the print out.

Project Information

Project ID: 55555 DEA: AMRL EFIS: AMRL QA Service Level:
DIST-CO-RTE-PM: 59---
Work Description: Special project for submitting Sample information for AASHTO Materials Reference Laboratory (AMRL).
Location Description:
Contractor Name: Unknown
Contractor Address: Unknown
Resident Engineer: Unknown Structure Rep.: Unknown

Sample Information

DIME Sample ID: 2020-10-08-14
TL Number from the TL Form: 262
Sample Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Sample Organization Contact: (916) 227-7302
Type of Sample: Proficiency
Type of Material: Asphalt Binder
Sample Taken Date: 10/08/2020
Date that the sample was received by the laboratory/organization performing the testing: 10/08/2020
The quantity of what the sample constitutes: 1 can, Due Nov, 19
A brief description of the sample: Asphalt Binder PG 58-34M
From where was the sample collected: Source
Laboratory sample identification:
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: AASHTO resource

Material Information

Performance Grade: PG 58-34 M
Modified: Yes
Lot number:
Sublot number:
Tank number:
Time of sample:
HMA Supplier:
Certified Asphalt Supplier:
Multigrade:
Multigrade Type:
Asphalt Binder Mix Number:

Test Results

Test 1 of 8

DIME Test ID: 2020-10-08-14-1
Test Method: AASHTO T240-17: Standard Method of Test for Effect of Heat and Air on a Moving Film of Asphalt Binder (Rolling Thin-Film Oven Test)
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
This test has been superseded on 10/16/2020.
Reason: retested

Test 2 of 8

DIME Test ID: 2020-10-08-14-2
Test Method: AASHTO T301-13: Standard Method of Test for Elastic Recovery Test of Asphalt Materials by Means of a Ductilometer
Verified Date: 10/15/2020
Date Tested: 10/15/2020
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Boulevard, Room 225,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test:
Test Result Compliance: not applicable
Additional Comments When Verified:
Final Reading from the testing machine (X) 5 cm
% Elongation Recovery 75 %

Test 3 of 8

DIME Test ID: 2020-10-08-14-3
Test Method: AASHTO T315-16: Standard Method of Test for Determining the Rheological Properties of Asphalt Binder Using a Dynamic Shear Rheometer (DSR) (Dynamic Shear)
Verified Date: 10/16/2020
Date Tested: 10/16/2020
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Boulevard, Room 225,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test:
Test Result Compliance: not applicable
Additional Comments When Verified:
Phase Original binder
Test Plate Diameter 25 mm
Test Gap 1 mm
Test Frequency 10.0 rad/s
Strain Amplitude 12.00 %
Stress Amplitude 0.176 kPa
Phase Angle (δ) (for the 10 cycles) 71.0 degree
Complex Modulus (G*) (for the 10 measurements) 1.470 kPa
Test Temperature (Specimen 1) 58.0 C
Dynamic Shear, G*/sin(δ) 1.55 kPa

Test 4 of 8

DIME Test ID: 2020-10-08-14-4
Test Method: AASHTO T315-16: Standard Method of Test for Determining the Rheological Properties of Asphalt Binder Using a Dynamic Shear Rheometer (DSR) (Dynamic Shear)
Verified Date: 10/16/2020
Date Tested: 10/16/2020
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Boulevard, Room 225,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test:
Test Result Compliance: not applicable
Additional Comments When Verified:
Phase RTFO residue
Test Plate Diameter 25 mm
Test Gap 1 mm
Test Frequency 10.0 rad/s
Strain Amplitude 10.00 %
Stress Amplitude 0.346 kPa
Phase Angle (δ) (for the 10 cycles) 65.6 degree
Complex Modulus (G*) (for the 10 measurements) 3.390 kPa
Test Temperature (Specimen 1) 58.0 C
Dynamic Shear, G*/sin(δ) 3.72 kPa

Test 5 of 8

DIME Test ID: 2020-10-08-14-5
Test Method: AASHTO T315-16: Standard Method of Test for Determining the Rheological Properties of Asphalt Binder Using a Dynamic Shear Rheometer (DSR) (Dynamic Shear)
Verified Date: 10/16/2020
Date Tested: 10/16/2020
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Boulevard, Room 225,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test:
Test Result Compliance: not applicable
Additional Comments When Verified:
Phase PAV residue
Test Plate Diameter 8 mm
Test Gap 2 mm
Test Frequency 10.0 rad/s
Strain Amplitude 1.00 %
Stress Amplitude 28.868 kPa
Phase Angle (δ) (for the 10 cycles) 50.5 degree
Complex Modulus (G*) (for the 10 measurements) 2869.070 kPa
Test Temperature (Specimen 1) 16.0 C
(G*) x sin(δ)= 2214 kPa

Test 6 of 8

DIME Test ID: 2020-10-08-14-6
Test Method: AASHTO T313-19: Standard Method of Test for Determining the Flexural Creep Stiffness of Asphalt Binder Using the Bending Beam Rheometer (BBR)
Verified Date: 10/16/2020
Date Tested: 10/16/2020
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Boulevard, Room 225,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test:
Test Result Compliance: not applicable
Additional Comments When Verified:
Minimum test bath temperature at 240 s no data
Maximum test bath temperature at 240 s no data
Time of test load application no data HH:MM:SS
File name of test data no data
Time beam in bath no data
Time test started no data HH:MM:SS
Flags issued by software during test no data
Correlation coefficient (R²) 0
Regression coefficient a no data
Regression coefficient b no data
Regression coefficient c no data
Load at time 0.0 0.0 mN
Deflection at time 0.0 s 0.000 µm
Load at time 0.5 s 0.0 mN
Deflection at time 0.5 s 0.000 µm
Load at 60.0 s 0.0 mN
Beam deflection 60.0 s 0.000 µm
Measured Stiffness Modulus 60.0 s 231.000 mPa
Estimated Stiffness Modulus 60.0 s no data
Difference between stiffness moduli 60.0 s no data
Estimated m-value 60.0 s 0.330

Test 7 of 8

DIME Test ID: 2020-10-08-14-7
Test Method: AASHTO T240-17: Standard Method of Test for Effect of Heat and Air on a Moving Film of Asphalt Binder (Rolling Thin-Film Oven Test)
Verified Date: 10/16/2020
Date Tested: 10/15/2020
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Boulevard, Room 225,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test:
Test Result Compliance: not applicable
Additional Comments When Verified:
Is mass change based on one or two containers? Two
Any material loss from containers during heating process/testing? No
Mass of empty container #1 174.970 grams
Mass of empty container #2 172.400 grams
Mass of container #1 before test (m1i) 209.740 grams
Mass of container #2 before test (m2i) 207.700 grams
Mass of container #1 after test (m1f) 209.590 grams
Mass of container #2 after test (m2f) 207.540 grams
Average mass change -0.442 percent

Test 8 of 8

DIME Test ID: 2020-10-08-14-8
Test Method: AASHTO T350-19: Multiple Stress Creep Recovery (MSCR) Test of Asphalt Binder Using a Dynamic Shear Rheometer (DSR) (Multiple Stress Creep Recovery)
Verified Date: 10/16/2020
Date Tested: 10/16/2020
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Boulevard, Room 225,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test:
Test Result Compliance: not applicable
Additional Comments When Verified:
PG test temperature 58.0 C
Average percent recovery at 0.1 kPa 69.0500 %
Average percent recovery at 3.2 kPa 41.9000 %
Nonrecoverable creep compliance 0.5394
Nonrecoverable creep compliance 1.0005
Percent difference between nonrecoverable creep compliance at 0.1 kPa and 3.2 kPa 85.4700 %