Print Report | Back to Sample Detail

Sample Record for 2020-07-21-6

Note: Fields with no data or with a value of "Unknown" will not be displayed on the print out.

Project Information

Project ID: 214687 DEA: 031G4904 EFIS: 0318000241 QA Service Level: 1
DIST-CO-RTE-PM: 03-ED,PLA,SAC,YOL-49,50,80-Var
Work Description: REPLACE JOINT SEALS AND PLACE POLYESTER CONCRETE OVERLAY.
Location Description: EL DORADO, PLACER, SACRAMENTO, AND YOLO COUNTIES AT VARIOUS LOCATIONS
Contractor Name: AMERICAN CIVIL CONSTRUCTORS WEST COAST LLC
Contractor Address: 3701 MALLARD DRIVE, BENICIA, CA 94510
Resident Engineer: Dean Elghassein Structure Rep.: Unknown

Sample Information

DIME Sample ID: 2020-07-21-6
TL Number from the TL Form: Sacramento Caltrans lab
Sample Submitted By Organization: Kwik Bond Polymers
Sample Organization Contact: (760) 518-6064
Type of Sample: Quality Control
Type of Material: Polyester
Sample Taken Date: 07/21/2020
Date that the sample was received by the laboratory/organization performing the testing: 07/21/2020
The quantity of what the sample constitutes: 2 tankers
A brief description of the sample: 1 gallon can
From where was the sample collected: Source
Laboratory sample identification:
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: Kwik Bond Polymers and Reichhold

Material Information

Mfg. Lot Number(s): 1265454
Batch number: 1265454
Mix number: 1265454

Test Results

Test 1 of 7

DIME Test ID: 2020-07-21-6-1
Test Method: ASTM D2196-Feb15: Standard Test Methods for Rheological Properties of Non-Newtonian Materials by Rotational Viscometer
Verified Date: 10/19/2020
Date Tested: 10/19/2020
Submitted By Organization: CT HQ - Sacramento Concrete Testing Laboratory
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: spencer.adams@dot.ca.gov
Organization Phone: (916) 227-5716
General Comments for this Test:
Test Result Compliance: complies
Additional Comments When Verified:
Viscosity 112

Test 2 of 7

DIME Test ID: 2020-07-21-6-2
Test Method: ASTM D1475-Nov13: Standard Test Method For Density of Liquid Coatings, Inks, and Related Products
Verified Date: 10/19/2020
Date Tested: 10/19/2020
Submitted By Organization: CT HQ - Sacramento Concrete Testing Laboratory
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: spencer.adams@dot.ca.gov
Organization Phone: (916) 227-5716
General Comments for this Test:
Test Result Compliance: complies
Additional Comments When Verified:
Density Units pounds/gallons
Liquid Density (pounds per gallon) 1.08

Test 3 of 7

DIME Test ID: 2020-07-21-6-3
Test Method: ASTM D638-Dec14: Standard Test Method for Tensile Properties of Plastics
Submitted By Organization: CT HQ - Sacramento Concrete Testing Laboratory
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: spencer.adams@dot.ca.gov
Organization Phone: (916) 594-1991
This test has been superseded on 10/19/2020.
Reason: retested

Test 4 of 7

DIME Test ID: 2020-07-21-6-4
Test Method: ASTM D2369-Jul10: Standard Test Method for Volatile Content of Coatings
Verified Date: 10/19/2020
Date Tested: 10/19/2020
Submitted By Organization: CT HQ - Sacramento Concrete Testing Laboratory
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: spencer.adams@dot.ca.gov
Organization Phone: (916) 227-5716
General Comments for this Test:
Test Result Compliance: complies
Additional Comments When Verified:
Mean of two volatile content determination 45.4

Test 5 of 7

DIME Test ID: 2020-07-21-6-5
Test Method: CTM 551-August 2012: Method of Test for Determining Suitability of Materials for Overlayment and Repair of Portland Cement Concrete Pavements and Structures
Verified Date: 10/19/2020
Date Tested: 10/19/2020
Submitted By Organization: CT HQ - Sacramento Concrete Testing Laboratory
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: spencer.adams@dot.ca.gov
Organization Phone: (916) 227-5716
General Comments for this Test:
Test Result Compliance: complies
Additional Comments When Verified:
Curing history for Sample 1 24hr
Maximum applied load (P) for Sample 1 1520 lb
Span length for Sample 1 9 in
Break location for Sample 1 bond
Specimen defects/notes for Sample 1 no data
Surface type for Sample 1 SSD
Modulus of rupture (R) for Sample 1 760 psi
Curing history for Sample 2 24hr
Maximum applied load (P) for Sample 2 1340 lb
Span length for Sample 2 9 in
Break location for Sample 2 bond
Specimen defects/notes for Sample 2 no data
Surface type for Sample 2 SSD
Modulus of rupture (R) for Sample 2 670 psi
Curing history for Sample 3 24hr
Maximum applied load (P) for Sample 3 1648 lb
Span length for Sample 3 9 in
Break location for Sample 3 bond
Specimen defects/notes for Sample 3 no data
Surface type for Sample 3 SSD
Modulus of rupture (R) for Sample 3 824 psi

Test 6 of 7

DIME Test ID: 2020-07-21-6-6
Test Method: SCAQMD 309-91-Feb93: Determination of Static Volatile Emissions
Verified Date: 10/19/2020
Date Tested: 10/19/2020
Submitted By Organization: CT HQ - Sacramento Concrete Testing Laboratory
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: spencer.adams@dot.ca.gov
Organization Phone: (916) 227-5716
General Comments for this Test:
Test Result Compliance: complies
Additional Comments When Verified:
Diameter of lid 153.9 mm
Room Temperature 77 f
Tare weight 0 grams
Initial weight 100 grams
Weight at 5 minutes 99.964 grams
Weight at 10 minutes 99.935 grams
Weight at 15 minutes 99.863 grams
Weight at 20 minutes 99.662 grams
Weight at 25 minutes 99.634 grams
Weight at 30 minutes 99.594 grams
Final weight 99.59 grams
Total weight loss 0.41 grams
Calculated radius of gallon can lid in cm 7.695 cm
Lid Factor 53.757 m^2
Volatile emission 22.04 grams/m^2

Test 7 of 7

DIME Test ID: 2020-07-21-6-7
Test Method: ASTM D638-Dec14: Standard Test Method for Tensile Properties of Plastics
Verified Date: 10/19/2020
Date Tested: 10/19/2020
Submitted By Organization: CT HQ - Sacramento Concrete Testing Laboratory
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: spencer.adams@dot.ca.gov
Organization Phone: (916) 227-5716
General Comments for this Test:
Test Result Compliance: complies
Additional Comments When Verified:
Number of specimens tested 6
Conditioning procedure 18/25/50+5/70
Speed of testing 0.45 in/min
Sample 1 Width 0.482 in
Sample 1 Ultimate strength 3235.8 psi
Sample 1 Thickness 0.256 in
Sample 1 Area 0.1234 in^2
Sample 1 Ultimate Strength Actual 399.3 lbs
Sample 1 percent elongation 59.93 %
Sample 1 Time 0 MM:SS
Sample 2 Width 0.483 in
Sample 2 Thickness 0.25 in
Sample 2 Area 0.1208 in^2
Sample 2 Ultimate strength 3162.3 psi
Sample 2 Ultimate Strength Actual 382 lbs
Sample 2 percent elongation 59.13 %
Sample 2 Time 0 MM:SS
Sample 3 Width 0.484 in
Sample 3 Thickness 0.251 in
Sample 3 Area 0.1215 in^2
Sample 3 Ultimate strength 3296.3 psi
Sample 3 Ultimate Strength Actual 400.5 lbs
Sample 3 percent elongation 62.54 %
Sample 3 Time 0 MM:SS
Sample 4 Width 0.483 in
Sample 4 Thickness 0.26 in
Sample 4 Area 0.1256 in^2
Sample 4 Ultimate strength 3229.3 psi
Sample 4 Ultimate Strength Actual 405.6 lbs
Sample 4 percent elongation 61.18 %
Sample 4 Time 0 MM:SS
Sample 5 Width 0.483 in
Sample 5 Thickness 0.259 in
Sample 5 Area 0.1251 in^2
Sample 5 Ultimate strength 3303.8 psi
Sample 5 Ultimate Strength Actual 413.3 lbs
Sample 5 percent elongation 62.33 %
Sample 5 Time 0 MM:SS
Sample 6 Width 0.483 in
Sample 6 Thickness 0.255 in
Sample 6 Area 0.1232 in^2
Sample 6 Ultimate strength 3237 psi
Sample 6 Ultimate Strength Actual 398.8 lbs
Sample 6 percent elongation 60.97 %
Sample 6 Time 0 MM:SS
Ultimate Strength Average 3244 psi
Percent Elongation Average 61 %