Unit system used?
|
US Units
|
Number of specimens
|
6
|
Test performed
|
With no density determined
|
Capped in accordance with?
|
ASTM C617/CTM521
|
Average diameter of cylinder 1
|
6.01 in
|
Average diameter of cylinder 2
|
6.00 in
|
Average diameter of cylinder 3
|
5.98 in
|
Average diameter of cylinder 4
|
5.97 in
|
Average diameter of cylinder 5
|
6.00 in
|
Average diameter of cylinder 6
|
6.01 in
|
Cross sectional area of cylinder 1
|
28.37 in^2
|
Cross sectional area of cylinder 2
|
28.27 in^2
|
Cross sectional area of cylinder 3
|
28.09 in^2
|
Cross sectional area of cylinder 4
|
27.99 in^2
|
Cross sectional area of cylinder 5
|
28.27 in^2
|
Cross sectional area of cylinder 6
|
28.37 in^2
|
Compressive strength (to nearest 10 psi)
|
570 psi
|
Maximum load on cylinder 1
|
15850 lb
|
Maximum load on cylinder 2
|
14970 lb
|
Maximum load on cylinder 3
|
17190 lb
|
Maximum load on cylinder 4
|
15510 lb
|
Maximum load on cylinder 5
|
16540 lb
|
Maximum load on cylinder 6
|
16320 lb
|
Compressive strength of cylinder 1
|
558.7 psi
|
Type of fracture pattern of cylinder 1
|
2
|
Compressive strength of cylinder 2
|
529.5 psi
|
Compressive strength of cylinder 3
|
612 psi
|
Compressive strength of cylinder 4
|
554.1 psi
|
Compressive strength of cylinder 5
|
585.1 psi
|
Compressive strength of cylinder 6
|
575.3 psi
|
Type of fracture pattern of cylinder 2
|
2
|
Type of fracture pattern of cylinder 3
|
2
|
Type of fracture pattern of cylinder 4
|
2
|
Type of fracture pattern of cylinder 5
|
2
|
Type of fracture pattern of cylinder 6
|
2
|
Comment on any defect in either specimen or caps (Max 250 Characters)
|
ALL CYLINDERS HAD LARGE AIR VOIDS IN THE TOP 1/2 TO 1/3
|
Correction factor for cylinder 1
|
1
|
Correction factor for cylinder 2
|
1
|
Correction factor for cylinder 3
|
1
|
Correction factor for cylinder 4
|
1
|
Correction factor for cylinder 5
|
1
|
Correction factor for cylinder 6
|
1
|
Age of specimen
|
7 days
|
Age of specimen in hours
|
no data
|