Note: Fields with no data or with a value of "Unknown" will not be displayed on the print out.
Project ID: 88888 DEA: SMTL-STOCK EFIS: SMTL-STOCK
QA Service Level:
DIST-CO-RTE-PM: 59---
Work Description: Special project for SMTL stock material. Object Code: 1025. J2 DEA: 912680.
Location Description:
Contractor Name: Unknown
Contractor Address: Unknown
Resident Engineer: Unknown Structure Rep.: Unknown
DIME Sample ID: 2019-03-27-9
TL Number from the TL Form:
Sample Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Sample Organization Contact: (530) 329-6527
Type of Sample: Quality Assurance
Type of Material: SMTL TM6 - Ductile Iron Cast Samples
Sample Taken Date: 03/27/2019
Date that the sample was received by the laboratory/organization performing the testing: 03/29/2019
The quantity of what the sample constitutes: 12
A brief description of the sample: casting
From where was the sample collected: Manufacturer
Laboratory sample identification:
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: Farrar
Heat Number (s): A319 B079 B219 B229 B289 C079 C089 C139 C149
Part Number (s): SDI 12 6 AH SDI 1 38 Bar BP SDI 12 6 PC BP SD
Material Specification: A536
Grades: 80-55-06
Metal Foundry Manufacturer (Mill): Farrar
Prestressing Manufacturer: SDI
DIME Test ID: 2019-03-27-9-1
Test Method: ASTM A370-15: Standard Test Methods and Definitions for Mechanical Testing of Steel Products (Tensile - Round Sample)
Verified Date: 04/04/2019
Date Tested: 04/03/2019
Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: joshua.moore@dot.ca.gov
Organization Phone: (530) 329-6527
General Comments for this Test:
Test Result Compliance:
Additional Comments When Verified:
Number of Samples
|
12
|
Sample | Heat Number | Diameter (in) | Area (sqin) | Stress at Offset (psi) | Tensile Strength (psi) | Elongation in 4 x d (%) | Tested By | | A319 | 0.501 | 0.1971 | 62373 | 109620 | 10.4 | Steve | | C139 | 0.503 | 0.1987 | 64303 | 112880 | 8.9 | Steve | | C149 - AH | 0.501 | 0.1971 | 62461 | 107340 | 10.8 | Steve | | C149 - PC BP | 0.502 | 0.1979 | 62645 | 110080 | 10.4 | Steve | | B079 | 0.503 | 0.1987 | 62345 | 108820 | 10.1 | Steve | | B219 - 12.6 | 0.502 | 0.1979 | 63596 | 109660 | 10.7 | Steve | | B219 - 19.6 | 0.501 | 0.1971 | 63835 | 110770 | 9.6 | Steve | | B229 - 12.6 | 0.502 | 0.1979 | 62141 | 106890 | 11.1 | Steve | | B229 - 19.6 | 0.502 | 0.1979 | 62027 | 106460 | 11.4 | Steve | | B289 | 0.504 | 0.1995 | 61235 | 106140 | 11.2 | Steve | | C079 | 0.501 | 0.1971 | 62039 | 107320 | 11.2 | Steve | | C089 | 0.501 | 0.1971 | 62522 | 109200 | 9.8 | Steve |
| |
UTM
|
67KIP
|
Temperature
|
72 F
|