Note: Fields with no data or with a value of "Unknown" will not be displayed on the print out.
Project ID: 88888 DEA: SMTL-STOCK EFIS: SMTL-STOCK
QA Service Level:
DIST-CO-RTE-PM: 59---
Work Description: Special project for SMTL stock material. Object Code: 1025. J2 DEA: 912680.
Location Description:
Contractor Name: Unknown
Contractor Address: Unknown
Resident Engineer: Unknown Structure Rep.: Unknown
DIME Sample ID: 2018-08-31-13
TL Number from the TL Form: NA
Sample Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Sample Organization Contact: (530) 329-6527
Type of Sample: Quality Assurance
Type of Material: SMTL TM6 - Ductile Iron Cast Samples
Sample Taken Date: 08/31/2018
Date that the sample was received by the laboratory/organization performing the testing: 09/20/2018
The quantity of what the sample constitutes: 3
A brief description of the sample: Coupon Casting
From where was the sample collected: Distributor
Laboratory sample identification: Unknown
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: Williams Form Gartland
Heat Number (s): 240Y, 236Y, 250Y
Part Number (s): 8118 8106 8140
Material Specification: A536
Grades: 80-55-06
Metal Foundry Manufacturer (Mill): Gartland Foundry
Prestressing Manufacturer: Williams Form Engineering
DIME Test ID: 2018-08-31-13-1
Test Method: ASTM A370-15: Standard Test Methods and Definitions for Mechanical Testing of Steel Products (Tensile - Round Sample)
Verified Date: 09/27/2018
Date Tested: 09/27/2018
Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: joshua.moore@dot.ca.gov
Organization Phone: (530) 329-6527
General Comments for this Test:
Test Result Compliance:
Additional Comments When Verified:
Number of Samples
|
3
|
Sample | Heat Number | Diameter (in) | Area (sqin) | Stress at Offset (psi) | Tensile Strength (psi) | Elongation in 4 x d (%) | Tested By | | 8106 | 0.505 | 0.2003 | 57960 | 95200 | 9.2 | Fred | | 8118 | 0.505 | 0.2003 | 59142 | 99830 | 10.7 | Fred | | 8140 | 0.504 | 0.1995 | 60112 | 86610 | 3.5 | Fred |
| |
UTM
|
67KIP
|
Temperature
|
72 F
|