Sample Record for 2018-08-30-5

Note: Fields with no data or with a value of "Unknown" will not be displayed on the print out.

Project Information

DEA: No Project QA Service Level:
DIST-CO-RTE-PM: ---
Work Description: Special project identifier for material not associated with a project
Location Description:
Contractor Name: Unknown
Contractor Address: Unknown
Resident Engineer: Unknown Structure Rep.: Unknown

Sample Information

DIME Sample ID: 2018-08-30-5
TL Number from the TL Form: NA
Sample Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Sample Organization Contact: (916) 227-7253
Type of Sample: Quality Assurance
Type of Material: SMTL TM6 - Ductile Iron Cast Samples
Sample Taken Date: 08/30/2018
Date that the sample was received by the laboratory/organization performing the testing: 08/31/2018
The quantity of what the sample constitutes: 15
A brief description of the sample: Ductile Iron Casting
From where was the sample collected: Distributor
Laboratory sample identification: Unknown
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: SDI Farrar

Material Information

Heat Number (s): E168 E178 D188 D198 D258 E038 E098 F018 F068
Part Number (s): 1 75 HS 1 38 HS 1 75 HS 1 75 HS 1 75 HS 19 6
Material Specification: A536
Grades: 80-55-06
Metal Foundry Manufacturer (Mill): Farrar Corporation
Prestressing Manufacturer: SDI

Test Results

Test 1 of 1

DIME Test ID: 2018-08-30-5-1
Test Method: ASTM A370-15: Standard Test Methods and Definitions for Mechanical Testing of Steel Products (Tensile - Round Sample)
Verified Date: 09/10/2018
Date Tested: 09/06/2018
Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: paul.lukkarila@dot.ca.gov
Organization Phone: 916-227-7257
General Comments for this Test:
Test Result Compliance:
Additional Comments When Verified:
Number of Samples 15
SampleHeat NumberDiameter (in)Area (sqin)Stress at Offset (psi)Tensile Strength (psi)Elongation in 4 x d (%)Tested By
E0980.5010.1971658331129307.2Fred
F0180.5010.19715998310356010.3Fred
D1980.5010.1971623391090708.2Fred
D2580.5010.1971647661135808Fred
E1680.5010.1971649921132706.9Fred
F0680.5010.1971639101115909.4Fred
F068A0.5010.1971646901099008Fred
F0780.5020.1979628661107009.2Fred
D1880.5010.19716424611293010.1Fred
F2780.5010.1971652671136107.1Fred
F2980.5010.1971647171136808.3Fred
E1780.5010.1971653511151607.5Fred
F1380.5010.1971632721110009.4Fred
E0380.5010.19716536111403010.7Fred
F1480.5010.1971646371142309.2Fred
UTM 67KIP
Temperature 72 F