Note: Fields with no data or with a value of "Unknown" will not be displayed on the print out.
DEA: No Project
QA Service Level:
DIST-CO-RTE-PM: ---
Work Description: Special project identifier for material not associated with a project
Location Description:
Contractor Name: Unknown
Contractor Address: Unknown
Resident Engineer: Unknown Structure Rep.: Unknown
DIME Sample ID: 2018-05-01-3
TL Number from the TL Form: Unknown
Sample Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Sample Organization Contact: (916) 227-7253
Type of Sample: Quality Assurance
Type of Material: SMTL TM6 - Ductile Iron Cast Samples
Sample Taken Date: 05/01/2018
Date that the sample was received by the laboratory/organization performing the testing: 05/01/2018
The quantity of what the sample constitutes: 11
A brief description of the sample: 11Cast iron samples
From where was the sample collected: Fabricator
Laboratory sample identification: Unknown
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: Schwagger Davis
Heat Number (s): B088, B028, A258, B018, B148, A188, A198, A25
Part Number (s): SDI 12 6 AH SDI 12 6 PC BP SDI 19 6 AH
Material Specification: A536
Grades: 80-55-06
Metal Foundry Manufacturer (Mill): Farrar
Prestressing Manufacturer: Schwager Davis inc
DIME Test ID: 2018-05-01-3-1
Test Method: ASTM A370-15: Standard Test Methods and Definitions for Mechanical Testing of Steel Products (Tensile - Round Sample)
Verified Date: 05/08/2018
Date Tested: 05/07/2018
Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: paul.lukkarila@dot.ca.gov
Organization Phone: 916-227-7257
General Comments for this Test:
Test Result Compliance:
Additional Comments When Verified:
|
Number of Samples
|
11
|
| Sample | Heat Number | Diameter (in) | Area (sqin) | Stress at Offset (psi) | Tensile Strength (psi) | Elongation in 4 x d (%) | Tested By | | B088 | 0.505 | 0.2003 | 65626 | 114740 | 7.8 | Brian | | B078 | 0.505 | 0.2003 | 62502 | 107310 | 8.7 | Brian | | B218 | 0.505 | 0.2003 | 63700 | 110770 | 8.7 | Brian | | B088 | 0.505 | 0.2003 | 57304 | 95430 | 11.4 | Brian | | B028 | 0.505 | 0.2003 | 56698 | 93060 | 9.2 | Brian | | A258 | 0.505 | 0.2003 | 61295 | 102370 | 7 | Brian | | A258 | 0.505 | 0.2003 | 60720 | 103370 | 8.6 | Brian | | B018 | 0.505 | 0.2003 | 60508 | 103490 | 11.4 | Brian | | B148 | 0.506 | 0.2011 | 59668 | 103240 | 11.5 | Brian | | A188 | 0.505 | 0.2003 | 61148 | 104590 | 9.4 | Brian | | A198 | 0.505 | 0.2003 | 60499 | 105070 | 9.7 | Brian |
| |
|
UTM
|
67KIP
|
|
Temperature
|
72 F
|