Sample Information

DIME Sample ID: 2017-04-28-7
TL Number from the TL Form: NA
Sample Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Sample Organization Contact: (916) 227-7253
Type of Sample: Quality Assurance
Type of Material: SMTL TM2 - Type B Elastomeric Joint Seal
Sample Taken Date: 04/28/2017
Date that the sample was received by the laboratory/organization performing the testing: 05/01/2017
The quantity of what the sample constitutes: 600ft
A brief description of the sample: 5in Joint Seal
From where was the sample collected: Manufacturer
Laboratory sample identification: Unknown
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: Watson Bowman

Material Information

Mfg. Lot Number(s): 0817208
Manufacturer(s): Watson Bowman
Temperature: 72
Humidity: 50
Comments: Unknown
Joint Seal Size: 5.00

Test Results

Test 1 of 7

DIME Test ID: 2017-04-28-7-1
Test Method: CTM 673-July 2012: Method of Determining Movement Rating of Type B1 and B2 Preformed Elastomeric Joint Seals
Verified Date: 05/17/2017
Date Tested: 05/03/2017
Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: paul.lukkarila@dot.ca.gov
Organization Phone: (916) 227-7253
General Comments for this Test:
Test Result Compliance:
Additional Comments When Verified:
UTM 11KIP
Temperature 72 ?F
Humidity 50 %
Load at W1 76.0282 lbs
Width at 4 x Load at W1 2.19097 in
Nominal Width 5 in
Measured Maximum Uncompressed Width 5.1205 in
Measured Minimum Uncompressed Width 5.0285 in
Minimum Uncompressed Width as Specified by the Manufacturer (MUWASBM) 5.075 in
Height of Contact Face 5.116 in
Spec Minimum Uncompressed Width 5.0285 in
Area (5 Times of the Height of Contact Face) 25.58 sqin
Half of the Spec Minimum Uncompressed Width 2.5375 in
85 Percent of the Spec Minimum Uncompressed Width 4.27423 in
3 Times of the Area 76.74 sqin
4 Times of the Load at W1 304.113 in
W1 (US Units) 4.274 in
W1 (Metric Units) 108.565 millimeters
W2 (US Units) 2.191 in
W2 (Metric Units) 55.651 millimeters
Satisfactory of MR of (US Units) 2.083 in
Satisfactory of MR of (Metric Units) 52.915 millimeters
Optional W1 Measurement 1 4.2742 in
Optional W1 Measurement 2 77.2516 sqin

Test 2 of 7

DIME Test ID: 2017-04-28-7-2
Test Method: ASTM D2240-05re10: Standard Test Method for Rubber Property - Durometer Hardness
Verified Date: 05/17/2017
Date Tested: 05/10/2017
Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: paul.lukkarila@dot.ca.gov
Organization Phone: (916) 227-7253
General Comments for this Test:
Test Result Compliance:
Additional Comments When Verified:
Temperature 72 f
Humidity 50 %
Reading #1 56
Reading #2 55
Reading #3 56
Reading #4 55
Reading #5 56
Mean 55.6

Test 3 of 7

DIME Test ID: 2017-04-28-7-3
Test Method: ASTM D412-06a-re13: Standard Test Methods for Vulcanized Rubber and Thermoplastic Elastomers-Tension
Verified Date: 05/17/2017
Date Tested: 05/10/2017
Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: paul.lukkarila@dot.ca.gov
Organization Phone: (916) 227-7253
General Comments for this Test:
Test Result Compliance:
Additional Comments When Verified:
UTM 2KIP
Humidity 50 %
Temperature 72 F
Sample 1 Median Thickness 0.068 in
Sample 1 Thickness all Within 0.003 inch? Yes
Sample 1 Ultimate Tensile 2411.8 lbf?in/in?
Sample 1 Elongation (350% Min) Pass
Sample 2 Median Thickness 0.073 in
Sample 2 Thickness all Within 0.003 inch? Yes
Sample 2 Ultimate Tensile 2349.7 lbf?in/in?
Sample 2 Elongation (350% Min) Pass
Sample 3 Median Thickness 0.071 in
Sample 3 Thickness all Within 0.003 inch? Yes
Sample 3 Ultimate Tensile 2191 lbf?in/in?
Sample 3 Elongation (350% Min) Pass
Median of the Ultimate Tensile Values 2349.7 psi

Test 4 of 7

DIME Test ID: 2017-04-28-7-4
Test Method: ASTM D2628-91-re11-low: Standard Specification for Preformed Polychloroprene Elastomeric Joint Seals for Concrete Pavements (Low Temp Recovery)
Verified Date: 05/17/2017
Date Tested: 05/10/2017
Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: paul.lukkarila@dot.ca.gov
Organization Phone: (916) 227-7253
General Comments for this Test:
Test Result Compliance:
Additional Comments When Verified:
Temperature 72 f
Humidity 50 %
Low Temp Recovery (22 hrs at -20F) Size Before (Height of Contact Face ) 5 in
Low Temp Recovery (22 hrs at -20F) Size After (Recovered Contact Face ) 4.63 in
Percent Recovery (Low Temp) 93 %

Test 5 of 7

DIME Test ID: 2017-04-28-7-5
Test Method: ASTM D2628-91-re11-high: Standard Specification for Preformed Polychloroprene Elastomeric Joint Seals for Concrete Pavements (High Temp Recovery)
Verified Date: 05/17/2017
Date Tested: 05/10/2017
Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: paul.lukkarila@dot.ca.gov
Organization Phone: (916) 227-7253
General Comments for this Test:
Test Result Compliance:
Additional Comments When Verified:
Temperature 72 f
Humidity 50 %
High Temp Recovery (70 hrs at 212F) Size Before (Height of Contact Face ) 5 in
High Temp Recovery (70 hrs at 212F) Size After (Expanded Contact Face ) 4.806 in
Percent Recovery (High Temp) 96 %

Test 6 of 7

DIME Test ID: 2017-04-28-7-6
Test Method: ASTM D471-15a: Standard Test Method for Rubber Property - Effect of Liquids
Verified Date: 05/17/2017
Date Tested: 05/15/2017
Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: paul.lukkarila@dot.ca.gov
Organization Phone: (916) 227-7253
General Comments for this Test:
Test Result Compliance: complies
Additional Comments When Verified:
Oil Swell Percentage 35 %

Test 7 of 7

DIME Test ID: 2017-04-28-7-7
Test Method: SMTL BILST-06: (Neoprene Verification) Bilstein Test
Verified Date: 05/17/2017
Date Tested: 05/15/2017
Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: paul.lukkarila@dot.ca.gov
Organization Phone: (916) 227-7253
General Comments for this Test:
Test Result Compliance: complies
Additional Comments When Verified:
Result Pass