Print Report | Back to Sample Detail

Sample Record for 2017-03-14-2

Note: Fields with no data or with a value of "Unknown" will not be displayed on the print out.

Project Information

Project ID: 88888 DEA: STOCK EFIS: STOCK QA Service Level:
DIST-CO-RTE-PM: 59---
Work Description: Special project for SMTL stock material. Object Code: 1025. J2 DEA: 912680.
Location Description:
Contractor Name: Unknown
Contractor Address: Unknown
Resident Engineer: Unknown Structure Rep.: Unknown

Sample Information

DIME Sample ID: 2017-03-14-2
TL Number from the TL Form: NA
Sample Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Sample Organization Contact: (916) 227-7253
Type of Sample: Quality Assurance
Type of Material: SMTL TM2 - Type B Elastomeric Joint Seal
Sample Taken Date: 03/14/2017
Date that the sample was received by the laboratory/organization performing the testing: 03/15/2017
The quantity of what the sample constitutes: 1
A brief description of the sample: Joint Seal
From where was the sample collected: Manufacturer
Laboratory sample identification: Unknown
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: Watson Bowman

Material Information

Mfg. Lot Number(s): 0517167
Manufacturer(s): Watson Bowman
Temperature: 72
Humidity: 45
Comments: Unknown
Joint Seal Size: 3.75

Test Results

Test 1 of 7

DIME Test ID: 2017-03-14-2-1
Test Method: CTM 673-July 2012: Method of Determining Movement Rating of Type B1 and B2 Preformed Elastomeric Joint Seals
Verified Date: 04/03/2017
Date Tested: 03/21/2017
Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Organization Address: 5900 Folsom Blvd,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: paul.lukkarila@dot.ca.gov
Organization Phone: (916) 227-7253
General Comments for this Test:
Test Result Compliance:
Additional Comments When Verified:
UTM 11KIP
Temperature 72 ?F
Humidity 52 %
Load at W1 54.908 lbs
Width at 4 x Load at W1 1.54257 in
Nominal Width 3.75 in
Measured Maximum Uncompressed Width 3.938 in
Measured Minimum Uncompressed Width 3.76 in
Minimum Uncompressed Width as Specified by the Manufacturer (MUWASBM) 3.826 in
Height of Contact Face 3.402 in
Spec Minimum Uncompressed Width 3.76 in
Area (5 Times of the Height of Contact Face) 17.01 sqin
Half of the Spec Minimum Uncompressed Width 1.913 in
85 Percent of the Spec Minimum Uncompressed Width 3.196 in
3 Times of the Area 51.03 sqin
4 Times of the Load at W1 219.632 in
W1 (US Units) 3.196 in
W1 (Metric Units) 81.178 millimeters
W2 (US Units) 1.543 in
W2 (Metric Units) 39.181 millimeters
Satisfactory of MR of (US Units) 1.653 in
Satisfactory of MR of (Metric Units) 41.997 millimeters
Optional W1 Measurement 1 3.196 in
Optional W1 Measurement 2 51.3702 sqin

Test 2 of 7

DIME Test ID: 2017-03-14-2-2
Test Method: ASTM D2240-05re10: Standard Test Method for Rubber Property - Durometer Hardness
Verified Date: 04/03/2017
Date Tested: 03/23/2017
Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Organization Address: 5900 Folsom Blvd,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: paul.lukkarila@dot.ca.gov
Organization Phone: (916) 227-7253
General Comments for this Test:
Test Result Compliance:
Additional Comments When Verified:
Temperature 72 f
Humidity 50 %
Reading #1 55
Reading #2 54
Reading #3 56
Reading #4 56
Reading #5 55
Mean 55.2

Test 3 of 7

DIME Test ID: 2017-03-14-2-3
Test Method: ASTM D412-06a-re13: Standard Test Methods for Vulcanized Rubber and Thermoplastic Elastomers—Tension
Verified Date: 04/03/2017
Date Tested: 03/23/2017
Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Organization Address: 5900 Folsom Blvd,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: paul.lukkarila@dot.ca.gov
Organization Phone: (916) 227-7253
General Comments for this Test:
Test Result Compliance:
Additional Comments When Verified:
UTM 2KIP
Humidity 50 %
Temperature 72 F
Sample 1 Median Thickness 0.071 in
Sample 1 Thickness all Within 0.003 inch? Yes
Sample 1 Ultimate Tensile 2584.3 lbf?in/in?
Sample 1 Elongation (350% Min) Pass
Sample 2 Median Thickness 0.072 in
Sample 2 Thickness all Within 0.003 inch? Yes
Sample 2 Ultimate Tensile 2611.1 lbf?in/in?
Sample 2 Elongation (350% Min) Pass
Sample 3 Median Thickness 0.072 in
Sample 3 Thickness all Within 0.003 inch? Yes
Sample 3 Ultimate Tensile 2555.6 lbf?in/in?
Sample 3 Elongation (350% Min) Pass
Median of the Ultimate Tensile Values 2584.3 psi

Test 4 of 7

DIME Test ID: 2017-03-14-2-4
Test Method: ASTM D2628-91-re11-low: Standard Specification for Preformed Polychloroprene Elastomeric Joint Seals for Concrete Pavements (Low Temp Recovery)
Verified Date: 04/03/2017
Date Tested: 03/24/2017
Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Organization Address: 5900 Folsom Blvd,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: paul.lukkarila@dot.ca.gov
Organization Phone: (916) 227-7253
General Comments for this Test:
Test Result Compliance:
Additional Comments When Verified:
Temperature 72 f
Humidity 50 %
Low Temp Recovery (22 hrs at -20F) Size Before (Height of Contact Face ) 3.75 in
Low Temp Recovery (22 hrs at -20F) Size After (Recovered Contact Face ) 3.488 in
Percent Recovery (Low Temp) 93 %

Test 5 of 7

DIME Test ID: 2017-03-14-2-5
Test Method: ASTM D2628-91-re11-high: Standard Specification for Preformed Polychloroprene Elastomeric Joint Seals for Concrete Pavements (High Temp Recovery)
Verified Date: 04/03/2017
Date Tested: 03/23/2017
Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Organization Address: 5900 Folsom Blvd,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: paul.lukkarila@dot.ca.gov
Organization Phone: (916) 227-7253
General Comments for this Test:
Test Result Compliance:
Additional Comments When Verified:
Temperature 72 f
Humidity 50 %
High Temp Recovery (70 hrs at 212F) Size Before (Height of Contact Face ) 3.75 in
High Temp Recovery (70 hrs at 212F) Size After (Expanded Contact Face ) 3.53 in
Percent Recovery (High Temp) 94 %

Test 6 of 7

DIME Test ID: 2017-03-14-2-6
Test Method: ASTM D471-15a: Standard Test Method for Rubber Property - Effect of Liquids
Verified Date: 04/03/2017
Date Tested: 03/28/2017
Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Organization Address: 5900 Folsom Blvd,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: paul.lukkarila@dot.ca.gov
Organization Phone: (916) 227-7253
General Comments for this Test:
Test Result Compliance: complies
Additional Comments When Verified:
Oil Swell Percentage 37 %

Test 7 of 7

DIME Test ID: 2017-03-14-2-7
Test Method: SMTL BILST-06: (Neoprene Verification) Bilstein Test
Verified Date: 04/03/2017
Date Tested: 03/28/2017
Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Organization Address: 5900 Folsom Blvd,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: paul.lukkarila@dot.ca.gov
Organization Phone: (916) 227-7253
General Comments for this Test:
Test Result Compliance: complies
Additional Comments When Verified:
Result Pass