Note: Fields with no data or with a value of "Unknown" will not be displayed on the print out.
Project ID: 88888 DEA: SMTL-STOCK EFIS: SMTL-STOCK
QA Service Level:
DIST-CO-RTE-PM: 59---
Work Description: Special project for SMTL stock material. Object Code: 1025. J2 DEA: 912680.
Location Description:
Contractor Name: Unknown
Contractor Address: Unknown
Resident Engineer: Unknown Structure Rep.: Unknown
DIME Sample ID: 2024-08-21-60
TL Number from the TL Form:
Sample Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Sample Organization Contact: (530) 329-6527
Type of Sample: Quality Assurance
Type of Material: SMTL TM6 - Ductile Iron Cast Samples
Sample Taken Date: 08/21/2024
Date that the sample was received by the laboratory/organization performing the testing: 08/22/2024
The quantity of what the sample constitutes: 12
A brief description of the sample: Ductile Iron Casting
From where was the sample collected: Manufacturer
Laboratory sample identification:
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: SDI
Heat Number (s): B023 B074 C064 C064 H312 I012 I222 J192 J202
Part Number (s): ACS 31 6 AH SDI 19 6 AH SDI 12 6 PC BP SDI 19
Material Specification: A536
Grades: 80-55-06
Metal Foundry Manufacturer (Mill): Farrar Corporation
Prestressing Manufacturer: SDI
DIME Test ID: 2024-08-21-60-1
Test Method: ASTM A370-20: Standard Test Methods and Definitions for Mechanical Testing of Steel Products (Tensile - Round Sample)
Verified Date: 10/14/2024
Date Tested: 09/24/2024
Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: joshua.moore@dot.ca.gov
Organization Phone: (530) 329-6527
General Comments for this Test:
Test Result Compliance:
Additional Comments When Verified:
|
Number of Samples
|
12
|
| Sample | Heat Number | Diameter (in) | Area (sqin) | Stress at Offset (psi) | Tensile Strength (psi) | Elongation in 4 x d (%) | Tested By | | J272 | 0.5 | 0.19635 | 64913 | 114889 | 8.5 | aauvinen | | B023 | 0.5 | 0.19635 | 62671 | 109529 | 10.6 | rmacias | | I012 | 0.5 | 0.19635 | 61628 | 106988 | 9.4 | aauvinen | | C064 | 0.5 | 0.19635 | 63577 | 111284 | 9.7 | aauvinen | | I222 | 0.499 | 0.19556 | 62065 | 109405 | 9.8 | aauvinen | | B074 | 0.5 | 0.19635 | 61858 | 107954 | 8.9 | aauvinen | | C064 | 0.5 | 0.19635 | 64588 | 112109 | 7.7 | aauvinen | | H312 | 0.501 | 0.19714 | 60593 | 101502 | 6.4 | aauvinen | | J192 | 0.5 | 0.19635 | 61804 | 108527 | 9.4 | aauvinen | | K153 | 0.5 | 0.19635 | 62663 | 108611 | 7.9 | aauvinen | | K083 | 0.5 | 0.19635 | 64620 | 112557 | 7 | aauvinen | | J202 | 0.5 | 0.19635 | 63021 | 109128 | 8.4 | aauvinen |
| |
|
UTM
|
67kip
|
|
Temperature
|
72 F
|